Grease special for plastic and preparation method thereof

A grease and plastic technology, applied in the field of plastic grease, can solve the problems of lack of protection and poor high temperature resistance of plastic materials, and achieve the effect of stable colloidal stability and strong high temperature resistance.

Inactive Publication Date: 2012-11-28
福州三辰新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Soap grease is widely used in various fields due to its good lubricating properties, extreme pressure, anti-wear, waterproof and other advantages, such as bearing lubrication for aircraft, automobiles, machine tools and various mechanical equipment; it is also suitable for various Lubrication of motors, transportation, iron and steel enterprises and various other industrial machinery and equipment, etc., are widely used, but this kind of grease has no special protective effect on plastic materials, and its high temperature resistance is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Grease special for plastic and preparation method thereof
  • Grease special for plastic and preparation method thereof
  • Grease special for plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1: a kind of special lubricating grease for plastics, its preparation steps are as follows:

[0034] 1. Add 40kg of polydimethylsiloxane with a polymerization viscosity of 50mPa.s at 25°C and 10kg of polymethylphenylsiloxane with a polymerization viscosity of 150mPa.s at 25°C into the reactor, and stir evenly.

[0035] 2. Add 1kg of polytetrafluoroethylene, 0.5kg of 2,6-di-tert-butyl-p-cresol, and 0.5kg of ethylene glycol, and stir evenly.

[0036] 3. Add 6kg and the specific surface area is 230m 2 / g dehydrated hydrophobic silica treated with chlorosilane, stir well.

[0037] 4. Raise the temperature of the reaction kettle to 140°C and stir at a constant temperature for 2 hours to form the base material.

[0038] 5. Grind the base material 2 times with a three-roll mill to form fat.

[0039] 6. Carry out defoaming treatment on the obtained grease, vacuumize for 2 hours under the condition of absolute vacuum greater than 0.08MPa, stop the vacuum, and pack ...

Embodiment 2

[0040] Embodiment 2: a kind of special lubricating grease for plastics, its preparation steps are as follows:

[0041] 1. Add 70kg of polydibutylsiloxane with a polymerization viscosity of 20000mPa.s at 25°C and 40kg of polymethylphenylsiloxane with a polymerization viscosity of 150mPa.s at 25°C into the reactor, and stir evenly.

[0042] 2. Add 3kg of polytetrafluoroethylene, 1kg of 4,4'-thiobis(3-methyl-6-tert-butyl)phenol, and 2kg of polyethylene glycol, and stir evenly.

[0043] 3. Adding 14kg specific surface area is 230m 2 / g dehydrated hydrophobic silica treated with chlorosilane, stir well.

[0044] 4. Raise the temperature of the reaction kettle to 140°C and stir at a constant temperature for 2 hours to form the base material.

[0045] 5. Grind the base material 2 times with a three-roll mill to form fat.

[0046] 6. Carry out defoaming treatment on the obtained grease, vacuumize for 2 hours under the condition of absolute vacuum greater than 0.08MPa, stop the vacu...

Embodiment 3

[0047] Embodiment 3: a kind of special lubricating grease for plastics, its preparation steps are as follows:

[0048] 1. Add 40kg of polymethylvinylsiloxane with a polymerization viscosity of 2000mPa.s at 25°C and 40kg of polymethylphenylsiloxane with a polymerization viscosity of 150mPa.s at 25°C into the reactor, and stir evenly.

[0049]2. Add 2 kg of molybdenum disulfide, 0.75 kg of 2,6-di-tert-butyl-p-cresol, and 1 kg of glycerin, and stir evenly.

[0050] 3. Adding 10kg specific surface area is 230m 2 / g dehydrated hydrophobic silica treated with silazane, stir evenly.

[0051] 4. Raise the temperature of the reaction kettle to 140°C and stir at a constant temperature for 2 hours to form the base material.

[0052] 5. Grind the base material 2 times with a three-roll mill to form fat.

[0053] 6. Carry out defoaming treatment on the obtained grease, vacuumize for 2 hours under the condition of absolute vacuum greater than 0.08MPa, stop the vacuum, and pack into cans....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses grease special for plastic and a preparation method thereof. The grease comprises the following components: organopolysiloxane, an additive, a heat stabilizer, a colloid stabilizer and a thickener, wherein the additive improves lubrication of dropping points and interfaces. The grease not only has the performance of common grease, but also has the advantages of stable colloid stability, strong high temperature resistance, and a special plastic protective function.

Description

technical field [0001] The invention relates to a non-saponifiable lubricating grease material, in particular to a plastic lubricating grease with a protective effect on plastics. Background technique [0002] With the rapid development of modern industry, most of the mechanical parts have different degrees of friction during operation, such as the rotation of the shaft, the rotation of the gear, etc. In order to reduce the movement resistance and wear of the moving parts, almost all mechanical devices The rotating, sliding and rolling parts of the machine must use lubricating oil or grease. [0003] Grease can be divided into two categories according to the thickener used to prepare the grease: soap grease and non-soap grease. The thickener of soap grease is mainly fatty acid metal salt, including single soap or mixed soap and compound soap; the thickener of non-soap grease includes hydrocarbon, inorganic and organic. [0004] At present, more than 90% of the lubricating ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/00C10M107/50C10M177/00C10N40/34C10N30/08
Inventor 林鹏远朱学松林杨
Owner 福州三辰新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com