Composite materials

A technology of composite materials and resin materials, which is applied in the field of manufacturing fiber-reinforced composite materials, can solve the problems of reducing the mechanical properties of compression and structural parts, etc., and achieve the effect of low adhesion and mutual adhesion

Inactive Publication Date: 2011-05-18
GURIT (UK) LTD
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This "loss of shape" causes some out-of-plane waviness to unidirectional fibers which degrades compressive mechanical properties since the fibers will tend to deform earlier under compressive loads
[0011] In addition, there are further technical problems in the use of full

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite materials
  • Composite materials
  • Composite materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0155] In this example, a sixteen-layer multilayer laminate of an elongated prepreg of the present invention was formed to make an elongated rod. Each prepreg is made of 1600g / m2 impregnated with 32wt% epoxy resin 2 Constructed of 4800tex unidirectional E-glass fibers, these epoxy resins are referred to as "Resin Example 1" and have the properties summarized below, resulting in a final cured laminate thickness of 20mm.

[0156] Resin "Resin Example 1" comprises an epoxy resin having the following properties:

[0157] Thermal reactivity was measured using a differential scanning calorimeter (Mettler Toledo DSC821E) as a feature. The program used was to increase the temperature from 25°C to 250°C at a rate of 10°C / min, then cool to 25°C and increase to 150°C.

[0158] ΔH (J / g) 242

[0159] T 初始 (℃) 133.4

[0160] T 峰顶 (℃) 150

[0161] T 终止 (°C) 181.2

[0162] Cold Tg2(℃) 9.7

[0163] UTg2(°C) 104.5

[0164] Viscoelasticity measurements can be made at application tempe...

Embodiment 2 and comparative example 2-6

[0194] Experiments were carried out in two modes using a rheometer to test and characterize the rheological properties of prepregs.

[0195] In the first flow experiment, a constant shear stress was applied to the prepreg and the shear strain was recorded. This test is used to characterize the lower viscosity properties of a prepreg to achieve resin flow and wet-out during its cure cycle.

[0196] In a third experiment, vibratory shear strain testing was used to study viscoelastic properties at typical prepreg lay-up temperatures to characterize the material's higher viscosity and viscoelastic handling properties.

[0197] Prepregs known in the art (see Comparative Examples 2-6) and prepregs according to an embodiment of the present invention (see Example 2) were tested using the above-mentioned TA Instruments AR2000 rheometer having a disposable aluminum plate with a diameter of 25 mm. Characterization was performed to measure its storage modulus, loss modulus and complex vi...

Embodiment 3-5 and comparative example 7-10

[0206] Seven resins were tested to determine the relationship between their phase angle δ and temperature. Figure 13 It is a graph showing the relationship between phase angle δ and temperature of seven resins in Examples 3-5 of the present invention and Comparative Examples 7-10.

[0207] It can be seen that for Examples 3-5, the transition between low and high phase angles δ (indicated by a sharp change in phase angle δ) occurs in the temperature range of 10-25°C. This means that at least one temperature value within this range, the phase angle δ has a value of 50-70°, which in turn shows that at least one temperature value within this temperature range, the resin has low tack and Good combination of deformability. Prepregs containing such resins can be deformed, yet have good inter-ply venting of any air present between adjacent prepreg layers during vacuum consolidation.

[0208]In contrast, for Comparative Examples 7-10, the transition between low phase angle δ and hig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Complex viscosityaaaaaaaaaa
Storage modulusaaaaaaaaaa
Loss modulusaaaaaaaaaa
Login to view more

Abstract

A prepreg for manufacturing a fibre-reinforced composite material, the prepreg comprising a layer of a layer of fibrous reinforcement fully impregnated by a matrix resin material, wherein at least the surface of the resin material has a viscosity and a tack at room temperature, and each prepreg has a stiffness at room temperature, such that when two of the prepregs are disposed as a vertical stack thereof at room temperature with adjacent resin material surfaces, the adjacent resin material surfaces are unadhered and form continuous air paths therebetween.

Description

technical field [0001] The present invention relates to prepregs for the manufacture of fibre-reinforced composite materials. Further, the invention relates to the use of such prepregs in the manufacture of fiber-reinforced composite materials and a method for the manufacture of fiber-reinforced composite materials. Background technique [0002] For many years, in the field of fibre-reinforced composites, it has been known to provide prepregs comprising layers of fibrous reinforcement impregnated with a structural polymer resin. The amount of structural polymer resin is carefully matched to the amount of fiber reinforcement. Thus, prepregs can be used in a method of forming fiber reinforced composites in which a multilayer stack of prepregs having a desired shape and configuration is provided and the The multi-layer laminate is heated so that the structural polymer resin melts and solidifies to form a single uniform resin matrix in which the fiber reinforcement is arranged...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J5/24B29B11/16B29B15/12B29C70/44B29C70/54
CPCB29C70/547B29B11/16B29K2707/04B29K2105/246B29C70/44B29B15/122B29K2063/00B29K2709/08C08J2363/00C08J5/24B29K2105/0872B29K2077/10B29C70/302C08J5/244B29B15/08B29C70/06B29C70/50
Inventor 尼古拉斯·邓肯·帕廷顿保罗·约翰·斯潘塞丹尼尔·托马斯·琼斯
Owner GURIT (UK) LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap