Ru red-dotted painted artistic glaze and application thereof

A technique of color painting and art, which is applied to Ru Kiln Dianhong Painted Art Glaze. Short time and other issues, to achieve the effect of good thermal stability, no cracks, beautiful appearance

Inactive Publication Date: 2010-06-23
张天庆
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to various historical reasons, Ru Kiln, a famous kiln of a generation, stopped firing. Due to the short firing time, there are less than 100 pieces in the collections of major museums in the world and our country, but there are no red painted art porcelain from Ru Kiln. A complete vessel has been handed down to the world, but only a few samples of ancient porcelain pieces have survived
However, from the observation of ancient porcelain samples, the existing Ru porcelain body is dry and astringent, with many gaps and cavities, and lacks the glass phase that porcelain usually has.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The Ru kiln point red colored painting art glaze of the present invention contains the following components in parts by weight: 10 parts of agate stone, 50 parts of feldspar, 6 parts of calcite, 4 parts of malachite and 3 parts of manganese stone.

[0024] The application of Ru kiln dot red painted art glaze on Ru porcelain of the present invention comprises the following steps:

[0025] 1) Bisque firing the green body at a temperature of 700°C;

[0026] 2) Apply glaze to the surface of the biscuit body after bisque firing. The method of glazing is: first apply the surface glaze, and then paint the Ru kiln dot red colored painting art glaze;

[0027] 3) Firing the glazed green body to obtain the Ru porcelain with red dotted painted artistic glaze.

Embodiment 2

[0029] The Ru kiln point red colored painting art glaze of the present invention contains the following components in parts by weight: 13 parts of agate stone, 53 parts of feldspar, 10 parts of calcite, 5 parts of malachite and 4 parts of manganese stone. The application of Ru kiln dot red painted art glaze on Ru porcelain of the present invention comprises the following steps:

[0030] 1) Bisque firing the green body at a temperature of 800°C;

[0031] 2) Apply glaze to the surface of the biscuit body after bisque firing. The method of glazing is: first apply the surface glaze, and then paint the Ru kiln dot red colored painting art glaze;

[0032] 3) Firing the glazed green body to obtain the Ru porcelain with red dotted painted artistic glaze.

Embodiment 3

[0034] The Ru kiln dot red colored painting art glaze of the present invention contains the following components in parts by weight: 17 parts of agate stone, 57 parts of feldspar, 15 parts of calcite, 6 parts of malachite and 4 parts of manganese stone.

[0035] The application of Ru kiln dot red painted art glaze on Ru porcelain of the present invention comprises the following steps:

[0036] 1) Bisque firing the green body at a temperature of 900°C;

[0037] 2) Apply glaze to the surface of the biscuit body after bisque firing. The method of glazing is: first apply the surface glaze, and then paint the Ru kiln dot red colored painting art glaze;

[0038] 3) Firing the glazed green body to obtain the Ru porcelain with red dotted painted artistic glaze.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a Ru red-dotted painted artistic glaze and application thereof on Ru porcelains, and also discloses a Ru porcelain, wherein the Ru red-dotted painted artistic glaze contains the following components by weight parts: 10 to 28 parts of agate, 50 to 68 parts of feldspar, 6 to 28 parts of calcite, 4 to 8 parts of malachite and 3 to 6 parts of manganese stone. The appearance of the Ru porcelain fired with the Ru red-dotted painted artistic glaze is good, moreover, the texture of the porcelain body is fine and dense, the porcelainizing degree is high, the water absorption does not exceed 1.2 percent, and the sound is silvery when the product is knocked; the thermostability is good, and defects, such as through cracks and leakage, do not exist.

Description

technical field [0001] The present invention relates to a kind of Ru kiln dot red color painting art glaze, also relates to the application of the Ru kiln dot red color painting art glaze, especially the application of a kind of Ru kiln dot red color painting art glaze on Ru kiln, and relates to a kind of Ru kiln art glaze at the same time , belongs to the technical field of silicate ceramics. Background technique [0002] Ru Kiln is one of the five famous kilns of Ru, Ge, Guan, Ding and Jun in the Song Dynasty in my country. Slices, wrapped feet and fired glaze to meet the typical characteristics of ". Ru Kiln Dianhong Painted Art Porcelain is a rare and precious variety of Ru Kiln. It is an important part of the national quintessence culture and has a very high evaluation in the history of Chinese ceramics. However, due to various historical reasons, Ru Kiln, a famous kiln of a generation, stopped firing. Due to the short firing time, there are less than 100 pieces in the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/86
Inventor 张天庆郭秀贞张颖政张颖裕
Owner 张天庆
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com