Lithium ion battery negative slurry and lithium ion battery

A lithium-ion battery and negative electrode slurry technology, which is applied to battery electrodes, secondary batteries, active material electrodes, etc., can solve the problems of poor battery performance consistency, poor battery quality consistency, and poor storage stability. Improved stability, improved normal temperature cycle performance and high temperature cycle performance, and stable storage performance

Inactive Publication Date: 2012-12-12
SHANGHAI BYD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the industrial production process of lithium-ion batteries, in order to meet the needs of mass production, the electrode slurry generally needs to stay on the production line for a long time (usually about 12 hours) after preparation. Therefore, there are certain requirements for the stability of the slurry , otherwise, the consistency of battery quality is poor
[0003] However, in the actual production process, the stability of the electrode slurry, especially the negative electrode slurry, often deteriorates when stored for a long time, and sedimentation and agglomeration occur, which makes the performance consistency of the battery worse and affects product quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium ion battery negative slurry and lithium ion battery
  • Lithium ion battery negative slurry and lithium ion battery
  • Lithium ion battery negative slurry and lithium ion battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1. Preparation of lithium-ion battery negative electrode sheet:

[0020] 5000 grams of artificial graphite, 90 grams of CMC with a weight average molecular weight of 400,000, 90 grams of SBR, 4500 grams of deionized water, and 4.5 grams of phenol were mixed and stirred evenly to obtain negative electrode slurry A1.

[0021] Coat the negative electrode slurry A1 obtained in the previous step on a copper foil with a thickness of 8um, dry at 90°C, press into sheets, and then cut into negative electrode sheets of length × width × thickness = 479mm × 43.5mm × 0.13mm , Each negative plate contains 2.95 grams of artificial graphite.

[0022] Preparation of positive electrode sheet of lithium ion battery: 5000 grams of lithium cobaltate, 75 grams of PVDF binder with a weight average molecular weight of 700,000, 150 grams of conductive agent carbon powder, 1500 grams of NMP, mixed and stirred evenly to obtain positive electrode slurry.

[0023] 2. Coat the positive electrode sl...

Embodiment 2

[0026] 5000 grams of artificial graphite, 90 grams of CMC with a weight average molecular weight of 400,000, 90 grams of SBR, 4500 grams of deionized water, and 450 grams of phenol were mixed and stirred evenly to obtain negative electrode slurry A2. Others are the same as embodiment 1.

Embodiment 3

[0028] 5000 grams of artificial graphite, 90 grams of CMC with a weight average molecular weight of 400,000, 90 grams of SBR, 4500 grams of deionized water, and 0.45 grams of phenol were mixed and stirred evenly to obtain negative electrode slurry A3. Others are the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to lithium ion battery negative slurry ad a lithium ion battery using the negative slurry, belonging to the field of lithium ion batteries. The invention adopts the technical scheme of adding a preservative capable of inhibiting the biodegradation of cellulose ether to the negative slurry, so that the technical problems of poor performance and performance consistence of the manufactured battery because the negative slurry has agglomeration and sedimentation after staying long time on the production line to reduce stability in industrial production are solved. The normal temperature cycle performance of the battery is improved.

Description

technical field [0001] The invention relates to a lithium ion battery negative electrode slurry and a lithium ion battery using the slurry. Background technique [0002] In the industrial production process of lithium-ion batteries, in order to meet the needs of mass production, the electrode slurry generally needs to stay on the production line for a long time (usually about 12 hours) after preparation. Therefore, there are certain requirements for the stability of the slurry , otherwise, the consistency of the battery quality is poor. [0003] However, in the actual production process, the stability of the electrode slurry, especially the negative electrode slurry, often deteriorates during long-term storage, and sedimentation and agglomeration occur, thereby deteriorating the performance consistency of the battery and affecting product quality. Contents of the invention [0004] In order to solve the technical problem that the stability of negative electrode slurry det...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/02H01M4/62H01M10/36H01M10/40
CPCY02E60/12Y02E60/10
Inventor 李海彦徐海英王涌雷磊
Owner SHANGHAI BYD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com