Precursor composition of polyimide and method for preparing polyimide

A technology of polyimide and composition is applied in the field of precursor composition of polyimide, which can solve the problems of time-consuming process, side chain damage, safety problems and the like

Active Publication Date: 2011-05-18
ETERNAL MATERIALS CO LTD
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the composition is limited only to imidization by heating
Generally speaking, the imidization by heating requires several hours of heating at a high temperature of 250° C. to 350° C. to obtain 100% imidization. This process is time-consuming and prone to safety problems, and When the product has side chains with lower bond energy, the high temperature environment tends to destroy the side chains before cyclization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Precursor composition of polyimide and method for preparing polyimide
  • Precursor composition of polyimide and method for preparing polyimide
  • Precursor composition of polyimide and method for preparing polyimide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0122] 2.181 grams (0.01 moles) of pyromellitic dianhydride (pyromellitic dianhydride, hereinafter referred to as PMDA) were dissolved in 200 grams of N-methyl-2-pyrrolidinone (N-methyl-2-pyrrolidinone; hereinafter referred to as NMP), The resulting mixture was heated to 50°C and the reaction was stirred for two hours. 2.322 g (0.02 mol) of 2-hydroxyethyl acrylate (2-Hydroxyethyl acrylate, hereinafter referred to as HEA) was added dropwise, and reacted and stirred at a constant temperature of 50° C. for two hours. Thereafter, 20.024 grams (0.1 mole) of 4,4'-oxidized dianiline (4,4'-oxy-dianiline, hereinafter referred to as ODA) was added to the solution, and after it was completely dissolved, 18.0216 grams (0.09 mol) of PMDA, reacted and stirred for six hours at a constant temperature of 50°C. Then 3.243 g (0.02 mol) of N, N'-carbonyldiimidazole (N, N'-Carbonyldiimidazole; CDI) was added, and the reaction was stirred at a constant temperature of 50° C. for one hour.

Embodiment 2

[0126] 2.181 grams (0.01 mol) of PMDA were dissolved in 200 grams of NMP, heated to 50°C and the reaction was stirred for two hours. 2.60 g (0.02 mol) of 2-hydroxyethyl methacrylate (2-hydroxyethyl methacrylate; hereinafter referred to as HEMA) was slowly added dropwise, and the reaction was stirred at a constant temperature of 50° C. for two hours. Add 20.024 g (0.1 mole) of ODA to the solution, and after it is completely dissolved, add 18.0216 g (0.09 mole) of PMDA, react and stir for six hours at a constant temperature of 50°C. Then add 3.243g (0.02mol) of CDI, react and stir at a fixed temperature of 50°C for one hour.

Embodiment 3

[0128] 2.181 grams (0.01 mol) of PMDA were dissolved in 200 grams of NMP, heated to 50°C and the reaction was stirred for two hours. 2.322 g (0.02 mol) of HEA was slowly added dropwise, and the reaction was stirred at a constant temperature of 50° C. for two hours. Add 10.814 grams (0.1 moles) of p-phenylenediamine (para-phenylenediamine, hereinafter referred to as pPDA) to the solution, and after it is completely dissolved, add 18.0216 grams (0.09 moles) of PMDA, and react with stirring at a constant temperature of 50°C six hours. Then add 3.243g (0.02mol) of CDI, react and stir at a fixed temperature of 50°C for one hour.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a precursor composition of polyimide and a method for preparing polyimide. The precursor composition of the polyimide comprises an acid amide oligomer which is shown as a formula (1) and a dicarboxylic anhydride derivative which is shown as a formula (2) and of which the tail end is provided with an ester group, namely (-C(O)OR) and a carboxyl group, namely (-C(O)OH), wherein R, G, G1, P, D and m are defined in the specifications. The invention also provides polyimide synthesized from the precursor composition.

Description

[0001] This application is a divisional application of the Chinese patent application with application number 200910001935.0; [0002] The filing date of the original application is: January 14, 2009; [0003] The application number of the original application is: 200910001935.0; [0004] The invention title of the original application is: polyimide precursor composition and method for preparing polyimide. [0005] Precursor composition of polyimide and method for preparing polyimide technical field [0006] The present invention relates to a polyimide (polyimide, PI for short) precursor composition, and the present invention also relates to the application of the composition in the preparation of polyimide. Background technique [0007] Polyimide has always been the first choice for high-performance polymer materials due to its excellent thermal stability and good mechanical, electrical and chemical properties. In addition, due to the higher and higher requirements on th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G73/10C08G73/12
Inventor 吴仲仁郑弼仁
Owner ETERNAL MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap