Method for producing regenerative heavy denier profiled polyester staple fibres

A polyester staple fiber and production method technology, applied in fiber processing, single-component polyester artificial filament, filament/thread forming, etc., can solve the problems of slow cooling speed, poor cooling effect, large fiber difference, etc., and achieve Save energy and resources, low cost, and good flexibility

Active Publication Date: 2011-06-15
广东秋盛资源股份有限公司
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing melt-spinning method produces special-shaped fibers. The fibers coming out of the spinneret are only cooled by the ring air. Because the cooling speed of the ring air is slow and the cooling effect is poor, the cross-section of the spun fiber is quite different from the cross-section of the spinneret hole. Large, unable to achieve the effect of "alien"

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] A production method of regenerated coarse denier profiled polyester staple fiber. The main steps include: selecting high-quality regenerated polyester bottle flakes and spinning them into cross-sectional profiled fibers through drying, melt spinning, cooling, stretching, and shaping. This implementation method , Is to make the following improvements and adjustments in the above conventional process:

[0023] A) Recycled polyester bottle flakes, after drying, the moisture content of the material is below 80PPM;

[0024] B) After drying, the recycled polyester bottle flakes are melted and extruded at high temperature by the screw, the melting temperature is controlled between 270~285℃, and the spinning box temperature is controlled at 275~278℃;

[0025] C) The cooling device adopts water spray and annular air dual-purpose cooling device;

[0026] F) The spray speed of water mist is 3.8~4.0m / s, and the water temperature is ≤30℃;

[0027] G) The ring blowing speed is 3.8~4.0m / s, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for producing regenerative heavy denier profiled polyester staple fibres. The method comprises the following main procedures: selecting high-quality regenerative polyester bottle chips and spinning the bottle chips to form fibres with profiled sections through drying, melting spinning, cooling, drawing and setting. The method has the following main characteristics: A) after being dried, the moisture contents of the regenerative polyester bottle chips are below 80PPM; B) the melting temperature is controlled between 270 DEG C and 285 DEG C and the spin beam temperature is controlled between 275 DEG C and 278 DEG C; and C) a mist and recirculating air dual-purpose cooling device is adopted for cooling, the mist spray speed is 3.8-4.0m / s and the water temperature is not more than 30 DEG C. The method has the following positive effects: by adopting the cooling method and device combining mist spray cooling and recirculating air cooling for the fibres which are extruded, melted and spouted, the good setting property of the profiled sections of the fibres is ensured and the problem that the sections of the fibres tend to be round due to surface tension existing when the polymer melt is extruded from the spinneret orifice is solved, so that the fibres have multidimensional reflecting effects as the diamond shaped mirrors.

Description

Technical field [0001] The invention relates to a production method for producing recycled coarse denier profiled polyester fibers by using water mist spraying and circulating air while cooling, in particular to a production method for spinning profiled polyester fibers using waste mineral water bottle flakes (regenerated polyester bottle flakes). Background technique [0002] The present invention is to deal with the environmental pollution caused by more and more discarded mineral water bottles at present, to recycle the waste mineral water bottles, to melt at high temperature through a temperature control system, and to spun a new type of environmentally friendly special-shaped polyester fiber as a garment , The warming raw materials for bedding and the raw materials for audio production to realize high-value-added products of high-performance fiber products and environmentally friendly fibers. [0003] Special-shaped fibers are mainly manifested in fibers with different shapes ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01D5/088D01D5/253D01F6/62
Inventor 马义忠马秋镇付文虎张开友段明述周小兵李林娟
Owner 广东秋盛资源股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap