Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cemented carbide and hard phase technology, applied in the field of cemented carbide materials, can solve the problems of WC grain growth, poor cobalt oxidation resistance and corrosion resistance, and cemented carbide cannot adapt to the working environment. Achieve the effect of low manufacturing cost and stable quality
Inactive Publication Date: 2011-05-25
ZHUZHOU LIZHOU CEMENTED CARBIDE
View PDF3 Cites 9 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] At present, the main grades of cemented carbide plates are YG15, YG20, etc. In the production process of these grades, WC powder of a single specification is used for production. The disadvantage of a single powder is that it cannot make the material have the characteristics of high strength and high hardness at the same time. That is to say, the product cannot have the characteristics of wear resistance and impact resistance at the same time; while the bonding component is only one element of cobalt, but the oxidation resistance and corrosion resistance of cobalt are poor, which makes the plate prone to corrosion in wire cutting and EDM And defects such as cracks; at the same time, at high temperature, WC grains dissolve in liquid cobalt, which easily leads to abnormal growth of WC grains
With the expansion of the use range of cemented carbide plates and its application in various environments, traditional cemented carbide can no longer adapt to the increasingly complex and changeable working environment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] The present invention comprises the following steps,
[0012] (1), get the raw material of following weight percent, the composite hard phase tungsten carbide powder 10% of 10-15 micron particle, the composite hard phase tungsten carbide powder 30% of 5-10 micron particle, the 1.0-1.5 micron particle Composite hard phase tungsten carbide powder 30%, chromium carbide powder 1.5%, cobalt powder 28.5%;
[0013] (2) The raw materials are mixed according to the proportion, ground, pressed and formed, and then kept at 1500°C for 30 minutes to obtain the cemented carbide material.
Embodiment 2
[0015] It includes the following steps,
[0016] (1), get the raw material of following weight percentage, the composite hard phase tungsten carbide powder 15% of 10-15 micron particle, the composite hard phase tungsten carbide powder 30% of 5-10 micron particle, the 1.0-1.5 micron particle Composite hard phase tungsten carbide powder 25%, chromium carbide powder 2%, cobalt powder 28%;
[0017] (2) The raw materials are mixed according to the proportion, ground, pressed and formed, and then kept at 1600° C. for 30 minutes to obtain the cemented carbide material.
Embodiment 3
[0019] It includes the following steps,
[0020] (1), get the raw material of following weight percent, the composite hard phase tungsten carbide powder 20% of 10-15 micron particle, the composite hard phase tungsten carbide powder 28% of 5-10 micron particle, the 1.0-1.5 micron particle Composite hard phase tungsten carbide powder 25%, chromium carbide powder 1.5%, cobalt powder 25.5%;
[0021] (2) The raw materials are mixed according to the proportion, ground, pressed and formed, and then kept at 1550° C. for 30 minutes to obtain the cemented carbide material.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a method for manufacturing hard alloy materials, which comprises the following steps: 1. taking the following raw material substances in percentage by weight: 10 to 20 percent of composite hard phase tungsten carbide powder in a particle form of 10 to 15 microns, 20 to 30 percent of composite hard phase tungsten carbide powder in a particle form of 5 to 10 microns, 20 to 30 percent of composite hard phase tungsten carbide powder in a particle form of 1.0 to 1.5 microns, 1.5 to 2 percent of chromium carbide powder and 25 to 30 percent of cobalt powder; and 2. mixing the raw material substances according to the mixture ratio, grinding, pressing and forming the materials, then, carrying out heat insulation for 30 minutes under the condition between 1500 DEG C and 1600 DEG C, and obtaining the hard alloy materials. The method provided by the invention is simple and reliable, and the produced hard alloy materials belong to the hard alloy materials with the advantages of wear resistance, impact resistance, stable quality and bicrystal corrosion resistance.
Description
technical field [0001] The invention relates to a method for manufacturing hard alloy materials. Background technique [0002] At present, the main grades of cemented carbide plates are YG15, YG20, etc. In the production process of these grades, WC powder of a single specification is used for production. The disadvantage of a single powder is that it cannot make the material have the characteristics of high strength and high hardness at the same time. That is to say, the product cannot have the characteristics of wear resistance and impact resistance at the same time; while the bonding component is only one element of cobalt, but the oxidation resistance and corrosion resistance of cobalt are poor, which makes the plate prone to corrosion in wire cutting and EDM And defects such as cracks; at the same time, at high temperature, WC grains dissolve in liquid cobalt, which easily leads to abnormal growth of WC grains. With the expansion of the use range of cemented carbide pla...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).