Production process of high-uniformity high-viscosity SSP (Solid State Polycondensation) polyester chip

A polyester chip and production process technology, applied in the field of chemical fiber production, can solve the problems that the SSP process cannot further improve the material flow speed, the uniformity of the chip viscosity is poor, and the production cycle is too long, so as to achieve rich process adjustment means and uniform chip crystallinity. , the effect of increasing the pre-reaction time

Active Publication Date: 2010-12-22
ZHEJIANG GUXIANDAO POLYESTER DOPE DYED YARN CO LTD
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. Due to the limitation of the pre-crystallizer and reactor, it is difficult to increase the intrinsic viscosity of slices produced by traditional SSP after a certain level. It is quite difficult to prepare slices with a viscosity above 1.05dl/g or even 1.07dl/g of;
[0006] 2. The viscosity uniformity of slices p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process of high-uniformity high-viscosity SSP (Solid State Polycondensation) polyester chip
  • Production process of high-uniformity high-viscosity SSP (Solid State Polycondensation) polyester chip
  • Production process of high-uniformity high-viscosity SSP (Solid State Polycondensation) polyester chip

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1: Production of high-uniformity and high-viscosity slices (viscosity at 1.07~1.09dl / g):

[0037]The low-viscosity chips with a viscosity of 0.67dl / g are sent from the polymer master sheet silo to two pre-crystallizers respectively. The temperature of the pre-crystallizers is controlled at 175-177°C, and the crystallization time is controlled at 12 minutes. Due to the addition of a pre-crystallizer, the input volume of the slices is greatly increased, and the crystallization time can be extended appropriately, which makes the crystallinity of the slices more uniform. The slices are transported to the top of the pre-reactor, where a roof-type reactor is installed on the top of the pre-reactor, that is, the original 4-stage pre-reactor is transformed into a 5-stage pre-reactor. When the slices pass through the uppermost ridge reactor, they will slide down from the gap of the ridge reactor and form a good and stable gradient. At this time, the slices push down a...

Embodiment 2

[0038] Embodiment 2: produce high uniformity low-viscosity chip (viscosity is at 0.96-0.98dl / g)

[0039] Low-viscosity slices with a viscosity of 0.67dl / g are sent to two pre-crystallizers from the polymer master chip silo. The temperature of the pre-crystallizers is controlled at 172-173°C, and the crystallization time is controlled at 15 minutes. Due to the addition of a crystallizer , the feeding amount of slices is greatly increased, and at the same time, the crystallization time can be extended appropriately to make the crystallinity of slices more uniform. The slices are transported to the top of the pre-reactor, where a roof-type reactor is installed on the top of the pre-reactor, that is, the original 3-stage pre-reactor is transformed into a 4-stage pre-reactor. When the slices pass through the uppermost ridge reactor, they will slide down from the gap of the ridge reactor and form a good and stable gradient. At this time, the slices push down and advance more evenly ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production process of a high-uniformity high-viscosity SSP polyester chip, belonging to the technical field of chemical fiber production and comprising the following steps of: (1) precrystallizing: respectively feeding polymerized and input chips the viscosity of about 0.67dl/g into two parallel precrystallizer from the upward side of the precrystallizers, and supplying hot air with the temperature of 177 DEG C from the downward side thereof, and then crystallizing for 12-15min and then outputting the chips from the crystallizers; (2) prereacting: feeding the chips output from the precrystallizers into a prereactor, wherein the upper part of the prereactor is additionally provided with a ridge-type reactor, and the viscosity of the chip output from the prereactor can reach 0.82dl/g; and (3) final polycondensation reaction: the maximum viscosity value of the chips output from a polycondensation reactor can reach 1.09dl/g. The invention optimizes the traditional SSP process flow, i.e. controls a precrystallizing process, a prereacting process and a final polycondensation process, thereby effectively ensuring the successful preparation of the high-uniformity high-viscosity polyester chip.

Description

Technical field: [0001] The invention relates to a high-uniformity SSP high-viscosity polyester chip production process, which belongs to the technical field of chemical fiber production. Background technique: [0002] Solid state polycondensation (SSP for short) refers to the condensation reaction of reaction materials in a solid state. In the field of polyester industrial yarn production, in order to develop higher-grade HMLS products, automotive safety belt fibers, and differentiated and functional industrial yarn products, the viscosity uniformity, molecular weight distribution, and carboxyl-end uniformity of SSP polyester chips Higher requirements are put forward, especially in the case of high viscosity, the uniformity of slice viscosity is the most intuitive requirement. [0003] At present, domestic industrial yarn manufacturers adopt different SSP processes. Different manufacturers have different technological processes: SSP implementation methods include batch an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G63/80D01F6/62
Inventor 王祖宏张朔温国奇樊继明
Owner ZHEJIANG GUXIANDAO POLYESTER DOPE DYED YARN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap