A technology of black masterbatch and carbon black, which is applied in the field of high-concentration black masterbatch and its preparation, can solve the problems of poor dispersibility of carbon melanin, low blackness and brightness, and low concentration of black masterbatch, and achieves good dyeing effect, The effect of high brightness and high carbon black concentration

Inactive Publication Date: 2011-05-04
SHENZHEN KEJU NEW MATERIAL
View PDF1 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing black masterbatch has the disadvantages of low concentration, pollut

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Black master batch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example 1:

[0024] Formula: LLDPE6201 15%

[0025] Degussa 900L 70%

[0026] PE wax 5%

[0027] EBS 9.4%

[0028] Antioxidant 1076 0.4%

[0029] Coupling agent KH-550 0.2%

[0030] Preparation method: first pre-mix according to the formula ratio, then mix evenly in a high-speed mixer (rotating speed 1500r / min), then add to the internal mixer, banbury at 150°C for 10 minutes, and pulverize the obtained material with crushing equipment. Finally, the pulverized material is added to a twin-screw extruder for extruding, and it is eagerly cut in water, cooled and dried to obtain the required masterbatch.

[0031] The process is as follows: twin screw first stage temperature 180-200℃, second stage temperature 180-200℃, third stage temperature 180-200℃, fourth stage temperature 180-200, fifth stage temperature 170-180, sixth stage temperature 170-180, Seven-stage temperature 170-180, eight-stage temperature 170-180, die temperature 190-210.

Example Embodiment

[0032] Example 2:

[0033] Formula: LLDPE6201 11%

[0034] Degussa 900L 80.4%

[0035] PE wax 3%

[0036] TAS-2A 5%

[0037] Antioxidant 1076 0.4%

[0038] Coupling agent KH-550 0.2%

[0039] Preparation method: first pre-mix according to the formula ratio, then mix evenly in a high-speed mixer (rotating speed 1500r / min), then add to the internal mixer, banbury at 150°C for 10 minutes, and pulverize the obtained material with crushing equipment. Finally, the pulverized materials are added to a twin-screw extruder for extrusion, hot-cut in water, cooled, and dried to obtain the required masterbatch.

Example Embodiment

[0040] Example 3

[0041] Formula: LLDPE620 15%

[0042] Degussa 900L 89.4%

[0043] PE wax 3%

[0044] TAS-2A 2%

[0045] Antioxidant 1076 0.4%

[0046] Coupling agent KH-550 0.2%

[0047] Preparation method: first pre-mix according to the formula ratio, then mix evenly in a high-speed mixer (rotating speed 1500r / min), then add to the internal mixer, banbury at 150°C for 10 minutes, and pulverize the obtained material with crushing equipment. Finally, the pulverized material is added to a twin-screw extruder for extruding, and it is eagerly cut in water, cooled and dried to obtain the required masterbatch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a black master batch and a preparation method thereof. The black master batch comprises the following components in percentage by weight: 5-15% of carrier resin, 70-90% of carbon black, 5-15% of dispersion lubricating agent and 0.6-1% of other auxiliaries. The black master batch prepared by the formula disclosed by the invention has the characteristics of high carbon black concentration, good dyeing effect, good dispersion high blackness brightness and no influence to mechanical properties of products compared with the existing black master batch, thus being widely applied to polyolefine resin and ABS (acrylonitrile butadiene styrene) resin.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a high-concentration black masterbatch and a preparation method thereof. Background technique [0002] Black masterbatch is mainly used in chemical fiber products (carpets, polyester, non-woven fabrics, etc.), blown film products (packaging bags, cast films, multi-layer composite films, etc.), blown products (medicine and cosmetic containers, paint containers, etc.) , Extruded products (sheets, pipes, cables, wires, etc.), injection products (auto parts, electrical appliances, building materials, daily necessities, toys, sporting goods, etc.). It is easy to use, has no pollution to the molding environment, has uniform and stable coloring, improves the quality of plastic parts, is easy to measure, and can be applied to a molding production system with a high degree of automation. It can integrate coloring, anti-aging agents, and antistatic agents in one place. Made of m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08K13/02C08K3/04B29B9/06C08L23/00C08L55/02
Inventor 徐东徐永程必舒
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap