Deoxidation and restoration method for smelting stainless steel in converter
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A converter smelting, stainless steel technology, applied in the direction of manufacturing converters, etc., can solve the problems of increasing stainless steel manufacturing costs and high prices of ferrosilicon
Active Publication Date: 2011-04-27
SHANXI TAIGANG STAINLESS STEEL CO LTD
View PDF2 Cites 9 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Silicon carbide has a strong reducing ability, and the price of ferrosilicon is relat
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
[0051] The weight percent of 80 silicon carbide components is:
[0052] SiC 82%; Free C 5.8%; S 0.05; SiO 9%; Moisture 0.4%;
[0053] Fire reduction of 2.75%.
[0054] The carbon, silicon and phosphorus components (percentage by weight) in the dephosphorized hot metal are:
[0055] C 3.8%; Si 0.08%; P 0.016%;
[0056] Requirements for C, Si, Mn and Cr (weight percent) in KOBMS converter tapping 409L:
[0057] C 0.20-0.40; Si 0.15-0.30; Mn 0.10-0.25; Cr 12.10-12.50.
[0058] This embodiment is:
[0059] C 0.32; Si 0.20; Mn 0.20; Cr 12.30.
[0060] The deoxidation reduction method embodiment of this converter smelting stainless steel is the followi...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a deoxidation and restoration method for smelting stainless steel in a converter. The method comprises the following steps of: (1) smelting stainless steel in a converter: blending dephosphorized molten iron in the converter, blowing in high-pressure oxygen and nitrogen in a flow ratio of 1 to (2.53-3.5) for decarburization and temperature rise, adding high-carbon chromium iron, high-carbon ferromanganese iron, steelmaking lime and caustic-burned dolomite to the converter in batch from a storage bin at the top of the converter, wherein the dephosphorized molten iron contains the following components in percentage by weight: 3.0-4.0 percent of C, not more than 0.1 percent of Si and not more than 0.025 percent of P, the molten iron contains 0.20-0.40 percent of carbon, and the contents of chromium and nickel reach a control range of a corresponding steel grade; and (2) restoring: calculating the amount of needed pure silicon to be added, converting into the amount of silicon carbide, adding fluorite, flushing nitrogen, stirring and restoring so that the amount of Cr2O3 in the converter is not more than 0.5 percent. The eoxidation and restoration method for smelting stainless steel in the converter can decrease the costs of the raw materials.
Description
technical field [0001] The invention relates to a deoxidation reduction method for smelting stainless steel in a converter. Background technique [0002] In the production of stainless steel by KOBMS converter, a certain amount of reducing agent needs to be added after the reduction period begins to reduce the metal oxides entering the slag during the oxygen blowing smelting period. The deoxidation reduction method of converter smelting stainless steel is to use ferrosilicon or ferrosilicon plus aluminum as reducing agent. Silicon carbide has a strong reducing ability, and the price of ferrosilicon is relatively high, which correspondingly increases the manufacturing cost of stainless steel. Contents of the invention [0003] In order to overcome the above-mentioned shortcomings of the existing deoxidation-reduction method for smelting stainless steel with a converter, the present invention provides a deoxidation-reduction method for smelting stainless steel with a lower ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more