An optical film, adhesive type technology, applied in the direction of film/sheet adhesive, adhesive type, ester copolymer adhesive, etc., can solve problems such as poor durability, coloration, and decreased near-infrared absorption capacity , to achieve the effect of reducing the number of layer structures and high pigment durability

Inactive Publication Date: 2011-09-28
TOMOEGAWA PAPER CO LTD
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The durability of the diimonium-based pigments may be poor, and the near-infrared absorption ability may be lowered or coloring may be caused.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bonding type optical film and adhesive composition
  • Bonding type optical film and adhesive composition
  • Bonding type optical film and adhesive composition

Examples

Experimental program
Comparison scheme
Effect test

manufacture example 1

[0108]

[0109] Butyl acrylate (412.7 g), methyl acrylate (117.9 g), and acrylic acid (10.4 g) were weighed and mixed well as monomers to obtain a polymerizable monomer mixture (A1). 160 g of ethyl acetate and 300 g of the polymerizable monomer mixture (A1) were charged into the flask. In addition, 300g of the polymerizable monomer mixture (A1), 16g of ethyl acetate and 0.15g of Naipa-BMT-K40 (polymerization initiator, produced by NOF Co., Ltd.) were added to the dropping funnel, and fully mixed to make a solution for dropping. Mixture (A2). While blowing nitrogen gas at 20ml / min, the temperature in the flask was raised to 95°C, and the polymerization initiator Naipa-BMT-K40 (0.15g) was put into the flask to initiate the polymerization reaction. The dropping mixture (A2) was dropped from the dropping funnel over 90 min. After completion of dripping the mixture for dripping (A2), aging was performed for 6 hours while diluting with ethyl acetate according to the increase in ...

manufacture example 2

[0110]

[0111] Butyl acrylate (458.6 g), methyl acrylate (131.0 g), and acrylic acid (10.4 g) were weighed and mixed well as monomers to obtain a polymerizable monomer mixture (B1). 160 g of ethyl acetate and 300 g of the polymerizable monomer mixture (B1) were charged into the flask. In addition, 300g polymerizable monomer mixture (B1), 16g ethyl acetate and 0.15g Naipa-BMT-K40 (polymerization initiator, produced by NOF Co., Ltd.) were added in the dropping funnel, and fully mixed to make the mixture for dropping ( B2). While blowing nitrogen gas at 20ml / min, the temperature inside the flask was raised to 95°C, and the polymerization initiator Naipa-BMT-K40 (0.15g) was put into the flask to initiate the polymerization reaction. The dropping mixture (B2) was dropped from the dropping funnel over 90 min. After completion of dripping the mixture for dripping (B2), aging was performed for 6 hours while diluting with ethyl acetate according to the increase in viscosity, and a...

manufacture example 3

[0112]

[0113] Butyl acrylate (409.1 g), methyl acrylate (116.9 g), and acrylic acid (15.6 g) were weighed and mixed well as monomers to obtain a polymerizable monomer mixture (C1). 160 g of ethyl acetate and 300 g of the polymerizable monomer mixture (C1) were charged into the flask. In addition, 300g of the polymerizable monomer mixture (C1), 16g of ethyl acetate and 0.15g of Naipa-BMT-K40 (polymerization initiator, produced by NOF Co., Ltd.) were added to the dropping funnel, and fully mixed to make a solution for dropping. Mixture (C2). While blowing nitrogen gas at 20 ml / min, the temperature inside the flask was raised to 95° C., and the polymerization initiator Naipa-BMT-K40 (0.15 g) was put into the flask to initiate the polymerization reaction. The dropping mixture (C2) was dropped from the dropping funnel over 90 min. After completion of dripping the mixture for dripping liquid (C2), aging was performed for 6 hours while diluting with ethyl acetate according to t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a bonding type optical film and an adhesive composition. The invention provides a method for improving the endurance of pigments in a bonding layer having a diimide pigment. The bonding type optical film includes a near infrared ray absorbability bonding layer having a acrylic acid series polymer and diimide pigment, and a base material layer. Needle-shaped aggregates are scattered in the near infrared ray absorbability bonding layer.

Description

technical field [0001] The present invention relates to an adhesive optical film and an adhesive composition. More specifically, the present invention relates to an adhesive optical film having a near infrared absorbing adhesive layer and an adhesive composition for forming the adhesive layer thing. Background technique [0002] In terms of its light-emitting principle, the plasma display can emit electromagnetic waves, neon light, and near-infrared rays while emitting visible light. Due to the adverse effects of these rays, it is necessary to shield them. Therefore optical films are used. [0003] In addition to the above-mentioned functions, in order to improve image quality by providing multiple functions such as preventing reflection on the audience side and improving contrast, an optical film laminated with multiple layers is used. However, in recent years, there is a demand for simplifying these optical films, and there is a tendency to reduce the cost by simplifyin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G02B5/22C09J11/06C09J7/02C09J133/00G09F9/313G02B1/10C09J163/00C09J175/04G09F9/00
CPCB05D5/10C09J7/22C09J7/29C09J7/38C09J7/385C09J11/06C09J133/04C09J2203/318C09J2301/302C09J2301/312C09J2301/408
Inventor 土师圭一朗后藤义宏
Owner TOMOEGAWA PAPER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap