A polyester resin, weather-resistant technology, applied in the field of polyester resin, can solve the problem of few patents on polyester resin and so on

Active Publication Date: 2010-06-16
GUANGZHOU KINTE IND
View PDF3 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A large number of literatures have reported the method of directly polymerizing polyols and polybasic acids into polyester resins under the condition of organotin catalysts, but there are not many patent reports on polyester resins specifically aimed at improving the boilin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

Some specific examples are enumerated below to illustrate the present invention. Table 1 shows examples of polyester resins, and A to F show comparative examples of different monomers and process combinations. In a 10-liter reactor, add neopentyl glycol, 2-methyl-1,3-propanediol, ethylene glycol, 1,4-cyclohexanedimethanol, trimethylol Propane, heat up until the material melts; then add terephthalic acid, adipic acid, and butyl tin oxide in sequence, and continue to heat up the reaction with nitrogen gas. Esterification water begins to form and distill at around 180°C, and then gradually heat up to 250°C. React for 5-10 hours until 95% of the esterification water is discharged, the acid value reaches 6-23 mgKOH / g, add acidolysis agent, react for 3-5 hours, the acid value reaches 40-50 mgKOH / g, vacuum polycondensation for about 1-4 hours , the acid value reaches 28 ~ 36mgKOH / g, the reaction can be stopped.

Acid value: 28~36mgKOH / g; glass transition temperature: 60~75℃; softenin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Acid valueaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Softening pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses weather resistant polyester resin with excellent water-boiling resisting performance, which is prepared through the melt polycondensation of the following components: 20-45 percent by weight of polyol, 40-55 percent by weight of aromatic polybasic acid, 0-8 percent by weight of fat polybasic acid, 0-5 percent by weight of branching agent, 5-15 percent by weight of acidolysis agent and 0.01-0.15 percent by weight of esterification catalyst. The invention also discloses a method for preparing the weather resistant polyester resin with excellent water-boiling resisting performance. The polyester resin prepared with the method has high glass transition temperature, high softening point, appropriate melt viscosity and appropriate storage stability. The powder coating produced from the polyester resin has excellent water-boiling resisting performance, good leveling performance and good impact performance, etc.

Description

technical field The present invention relates to a kind of polyester resin, and the present invention also relates to a kind of preparation method of polyester resin. Background technique With its advantages of economy, environmental protection, high efficiency and excellent performance, powder coatings are gradually replacing organic solvent-based coatings, becoming an important development direction in the coatings industry, and have maintained a relatively fast growth rate. Powder coating metal building materials are also widely used in all aspects of buildings due to their excellent durability, decoration and processing formability. Since the advent of powder coatings in the early 1970s, its application in aluminum building materials has grown rapidly. At present, the application of powder coatings in aluminum building materials has expanded from Europe to the Americas, Australia, the Far East, the Middle East and Africa. In the coating of aluminum building materials, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G63/20C08G63/183C08G63/78C09D167/02C09D5/03C09D7/12
Inventor 李勇何涛周年忠
Owner GUANGZHOU KINTE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap