High wear-resistant and cold-resistant toughened nylon composite material

A nylon composite material, cold-resistant and toughening technology, which is applied in the field of high-wear-resistant, cold-resistant and toughened nylon composite materials to achieve the effects of good mechanical properties and low temperature resistance, broad market application prospects and low cost.

Active Publication Date: 2011-05-11
SHANGHAI KINGFA SCI & TECH +1
View PDF1 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At home and abroad, the research on toughening nylon to improve its low-temperature resistance is increasingly in-depth, but there are few literature reports on the research on the wea

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] Example 1

[0027] The composition and weight percentage of the high wear-resistant, cold-resistant and toughened nylon composite material of this embodiment are as follows:

[0028] Nylon resin 91.5%

[0029] Toughening agent 2%

[0030] Anti-wear agent 5%

[0031] Processing aid 1.5%

[0032] The nylon resin is nylon 66 (PA66), the toughening agent is maleic anhydride grafted polyolefin elastomer POE, the anti-wear agent is polytetrafluoroethylene powder, and the processing aid is copper salt.

[0033] The preparation process of the high wear-resistant, cold-resistant and toughened nylon composite material is as follows:

[0034] A) Add nylon resin, toughening agent, anti-wear agent and processing aid into the high mixer according to the proportion, and mix them evenly at room temperature;

[0035] B)Using twin-screw extruder for extrusion granulation, the process conditions of extrusion granulation are: temperature in zone one is 240℃, temperature in zone two is 280℃, temperature ...

Example Embodiment

[0036] Example 2

[0037] The composition and weight percentage of the high wear-resistant, cold-resistant and toughened nylon composite material of this embodiment are as follows:

[0038] Nylon resin 76.5%

[0039] Toughening agent 6%

[0040] Anti-wear agent 15%

[0041] Processing aid 1.5%

[0042] The nylon resin is nylon 66 (PA66), the toughening agent is maleic anhydride grafted polyolefin elastomer POE, the anti-wear agent is polytetrafluoroethylene powder, and the processing aid is copper salt.

[0043] The preparation process of the highly wear-resistant, cold-resistant and toughened nylon composite material of this embodiment is the same as that of Example 1.

Example Embodiment

[0044] Example 3

[0045] The composition and weight percentage of the high wear-resistant, cold-resistant and toughened nylon composite material of this embodiment are as follows:

[0046] Nylon resin 74.5%

[0047] Toughening agent 9%

[0048] Anti-wear agent 15%

[0049] Processing aid 1.5%

[0050] The nylon resin is nylon 66 (PA66), the toughening agent is maleic anhydride grafted polyolefin elastomer POE, the anti-wear agent is polytetrafluoroethylene powder, and the processing aid is copper salt.

[0051] The preparation process of the highly wear-resistant, cold-resistant and toughened nylon composite material of this embodiment is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high wear-resistant and cold-resistant toughened nylon composite material, which comprises the following components in percentage by weight: 69.5 to 95 percent of nylon resin, 2 to 9 percent of toughening agent, 0.5 to 20 percent of wear-resisting agent and 1 to 2 percent of processing aid, wherein the toughening agent is maleic anhydride grafted polymer, and the wear-resisting agent is molybdenum disulfide or polytetrafluoroethylene micropowder. The product has higher wear resistance and better mechanical properties and low-temperature resistance, can be used for preparing relatively moving parts such as wearing plates and centre plates in the industries such as railway locomotives and automobiles, and can greatly improve the working stability of the parts and prolong the service life of the parts; in addition, the preparation process for the product is simple and low in cost and meets the requirement of industrial production; therefore, the high wear-resistant and cold-resistant toughened nylon composite material has wide market application prospect.

Description

technical field [0001] The invention relates to a high wear-resistant, cold-resistant and toughened nylon composite material that can be used to prepare parts with relative motion, and belongs to the technical field of modified nylon composite materials. Background technique [0002] Although nylon resin has excellent comprehensive properties such as high mechanical strength, heat resistance, self-lubricating property, excellent barrier performance and chemical corrosion resistance, it can be widely used in the fields of machinery manufacturing, electronic appliances and transportation, but Pure nylon also has obvious disadvantages, such as: high water absorption, poor dimensional stability of the product; poor low temperature performance, which restricts its use in low temperature environments; although it has certain self-lubricating properties, its friction Coefficients do not meet the requirements of use. In order to meet the needs of industrial development, in recent y...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/00C08L77/06C08K3/30C08L27/18
Inventor 丁正亚冯德才张永苏妤
Owner SHANGHAI KINGFA SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products