Formula of gypsum binder

A binder and formula technology, applied in the field of gypsum binder formulation, can solve problems such as labor-intensive, time-consuming, and prone to cracking

Inactive Publication Date: 2010-06-16
河南省翔宇建材科技有限公司
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the joints between the existing gypsum slats are bonded with gauze coated with glue. This

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0005] 100 parts of desulfurized gypsum; 0.01 part of polyvinyl alcohol; 0.1 part of methyl cellulose; 0.01 part of citric acid;

[0006] The test report is as follows: initial setting time: 30min

[0007] Final setting time: 45min

[0008] Flexural strength: 2.3MPa

[0009] Compressive strength: 5.5MPa

[0010] Bonding (compression shear) strength: 0.40MPa

Embodiment 2

[0012] 100 parts of desulfurized gypsum; 5 parts of polyvinyl alcohol; 0.7 parts of methyl cellulose; 0.2 parts of citric acid;

[0013] The test report is as follows: initial setting time: 100min

[0014] Final setting time: 115min

[0015] Flexural strength: 2.5MPa

[0016] Compressive strength: 6.5MPa

[0017] Bonding (compression shear) strength: 0.60MPa

Embodiment 3

[0019] 100 parts of desulfurized gypsum; 3 parts of polyvinyl alcohol; 0.3 parts of methyl cellulose; 0.1 part of citric acid;

[0020] The test report is as follows: initial setting time: 85min

[0021] Final setting time: 105min

[0022] Flexural strength: 2.90MPa

[0023] Compressive strength: 6.5MPa

[0024] Bonding (compression shear) strength: 0.9MPa

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Flexural strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a formula of a gypsum binder. The gypsum binder comprises the following raw materials in parts by weight: 100 parts of desulfurized gypsum, 0-5 parts of polyvinyl alcohol, 0.1-0.7 part of methyl cellulose and 0-0.2 part of sodium citrate. The dry powder is evenly stirred and mixed to obtain the product. The test report indicates that the initial setting time is 30-100 minutes, the final setting time is 45-115 minutes, the folding strength is 2.3-2.9 MPa, the compression strength is 5.5-6.5 MPa, and the bonding (compression shear) strength is 0.40-0.9 MPa. The invention has the advantages of favorable stability, water retention and flow slide property, strong binding performance and favorable affinity, has the function of interfacial activity and greatly enhances the adhesive force between the product and the base material; and the invention has stable pH values, favorable lubricating property, favorable shrink resistance, favorable mildew resistance and the like, and does not need to use gauze at the seam, thereby having the advantages of firm binding and slight expansibility and preventing the phenomenon of cracking.

Description

Technical field: [0001] The invention relates to a formula of gypsum adhesive, which is especially suitable for bonding various gypsum boards and gypsum decorative art products. Background technique: [0002] Most of the joints between the existing gypsum slats are bonded with gauze coated with glue. This bonding method is labor-intensive, time-consuming, and a slight expansion is prone to cracking and the like. Invention content: [0003] The task of the present invention is to propose a formulation of a gypsum binder that is reliable in bonding, has good affinity, has interfacial activity, and greatly improves the adhesion between the product and the base material. The task of the present invention is accomplished like this, a kind of formula of gypsum binder, it is characterized in that: raw material deployment ratio by weight is: 100 parts of desulfurized gypsum, 0-5 part of polyvinyl alcohol, 0.1-0.7 part of methyl cellulose , 0-0.2 parts of sodium citrate, dry powde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/14C04B24/38C04B24/04
Inventor 李耕伟
Owner 河南省翔宇建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap