Method for preparing polypropylene fiber with anti-mosquito function

A technology of polypropylene fiber and polypropylene resin, which is applied in the field of polypropylene fiber preparation, can solve the problems of easy volatilization, easy decomposition, and few types of mosquito repellents, achieve good mosquito repellent effect, good processing performance, and improve anti-mosquito The effect of washing performance

Inactive Publication Date: 2011-02-09
DONGHUA UNIV
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are many kinds of anti-mosquito agents or anti-mosquito drugs, many of the commonly used anti-mosquito agents in daily life are extracted from plants, which have the characteristics of low melting point and boiling point, volatile and easy to decompose at high temperature, so blending and melting There are not many types of mosquito repellants available for spinning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing polypropylene fiber with anti-mosquito function
  • Method for preparing polypropylene fiber with anti-mosquito function
  • Method for preparing polypropylene fiber with anti-mosquito function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] After the purified 5 grams of FWJ and 495 grams of polypropylene resin slices were stirred and mixed, they were fed into a twin-screw extruder for blending and granulation to obtain mosquito-resistant spinning chips with a mosquito repellent content of 1%. Slicing method for melt spinning. The feeding screw speed is 50r / min, the main screw speed is 120r / min, the twin-screw extruded filaments are cooled in a water bath, and the anti-mosquito masterbatch is obtained by pelletizing with a pelletizer. The cutting speed is 400r / min, and the twin-screw extrusion The temperature of each zone of the machine is as follows:

[0024]

[0025] The above-mentioned anti-mosquito slices are spun on the spinning machine with full slice method, the pump supply rate is 4g / min, and the anti-mosquito primary fibers are prepared under the condition of cold air blowing, the component pressure is about 40 kg, and the winding speed is 400 m / min . The spinning temperature is as follows:

...

Embodiment 2

[0029] 15 grams of FWJ after purification and 485 grams of polypropylene resin chips are fed into a twin-screw extruder after being stirred and mixed for blending and granulation to obtain mosquito-proof spinning chips with a mosquito-repellent content of 3%. The speed of the feed screw is 50r / min, the speed of the main screw is 120r / min, the filaments extruded by the twin-screw are cooled in a water bath, and cut into pellets by a pelletizer to obtain the anti-mosquito masterbatch, the cutting speed is 400r / min, the twin-screw extruder The temperature of each zone is as follows:

[0030]

[0031] The above-mentioned anti-mosquito slices are spun on the spinning machine by the full slice method, the pump supply rate is 10g / min, and the anti-mosquito primary fibers are prepared under the condition of cold air blowing, the component pressure is about 40 kg, and the winding speed is 400 m / min . The spinning temperature is as follows:

[0032]

[0033] The as-spun fiber ob...

Embodiment 3

[0035] After the purified 50 grams of FWJ and 450 grams of polypropylene resin slices were stirred and mixed, they were fed into a twin-screw extruder for blending and granulation to obtain mosquito repellent masterbatches with a mosquito repellent content of 10%. The speed is 50r / min, the speed of the main screw is 120r / min, the twin-screw extruded filaments are cooled in a water bath, and the anti-mosquito masterbatch is obtained by pelletizing with a pelletizer. The cutting speed is 400r / min, and the temperature in each zone of the twin-screw extruder as follows:

[0036]

[0037] Get above-mentioned anti-mosquito master batch 100 grams and 400 grams of pure polypropylene resin chips to mix and carry out master batch method spinning (the content of anti-mosquito agent is 2%) on the spinning machine, pump feed rate 6g / min, cold blowing The as-spun fibers were prepared under the following conditions, the component pressure was about 40 kg, and the winding speed was 400 m / m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
boiling pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing a polypropylene fiber with anti-mosquito function, which comprises the following steps of: (1) mixing a mosquito repellent and dried polypropylene resin slices and preparing anti-mosquito master batches or anti-mosquito spinning slices by using a double-screw extruder; (2) blending the prepared anti-mosquito master batches and pure polypropylene resin slices for melt spinning, or directly performing melt spinning on the prepared anti-mosquito spinning slices by a whole section method; and (3) drawing an as-spun fiber for shaping. The method is simple and suitable for industrial production; and the prepared fiber has good anti-mosquito effect and the washing fastness of the fiber is improved.

Description

technical field [0001] The invention belongs to the field of polypropylene fiber preparation, in particular to a preparation method of polypropylene fiber with anti-mosquito function. Background technique [0002] In real life, especially in hot summer, people are often bitten by mosquitoes, which spread diseases through contact with human blood and affect human health. In the prior art, people generally use some anti-mosquito agents to post-treat the fibers or fabrics, or use microcapsules to coat the anti-mosquito drugs, and then arrange them on the surface of the fibers or fabrics. In this method, the anti-mosquito agents or The anti-mosquito drug is only attached to the surface of the fiber and has poor washing resistance. [0003] The insecticide or anti-mosquito agent is added to the chips before spinning for blending and melt spinning, and the anti-mosquito functional components are evenly dispersed in the fiber instead of just adhering to the fiber surface, which ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/12D01D5/08D01F1/10D01F6/46
Inventor 陈彦模蔡再生陈龙李秋林张瑜魏发云张小丽闫坤
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap