Antiseptic rubber lining and preparation method thereof

An anti-corrosion rubber and natural rubber technology, applied in the field of chemical anti-corrosion materials, can solve problems such as whether the anti-corrosion performance can not meet the requirements, and achieve the effect of solving the problem of anti-corrosion performance, good anti-corrosion performance, and easy to achieve

Inactive Publication Date: 2011-07-27
TAICANG KUBO ANTI CORROSION MATERIAL
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After research, it is found that the form of rubber after vulcanization has some of the above characteristics, but it is only natural rubber after vulcanization, and its anti-corrosion performance is far from meeting the requirements. Tensile strength, etc. need to be studied a lot

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antiseptic rubber lining and preparation method thereof
  • Antiseptic rubber lining and preparation method thereof
  • Antiseptic rubber lining and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of anticorrosion rubber lining, comprises the component of following parts by weight:

[0022]

[0023] The production method is as follows:

[0024] (1) Add the No. 1 standard rubber, 1502-type styrene-butadiene rubber and peptizer Struktol A82 into the internal mixer, and masticate for 12 minutes at 60°C to form plastic rubber;

[0025] (2) Add high styrene, graphite powder, sulfur, TMTM promotor and dispersant in the above-mentioned masticated rubber, and knead in the internal mixer for 15 minutes at 80° C. to form a mixed rubber;

[0026] (3) above-mentioned mixed rubber is carried out refining in open mill, makes triangular bag 4 times, enters filter machine to filter then;

[0027] (4) Carry out the second milling of the above-mentioned filtered mixed rubber on the open mill, cut into strips and enter the film cooler to cool to 30°C for storage and wait for extrusion;

[0028] (5) Extrude the stored film into an extruder.

Embodiment 2

[0030] A kind of anticorrosion rubber lining, comprises the component of following parts by weight:

[0031]

[0032] The production method is as follows:

[0033] (1) Add the No. 1 standard rubber, 1502-type styrene-butadiene rubber and peptizer Struktol A82 into the internal mixer, and masticate for 10 minutes at 80°C to form plastic rubber;

[0034] (2) Add high styrene, graphite powder, sulfur, TMTM accelerant and dispersing agent of formulation amount to above-mentioned masticated rubber, under the condition of 65 ℃, knead in described internal mixer for 10min to form mixed rubber;

[0035] (3) The above-mentioned mixed rubber is carried out in an open mill, and the triangular bag is made 3 times, and then enters the filter to filter;

[0036] (4) Carry out the second milling of the above-mentioned filtered mixed rubber on the mill, cut into strips and enter the film cooler to cool to 28°C for storage and wait for extrusion;

[0037] (5) Extrude the stored film into ...

Embodiment 3

[0039] A kind of anticorrosion rubber lining, comprises the component of following parts by weight:

[0040]

[0041]

[0042] The production method is as follows:

[0043] (1) Add the No. 1 standard rubber, 1502-type styrene-butadiene rubber and peptizer Struktol A82 into the internal mixer, and masticate for 15 minutes at 70°C to form plastic rubber;

[0044] (2) Add high styrene, graphite powder, sulfur, TMTM accelerant and dispersant of formulation amount to above-mentioned masticated rubber, under the condition of 50 ℃, knead in described internal mixer for 12min to form mixed rubber;

[0045] (3) above-mentioned mixed rubber is carried out refining in open mill, makes triangular bag 5 times, enters filter machine to filter then;

[0046] (4) Carry out the second milling of the above-mentioned filtered mixed rubber on the open mill, cut into strips and enter the film cooler to cool to 30°C for storage and wait for extrusion;

[0047] (6) Extrude the stored film in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antiseptic rubber lining which comprises 20-40 parts of nature rubber, 8-16 parts of butadiene styrene rubber, 0.5-1.5 parts of peptizer, 8-16 parts of high styrene, 10-20 parts of graphite powder, 20-30 parts of sulfur, 0.5-2 parts of high-speed accelerator and 2-4 parts of dispersing agent. The invention also discloses a preparation method of the antiseptic rubber lining. The antiseptic rubber lining disclosed by the invention has excellent corrosion resisting property on various acid and alkali media; and the problem of the corrosion resisting property of a steelmaterial is solved, so that the effective service life of a steel member can be prolonged by 10 to 20 years; and the lining is applied to a smoke absorption column in a waste incineration factory, a kettle operating at a high temperature, a storage tank and other steel members, and has the characteristics of excellent combination property, high hardness, high-temperature resistance, pressure resistance, wearing resistance, tension stress, good ductility and the like. The preparation process is simple, can be used in a workshop or in site operation, and the hot water or steam is used for vulcanization, thereby being easy to realize.

Description

technical field [0001] The invention relates to the field of chemical anticorrosion materials, in particular to an anticorrosion rubber lining and a preparation method thereof. Background technique [0002] The pure steel equipment used in the production process of the chemical industry and metallurgical industry, such as containers, has been subject to internal and external corrosion of different chemical substances, and it is prone to rust and wear after a long time, which will cause damage to the equipment and seriously affect Production Process. Corrosion of steel structure materials has been a problem that has plagued all walks of life. Due to the high temperature and high pressure resistance of steel structure materials, other materials such as plastics cannot be replaced. Therefore, the surface of steel structure materials can be anti-corrosion without affecting the characteristics of steel materials Processing research is of great significance. [0003] In the prio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/06C08K3/04C08K3/06C08F291/02
Inventor 李杰
Owner TAICANG KUBO ANTI CORROSION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com