Method for producing high-visibility polyurethane artificial leather

A manufacturing method and polyurethane technology, which are used in textiles and papermaking, devices for applying liquid to surfaces, coatings, etc. Simple process and improved hydrolysis resistance

Active Publication Date: 2012-10-03
FUZHOU FUYING PLASTIC & RUBBER PRODS
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing fluorescent fabrics have poor light fastness and easy fading on the surface, which cannot meet the requirements of EN471 or ANSI / ISEA107 standards, resulting in a decline in performance and seriously affecting the service life of the finished product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of manufacture method of highly visible polyurethane artificial leather, comprises the steps:

[0033] Step 10: Prepare the required slurry: specifically include the following steps:

[0034] Step 11: Prepare the surface layer slurry, the surface layer slurry is prepared according to the following weight ratio:

[0035] Polycarbonate polyurethane 100 parts

[0036] 10 parts of dimethylformamide

[0037] 0.1 parts of waterproofing agent

[0038] Modified polysiloxane defoamer 0.1 part

[0039] Anti-aging agent 0.1 parts

[0040] 5 parts of water-based fluorescent color paste.

[0041] After the prepared surface layer slurry is fully mixed and stirred, it is filtered through 200 mesh and degassed by a vacuum degassing machine for later use;

[0042] Step 12: Prepare the adhesive layer slurry, the adhesive layer slurry is prepared according to the following weight ratio:

[0043] Polyurethane 100 parts

[0044] 10 parts of dimethylformamide

[0045] 1 part ...

Embodiment 2

[0051] A kind of manufacture method of highly visible polyurethane artificial leather, comprises the steps:

[0052] Step 10: Prepare the required slurry: specifically include the following steps:

[0053] Step 11: Prepare the surface layer slurry, the surface layer slurry is prepared according to the following weight ratio:

[0054] Polycarbonate polyurethane 100 parts

[0055] 150 parts of dimethylformamide

[0056] 1 part waterproofing agent

[0057] Modified polysiloxane defoamer 3 parts

[0058] Anti-aging agent 5 parts

[0059] 50 parts of water-based fluorescent color paste.

[0060] After the prepared surface layer slurry is fully mixed and stirred, it is filtered through 200 mesh and degassed by a vacuum degassing machine for later use;

[0061] Step 12: Prepare the adhesive layer slurry, the adhesive layer slurry is prepared according to the following weight ratio:

[0062] Polyurethane 100 parts

[0063] 100 parts of dimethylformamide

[0064] 8 parts of UV...

Embodiment 3

[0070] A kind of manufacture method of highly visible polyurethane artificial leather, comprises the steps:

[0071] Step 10: Prepare the required slurry: specifically include the following steps:

[0072] Step 11: Prepare the surface layer slurry, the surface layer slurry is prepared according to the following weight ratio:

[0073] Polycarbonate polyurethane 100 parts

[0074] 80 parts of dimethylformamide

[0075] 35 parts of toluene

[0076] Butanone 20 parts

[0077] 0.5 parts of waterproofing agent

[0078] Modified polysiloxane defoamer 0.5 parts

[0079] Anti-aging agent 0.5 parts

[0080] 30 parts of water-based fluorescent color paste.

[0081] After the prepared surface layer slurry is fully mixed and stirred, it is filtered through 200 mesh and degassed by a vacuum degassing machine for later use;

[0082] Step 12: Prepare the adhesive layer slurry, the adhesive layer slurry is prepared according to the following weight ratio:

[0083] Polyurethane 100 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing high-visibility polyurethane artificial leather, comprising the following steps: blending a surface course sizing agent, wherein the surface course sizing agent is prepared from the raw materials comprising polycarbonate type polyurethane, dimethyl fomamide, a waterproof agent, a modified polysiloxane defoamer, an antiager and an aqueous fluorescencepigment; fully mixing and blending the blended surface course sizing agent; filtering by utilizing a 200-mesh sieve; defoaming by utilizing a vacuum defoaming machine for standby; blending an adhesive coating sizing agent, wherein the coating sizing agent is prepared the raw materials comprising polyurethane, dimethyl fomamide, a ultraviolet light absorber, an accelerant and a cross linking agent; fully mixing and blending the blended coating sizing agent; filtering by utilizing the 200-mesh sieve for standby; and coating. In the method, the existing formula is regulated, produced products completely conform to the requirements of EN471 high-visibility materials, and the aspects such as weather resistance, hydrolysis resistance, waterproof vapor permeability and the like all exceed the similar products in the market.

Description

【Technical field】 [0001] The invention relates to a method for manufacturing polyurethane artificial leather, in particular to a method for manufacturing highly visible polyurethane artificial leather. 【Background technique】 [0002] With the development of society and the improvement of people's living standards, the society pays more and more attention to various safety protection, and the demand for various high-visibility materials is increasing. Fluorescent materials are bright in color and have good visual effects. They are widely used in luggage and clothing fabrics, and are also deeply loved by consumers. Especially in Europe and the United States, there is a great demand for highly visible protective clothing with warning signs. However, the existing fluorescent fabrics have poor light fastness and easy fading on the surface, which cannot meet the requirements of EN471 or ANSI / ISEA107 standards, resulting in reduced performance and seriously affecting the service l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06N3/12B05D7/12B05D7/24
Inventor 潘则荣
Owner FUZHOU FUYING PLASTIC & RUBBER PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com