Port machine cable storage basket sling cable sheath rubber and preparation method thereof

A technology of cable sheath and cable storage basket, which is applied in the manufacture of cable sheath rubber of port machinery cable storage basket spreader, and in the field of port machinery cable storage basket spreader cable sheath rubber, which can solve the problem of short service life, harsh environment, Changeable wind direction and other issues, to achieve the effect of good anti-aging performance and superior mechanical properties

Inactive Publication Date: 2011-06-15
JIANGSU YUANYANG DONGZE CABLE
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The cable storage basket of the port mechanical spreader is close to the sea, and it is operated outdoors. The wind is strong, the environment is harsh, and the wind direction is changeable. The cable will shake a lot in this environment. The cable is distorted and deformed, and the cable is easy to fall off from the cable storage basket when it is retracted; in order to reduce the shaking, the weight of the cable itself is often increased, so the cable sheath rubber is required to have superior mechanical properties, corrosion resistance, and aging resistance. The cable sheath rubber is difficult to meet this requirement, and the service life is often very short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Port machine cable storage basket sling cable sheath rubber and preparation method thereof
  • Port machine cable storage basket sling cable sheath rubber and preparation method thereof
  • Port machine cable storage basket sling cable sheath rubber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The preparation steps of sheath rubber are as follows:

[0018] (1) Prepare raw materials according to the following components and weight content: chlorinated polyethylene 352: 26.5 parts; magnesium oxide: 2.5 parts; 2,2,4-trimethyl-1,2-dihydroquinoline polymer: 0.3 Parts; Paraffin: 0.25 parts; Diisooctyl sebacate (DOS): 3.5 parts; Trioctyl trimellitate (TOTM): 2.0 parts; White carbon black: 1.5 parts; Antimony trioxide: 1.2 parts; Chlorinated paraffin 70: 1.2 parts; lead stearate: 0.3 parts; tri-salt: 0.2 parts; calcined clay: 6 parts; A-172 vinyl tris (b-methoxyethoxy): 0.2 parts; Wear-resistant carbon black: 3 parts; semi-reinforcing carbon black: 3 parts; dicumyl peroxide (DCP): 0.85 parts; triallyl cyanurate (TAC): 1 part;

[0019] (2) First mix chlorinated polyethylene 352 for 4 minutes, then add magnesium oxide, antioxidant RD, paraffin, diisooctyl sebacate, trioctyl trimellitate, white carbon black, antimony trioxide , chlorinated paraffin 70, lead stearate, ...

Embodiment 2

[0032] The preparation steps of sheath rubber are as follows:

[0033] (1) Prepare raw materials according to the following components and weight content: chlorinated polyethylene 352: 26.5 parts; magnesium oxide: 3 parts; 2,2,4-trimethyl-1,2-dihydroquinoline polymer: 0.5 Parts; paraffin: 0.5 parts; diisooctyl sebacate: 4.0 parts; trioctyl trimellitate: 2.5 parts; white carbon black: 2.0 parts; antimony trioxide: 1.5 parts; lead stearate: 0.5 parts; three salts: 0.4 parts; calcined clay: 8 parts; vinyl tris(b-methoxyethoxy): 0.3 parts; high wear-resistant carbon black: 4 parts; Strong carbon black: 4 parts; Dicumyl peroxide: 1 part; Triallyl cyanurate: 1.5 parts;

[0034] (2) First mix chlorinated polyethylene 352 for 4 minutes, then add magnesium oxide, antioxidant RD, paraffin, DOS, TOTM, white carbon black, antimony trioxide, chlorinated paraffin 70, lead stearate, three Salt, calcined clay, A-172, high wear-resistant carbon black, semi-reinforcing carbon black and mixed ...

Embodiment 3

[0038] The preparation steps of sheath rubber are as follows:

[0039] (1) Prepare raw materials according to the following components and weight content: chlorinated polyethylene 352: 26.5 parts; magnesium oxide: 2.8 parts; 2,2,4-trimethyl-1,2-dichloroquinoline polymer: 0.4 parts; paraffin: 0.35 parts; diisooctyl sebacate: 3.75 parts; trioctyl trimellitate: 2.25 parts; white carbon black: 1.75 parts; antimony trioxide: 1.35 parts; 1.35 parts; Lead stearate: 0.4 parts; Tri-salt: 0.3 parts; Calcined clay: 7 parts; Vinyl tri(b-methoxyethoxy): 0.25 parts; Reinforcing carbon black: 3.5 parts; Dicumyl peroxide: 0.92 parts; Triallyl cyanurate: 1.25 parts;

[0040] (2) First mix chlorinated polyethylene 352 for 4 minutes, then add magnesium oxide, antioxidant RD, paraffin, DOS, TOTM, white carbon black, antimony trioxide, chlorinated paraffin 70, lead stearate, three Salt, calcined clay, A-172, high wear-resistant carbon black, semi-reinforcing carbon black and mixed and stirred ev...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a port machine cable storage basket sling cable sheath rubber and a preparation method thereof, belonging to the field of cables. The sheath rubber comprises the following components: 26.5 parts of chlorinated polyethylene 352, 2.5-3 parts of magnesium oxide, 0.3-0.5 part of antioxidant RD, 0.25-0.5 part of paraffin wax, 3.5-4.0 parts of DOS (Dioctyl Sebacate), 2.0-2.5 parts of TOTM (Trioctyl Trimellitate), 1.5-2.0 parts of white carbon black, 1.2-1.5 parts of diantimony trioxide, 1.2-1.5 parts of chlorinated paraffin 70, 0.3-0.5 part of lead stearate, 0.2-0.4 part of three salts, 6-8 parts of calcined clay, 0.2-0.3 part of A-172, 3-4 parts of high-abrasion carbon black, 3-4 parts of semi-reinforcing carbon black, 0.85-1 part of DCP (Dibasic Calcium Phosphate) and 1-1.5 parts of triallyl cyanurate (TAC). The preparation method of the port machine cable storage basket sling cable sheath rubber comprises the following steps of: firstly, blending the chlorinated polyethylene 352, adding the magnesium oxide and the like, blending and stirring uniformly; pouring filtered rubber into an internal mixer, adding the DCP and the TAC, blending uniformly, and blanking; and making the mixture into five triangular packages in an open mill, rolling for five times and delivering out sheets. The sheath rubber has excellent mechanical properties and good corrosion resistance and aging resistance.

Description

technical field [0001] The invention relates to a cable, in particular to a cable sheath rubber for a cable storage basket spreader of a port machine. The invention also relates to a method for manufacturing cable sheath rubber of a cable storage basket spreader of a port machine. Background technique [0002] The cable storage basket of the port machinery spreader is close to the sea, and it is operated outdoors. The wind is strong, the environment is harsh, and the wind direction is changeable. The cable will shake a lot in this environment, and the cable core and its outer sheath must constantly withstand a certain range The cable is distorted and deformed, and the cable is easy to fall off from the cable storage basket when it is retracted; in order to reduce the shaking, the weight of the cable itself is often increased, so the cable sheath rubber is required to have superior mechanical properties, corrosion resistance, and aging resistance. High-quality cable sheath r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/28C08K13/02C08K3/22C08K5/11C08K5/12C08K3/36C08K5/098C08K3/34C08K3/04C08K5/14C08K5/3492H01B3/44B29C47/92B29C48/92
CPCB29C48/92B29C2948/92514B29C2948/92704B29C2948/92895B29C2948/92904B29C2948/92923
Inventor 李永江陆云春
Owner JIANGSU YUANYANG DONGZE CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products