Bamboo pellet fuel and manufacture method thereof

A technology of pellet fuel and manufacturing method, which is applied in the direction of fuel, solid fuel, biofuel, etc., can solve the problems of high ash content, high combustion value, and unfavorable environmental protection, and achieve low ash content, high combustion value, and harmful substances. The effect of low content

Inactive Publication Date: 2011-07-13
吴谦
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantage of this type of pellet fuel is that it has a large combustion value, but the disadvantage is that it has a high ash content after combustion. It has been tested that the ash content of this type of fuel contains a variety of toxic and harmful substances, which is not conducive to the protection of the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] Bamboo pellet fuel, its raw material contains 60% bamboo chips, and the rest is wood chips; the moisture content of the bamboo pellet fuel is less than 10%, the combustion value is ≥ 4050kcal / kg, the ash content is 1.0-1.5%, and the sulfur content is ≤ 0.06%, density ≥ 1.1g / cm 3 , bulk density ≥ 0.68g / cm 3 .

[0072] The above-mentioned bamboo pellet fuel is manufactured by the following method:

[0073] ① Send bamboo chips and wood chips to the air dryer for drying, the drying temperature is controlled at 100°C, and the moisture content of bamboo chips and wood chips is controlled at 14% to 17%;

[0074] ② Mix the above-mentioned dried bamboo chips and wood chips in a ratio of 3:2, and then crush them into fine powder to obtain the material;

[0075] ③ Feed the material obtained in step ② into the reformed granulator and press it into granules;

[0076] ④ Send the granules prepared in step ③ into the cooling and screening combination machine, cool to 40°C and then ...

Embodiment 2

[0082] Bamboo pellet fuel, its raw material contains 70% bamboo chips, and the rest is wood chips; the moisture content of the bamboo pellet fuel is less than 10%, the combustion value is ≥ 4200kcal / kg, the ash content is 1.0-1.4%, and the sulfur content is ≤ 0.06%, density ≥ 1.1g / cm 3 , bulk density ≥ 0.68g / cm 3 .

[0083] The above-mentioned bamboo pellet fuel is manufactured by the following method:

[0084] ①Send bamboo chips and wood chips into the air dryer for drying, the drying temperature is controlled at 120°C, and the moisture content of bamboo chips and wood chips is controlled at 14% to 17%;

[0085] ② Mix the above-mentioned dried bamboo chips and wood chips in a ratio of 7:3, and then crush them into fine powder to obtain the material;

[0086] ③ Feed the material obtained in step ② into the reformed granulator and press it into granules;

[0087] ④ Send the granules prepared in step ③ into the cooling and screening combination machine, cool to 40°C and then...

Embodiment 3

[0091] Bamboo pellet fuel, its raw material contains 80% bamboo chips, and the remaining components are wood chips and straw chips; the moisture content of the bamboo pellet fuel is less than 10%, the combustion value is ≥ 4400kcal / kg, and the ash content is 1.0-1.3%. Sulfur content≤0.06%, density≥1.1g / cm 3 , bulk density ≥ 0.68g / cm 3 .

[0092] The above-mentioned bamboo pellet fuel is manufactured by the following method:

[0093] ①Send bamboo chips, wood chips and straw chips into the air dryer for drying, the drying temperature is controlled at 120°C, and the moisture content of bamboo chips and wood chips is controlled at 14% to 17%;

[0094] ② mixing the above-mentioned dried bamboo chips, wood chips and straw chips in a ratio of 8:1:1, and then pulverizing them into fine powder to obtain the material;

[0095] ③ Feed the material obtained in step ② into the reformed granulator and press it into granules;

[0096] ④ Send the granules prepared in step ③ into the cooli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a bamboo pellet fuel and a manufacture method thereof, belonging to the technical field of biomass energy utilization. The bamboo pellet fuel is characterized in that raw materials in the fuel at least comprise 60 percent of bamboo bits and the balance of wood bits or straw bits, wherein the water content of the bamboo fuel is less than 10 percent, the combustion value is4-50-4800kcal / kg, the ash content is 1.0-1.5 percent, the sulfur content is not more than 0.06 percent, the density is not less than 1.1g / cm<3> and the accumulation density is not less than 0.68g / cm<3>. The bamboo pellet fuel has the advantages of large combustion value, low ash content and low content of harmful materials. The bamboo pellet fuel has faint scent during the combustion and a function of refreshing and restoring consciousness.

Description

technical field [0001] The invention relates to a bamboo particle fuel and a manufacturing method thereof, belonging to the technical field of biomass energy utilization. Background technique [0002] Many of the current biomass pellet fuels are compressed from agricultural waste such as straw and peanut shells. For example, the Chinese patent No. 200610046801.7 discloses a "biomass pellet fuel", which is made of 92-94 parts of straw powder, 1-2 parts of mugwort and 5-6 parts of water and extruded by a granulator. Granules; the patent No. is the Chinese patent of 200710034411.2, which is pressed into granules after being mixed with sweet potatoes or potatoes with a weight ratio of 100:2-5 by the biomass pellet fuel with a particle size below 14% and a particle size of less than 8mm. The disadvantage of this type of pellet fuel is the low combustion value. There are also biomass pellet fuels that use sawdust as the main raw material, such as the Chinese patent No. 200410046...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10L5/44
CPCY02E50/30Y02E50/10
Inventor 吴向武杨吉荣余金芳
Owner 吴谦
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com