Low-VOC scratch-resistant modified polypropylene composite material and preparation method thereof

A composite material and polypropylene technology, applied in the field of modified polypropylene composite materials, can solve the problems of not meeting the performance requirements of automotive interior parts such as odor and atomization, and high content of volatile organic compounds

Inactive Publication Date: 2010-07-28
SUZHOU SUNWAY POLYMER
View PDF0 Cites 55 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, due to the characteristics of the anti-scratch agent itself, the content of volatile organic compounds in t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Prepare according to the following formula:

[0039] (a) 70 parts by mass of polypropylene

[0040] (b) 10 parts by mass of toughening agent (POE)

[0041] (c) 20 parts by mass of mineral filler (talcum powder)

[0042] (d) 3 parts by mass of odor adsorbent

[0043] (e) 6 parts by mass of wear-resistant agent / scratch-resistant agent

[0044] (f) 1 part by mass of other additives

[0045] Wherein, the odor adsorbent includes: bentonite, porous silica and activated alumina, according to the mass ratio, bentonite: porous silica: activated alumina=1:1:1; wear-resistant / scratch-resistant agents include TF9207, TEGOMER H-Si 6440P, according to mass ratio, TF 9207: TEGOMER H-Si 6440P=10:1.

[0046] Mix polypropylene and toughener at 1000-2000 rpm for 5 minutes at high speed; then add mineral filler and mix at 1000-2000 rpm for 5 minutes at high speed; then add wear-resistant / scratch-resistant agent, Mix at high speed for 3 minutes at 1000-2000 rpm, and finally add odor ads...

Embodiment 2

[0049] Prepare according to the following formula:

[0050] (a) 70 parts by mass of polypropylene

[0051] (b) 10 parts by mass of toughening agent (POE)

[0052] (c) 20 parts by mass of mineral filler (talcum powder)

[0053] (d) 3 parts by mass of odor adsorbent

[0054] (e) 6 parts by mass of wear-resistant agent / scratch-resistant agent

[0055] (f) 1 part by mass of other additives

[0056] Wherein, the odor adsorbent includes: bentonite, porous silica and activated alumina, according to the mass ratio, bentonite: porous silica: activated alumina=1:1:1; wear-resistant / scratch-resistant agents include TF9207, TEGOMER H-Si 6440P, according to mass ratio, TF 9207: TEGOMER H-Si 6440P=15:1.

[0057] Mix polypropylene and toughener at 1000-2000 rpm for 5 minutes at high speed; then add mineral filler and mix at 1000-2000 rpm for 5 minutes at high speed; then add wear-resistant / scratch-resistant agent, Mix at high speed for 3 minutes at 1000-2000 rpm, and finally add odor a...

Embodiment 3

[0060] Prepare according to the following formula:

[0061] (a) 70 parts by mass of polypropylene

[0062] (b) 10 parts by mass of toughening agent (POE)

[0063] (c) 20 parts by mass of mineral filler (talcum powder)

[0064] (d) 3 parts by mass of odor adsorbent

[0065] (e) 6 parts by mass of wear-resistant agent / scratch-resistant agent

[0066] (f) 1 part by mass of other additives

[0067] Wherein, the odor adsorbent includes: bentonite, porous silica and activated alumina, according to the mass ratio, bentonite: porous silica: activated alumina=1:1:1; wear-resistant / scratch-resistant agents include TF9207, TEGOMER H-Si 6440P, according to mass ratio, TF 9207: TEGOMER H-Si 6440P=20:1.

[0068] Mix polypropylene and toughener at 1000-2000 rpm for 5 minutes at high speed; then add mineral filler and mix at 1000-2000 rpm for 5 minutes at high speed; then add wear-resistant / scratch-resistant agent, Mix at high speed for 3 minutes at 1000-2000 rpm, and finally add odor a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of modified polypropylene composite material, and relates to a low-VOC scratch-resistant modified polypropylene composite material which is applicable to manufacturing automobile interior trim parts, and comprises the components based on the parts by weight: 60-90 parts of polypropylene, 5-20 parts of toughening agent, 5-20 parts of mineral filler, 0.1-4 parts of odor adsorbent, 5-15 parts of wear-resistant agent/scratch-resistant agent and 0.1-3 parts of auxiliary agent, wherein the odor adsorbent is a mixture of three selected from clay, bentonite, porous silicon dioxide, activated aluminium oxide or molecular sieve; and the wear-resistant agent/scratch-resistant agent is one or a mixture of two in polytetrafluoroethylene micro powder or reaction-type polyorganosiloxane. The modified polypropylene composite material not only has better impact-resistant performance and strength, but also has excellent scratch-resistant performance and low-VOC diffusion characteristic; and the needed raw materials have wide source and can be conveniently and easily obtained.

Description

technical field [0001] The invention belongs to the field of modified polypropylene composite materials, in particular to a polypropylene composite material modified by an anti-wear agent / scratch-resistant agent, and in particular to a low-VOC scratch-resistant modification suitable for manufacturing automotive interior parts Polypropylene composite material; the present invention also relates to a preparation method of the modified polypropylene composite material. Background technique [0002] Polypropylene is widely used in automobiles due to its low density, high cost performance, excellent heat resistance, rigidity, chemical corrosion resistance, easy processing and recycling, and has become the largest and fastest growing plastic in automobiles. The fast variety. However, polyolefins are significantly less resistant to scratches, which is a critical property for automotive interior applications such as instrument panels, consoles and door skins. Scratch resistance is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/14C08L53/00C08L27/18C08L83/04C08K13/02C08K3/34C08K3/36C08K3/22
Inventor 顾在春任俊余林华
Owner SUZHOU SUNWAY POLYMER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap