Method for preparing anti-mosquito EVA (Ethylene-Vinyl Acetate copolymer) shoe sole material

A shoe sole material and anti-mosquito technology, which is applied in the field of shoe sole materials, can solve the problems of affecting the appearance, easy wrinkling of the surface, and lack of anti-mosquito function, etc., to achieve the effect of improving anti-mosquito performance, improving antibacterial performance, and improving compatibility

Inactive Publication Date: 2016-04-27
SUZHOU JINGRO TECH
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The shoe material provided by this patent overcomes the defect that the surface of the traditional EVA foam shoe material is easy to wrinkle and affects the appearance, but it does not have the same anti-mosquito function as the EVA shoe material on the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of preparation method of anti-mosquito EVA sole material, its step is as follows:

[0024] (1) The citronella grass is pulverized with a pulverizer to obtain the citronella grass powder, and the citronella grass powder is added to the supercritical CO 2 The pressure in the extraction tank is 12 MPa, the temperature is 40 ℃ and extracting for 2 hours, obtains the extract solution, carries out secondary extraction to the extract solution with diethyl ether, takes out the diethyl ether layer and dries with blast drier for 2 hours, obtains the citronella extract for later use;

[0025] (2) Apatite was ball milled with a ball mill for 5 hours, and the citronella extract obtained in step (1) was added to a mixer and stirred at room temperature for 4 hours to obtain a citronella mixture, and the citronella mixture was added with a mass fraction of 70%. In the ethanol solution, after stirring evenly, add the silane coupling agent WD-10 to ultrasonically disperse for 2 ho...

Embodiment 2

[0028] A kind of preparation method of anti-mosquito EVA sole material, its step is as follows:

[0029] (1) The citronella grass is pulverized with a pulverizer to obtain the citronella grass powder, and the citronella grass powder is added to the supercritical CO 2 The pressure in the extraction tank is 12 MPa, the temperature is 40 ℃ and extracting for 2 hours, obtains the extract solution, carries out secondary extraction to the extract solution with diethyl ether, takes out the diethyl ether layer and dries with blast drier for 2 hours, obtains the citronella extract for later use;

[0030] (2) Apatite was ball milled with a ball mill for 5 hours, and the citronella extract obtained in step (1) was added to a mixer and stirred at room temperature for 4 hours to obtain a citronella mixture, and the citronella mixture was added with a mass fraction of 70%. In the ethanol solution, after stirring evenly, add the silane coupling agent WD-10 to ultrasonically disperse for 2 ho...

Embodiment 3

[0033] A kind of preparation method of anti-mosquito EVA sole material, its step is as follows:

[0034] (1) The citronella grass is pulverized with a pulverizer to obtain the citronella grass powder, and the citronella grass powder is added to the supercritical CO 2 The pressure in the extraction tank is 12 MPa, the temperature is 40 ℃ and extracting for 2 hours, obtains the extract solution, carries out secondary extraction to the extract solution with diethyl ether, takes out the diethyl ether layer and dries with blast drier for 2 hours, obtains the citronella extract for later use;

[0035] (2) Apatite was ball milled with a ball mill for 5 hours, and the citronella extract obtained in step (1) was added to a mixer and stirred at room temperature for 4 hours to obtain a citronella mixture, and the citronella mixture was added with a mass fraction of 70%. In the ethanol solution, after stirring evenly, add the silane coupling agent WD-10 to ultrasonically disperse for 2 ho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for preparing an anti-mosquito EVA (Ethylene-Vinyl Acetate copolymer) shoe sole material. The method comprises the following steps: (1) crushing lemon grass by a crusher so as to prepare lemon grass powder, adding the lemon grass powder into a supercritical CO2 extraction pool for extracting so as to obtain extract liquor, carrying out re-extraction by using diethyl ether, taking out a diethyl ether layer, and then, carrying out drying, so as to obtain a lemon grass extract for later use; (2) carrying out ball-milling on apatite, adding apatite powder and the lemon grass extract into a stirrer, carrying out stirring at room temperature so as to obtain a lemon grass-apatite mixture, adding the lemon grass-apatite mixture into an ethanol solution, carrying out uniform stirring, then, adding a coupling agent into the solution for ultrasonic dispersion, transferring the dispersion solution into a constant-temperature water bath, carrying out stirring, carrying out discharging, then, carrying out suction filtration and washing, and carrying out drying, so as to obtain a modified lemon grass-apatite mixture for later use; (3) pouring EVA, zinc white, stearic acid and the modified lemon grass-apatite mixture into a Banbury mixer for first-stage mixing, adding diisopropylbenzene hyperoxide and azobisformamide into the Banbury mixer for second-stage mixing, then, carrying out roll mixing and granulating so as to obtain granules, carrying out injection molding, and carrying out baking, thereby obtaining the anti-mosquito EVA shoe sole material. The shoe sole material prepared by the method has a very good anti-mosquito function.

Description

Technical field: [0001] The invention relates to a shoe sole material, in particular to a preparation method of an anti-mosquito EVA shoe sole material. Background technique: [0002] Shoe material is the main application field of EVA resin in my country. In the EVA resin used in shoe material, the content of vinyl acetate is generally 15% to 22%. Compared with polyethylene, due to the introduction of vinyl acetate monomer in the molecular chain, EVA reduces high crystallinity, improves flexibility, impact resistance, filler compatibility and heat sealing performance, and also has good cushioning and shock resistance. , Moisture-proof, anti-chemical corrosion, non-toxic, non-absorbent and other advantages, it is widely used in the soles and interior materials of middle and high-end travel shoes, hiking shoes, slippers, sandals. In addition, this material is also used in the field of sound insulation panels, gym mats and sealing materials. Shunde and Zhongshan in Guangdong,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08K13/06C08K9/12C08K9/06C08K9/00C08K5/00C08J9/10A43B13/04
CPCA43B13/04C08J9/103C08J2323/08C08K5/0058C08K9/00C08K9/06C08K9/12C08K13/06C08L2201/08C08L2203/14C08L23/0853Y02P20/54
Inventor 黄超
Owner SUZHOU JINGRO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com