Terylene regeneration staple spandex-free mechanical elastic CVC drill fabric and production method thereof

A technology of short fiber and polyester, which is applied in the field of CVC yarn card fabric, can solve the problems of hand feeling and insufficient elasticity, and achieve the effect of saving the cost of spandex raw materials, soft and smooth hand feeling, and clear texture of the fabric

Inactive Publication Date: 2010-09-22
YIXING XINLEQI TEXTILE PRINTING & DYEING
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of fabric belongs to polyester, which has insufficient hand feeling and elasticity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Example 1, a polyester regenerated staple fiber non-spandex mechanical elastic CVC gauze fabric, gray cloth width 70 hours, gray cloth density 100 × 55 pieces / hour, cloth weight 7.5oz, 3 / 1 twill, made of polyester recycled staple fiber, Cotton yarn and cotton fiber are blended, the warp direction is made of cotton yarn, and the weft direction is a blended yarn made of polyester regenerated staple fiber and cotton fiber. The weight percentage ratio of polyester regenerated staple fiber and cotton fiber is 65:35.

[0017] The manufacturing method is:

[0018] 1. Enzyme desizing: While removing the size of the gray cloth, shrink the width of the gray cloth as much as possible, that is, pad the gray cloth on the desizing machine with the desizing working solution (the desizing working solution is composed of wide temperature enzyme and penetrant JFC, wide temperature The temperature enzyme content is 5-8g / L, the penetrant JFC content is 5±1g / L), and after dyeing, it is loos...

Embodiment 2

[0023] Example 2, a polyester regenerated staple fiber non-spandex mechanical elastic CVC yarn card fabric, gray cloth width 72 hours, gray cloth density 105 × 58 pieces / hour, cloth weight 7.75oz, 3 / 1 twill, made of polyester recycled staple fiber, Cotton yarn and cotton fiber are blended, the warp direction is made of cotton yarn, and the weft direction is a blended yarn made of polyester regenerated staple fiber and cotton fiber. The weight percentage ratio of polyester regenerated staple fiber and cotton fiber is 70:30.

[0024] The elasticity reaches 15% (ASTM D3107); without non-iron finishing, the ideal flatness effect can be achieved, and the flatness is 3.5 (after 30 times of washing and pressing, AATCC 124).

[0025] Refer to Example 1 for the manufacturing method.

Embodiment 3

[0026] Example 3, a polyester regenerated staple fiber non-spandex mechanical elastic CVC yarn card fabric, gray cloth width 68 hours, gray cloth density 102 × 56 pieces / hour, cloth weight 7.25oz, 3 / 1 twill, made of polyester recycled staple fiber, Cotton yarn and cotton fiber are blended, the warp direction is made of cotton yarn, and the weft direction is a blended yarn made of polyester regenerated staple fiber and cotton fiber. The weight percentage ratio of polyester regenerated staple fiber and cotton fiber is 75:25.

[0027] The elasticity reaches 13% (ASTM D3107); without non-iron finishing, the ideal flatness effect can be achieved, and the flatness is 3.5 (after 30 times of washing and pressing, AATCC 124).

[0028] Refer to Example 1 for the manufacturing method.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a terylene regeneration staple spandex-free mechanical elastic CVC drill fabric, belonging to the field of textile, and being produced by blending terylene regeneration staples, pure cotton yarns and cotton fibers, wherein the warp direction adopts the pure cotton yarns, the weft direction adopts blended yarns which are produced by the terylene regeneration staples and the cotton fibers, the weight percentage preparation ratio of the terylene regeneration staples and the cotton fibers is 65-75:35-25, the fabric has elasticity after a reasonable mechanical elastic organization design and a finishing technology, and the elasticity reaches 10-15% (ASTM D3107); ideal planeness effect can be realized without noniron finish, and the planeness of the fabric reaches 3.0-3.5 level (being washed for 30 times after pressing, AATCC 124); and the fabric is particularly suitable to make leisure wears of men, each index meets the requirements of customers of world brands, and the handfeel and the style are received great favor by customers.

Description

technical field [0001] The invention relates to a CVC gauze fabric, which belongs to the field of textiles, in particular to a CVC gauze fabric with recycled polyester staple fiber without spandex mechanical elasticity, and at the same time provides a method for manufacturing the fabric. Background technique [0002] Pure cotton fabrics have many advantages, such as good air permeability and softness, but they are easy to wrinkle and difficult to care for. Usually, in order to achieve a certain flatness effect, it is necessary to use a resin-added non-ironing process; the more polyester components in polyester-cotton fabrics, the more moisture-absorbing. The worse the performance, the easier it is to generate static electricity, and the feel and wearing comfort are reduced; in order to make the fabric elastic, the method of adding spandex is usually used, but the phenomenon of "orange peel" will appear after washing the fabric with spandex, which is not very scratchy and easy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D03D17/00D06B7/08D06M16/00C12S11/00D06M101/32D06M101/06D03D15/217D03D15/283D03D15/47D03D15/50D03D15/56
Inventor 甄峤源潘文英
Owner YIXING XINLEQI TEXTILE PRINTING & DYEING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com