Production method for mixed grinding material

A technology of abrasive materials and production methods, applied in chemical instruments and methods, other chemical processes, etc., can solve problems such as unsatisfactory effects, and achieve the effect of reducing polishing quality and reducing surface damage

Active Publication Date: 2011-11-16
无锡成旸科技股份有限公司
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the surface quality of the object is controlled by controlling the proportion of the abrasive during the grinding process, but the effect of this method is not satisfactory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: A kind of production method of novel hybrid grinding material, comprises the following processing steps: its formula proportion is counted by weight:

[0020] (1) Mixing: put zirconium silicate and alumina micropowder into the mixing tank and mix, the mass ratio of zirconium silicate and alumina micropowder is 1:0.8;

[0021] (2) Ball milling: Mill the mixed fine powder on a ball mill for 3 hours to obtain mixed fine powder with a particle size of 10-11 μm;

[0022] (3) Put 300 parts of ball-milled mixed micropowder, 800 parts of water and 1 part of dispersant into the sorting barrel, and fully stir at a stirring speed of 300 rpm for 60 minutes; after stirring, let it settle, Settling time is 10min;

[0023] (4) Sorting:

[0024] a. Use a siphon to suck out the upper layer slurry in the sorting bucket once, then add clear water to the initial liquid level before the siphon in the sorting bucket; then stir, settle, and siphon, and the stirring speed is 30...

Embodiment 2

[0028] Embodiment two: a kind of production method of novel hybrid grinding material, comprises the following processing steps: its formula ratio is counted by weight:

[0029] (1) Mixing: Put zirconium silicate and alumina micropowder into the mixing tank and mix, the mass ratio of zirconium silicate and alumina micropowder is 1: 1.2;

[0030] (2) Ball milling: Mill the mixed fine powder on a ball mill for 8 hours to obtain mixed fine powder with a particle size of 10-11 μm;

[0031] (3) Put 500 parts of ball-milled mixed micropowder, 1000 parts of water and 5 parts of dispersant into the sorting barrel, and fully stir at a stirring speed of 500 rpm for 5 minutes; after stirring, let it settle, Settling time is 30min;

[0032] (4) Sorting:

[0033] a. Use a siphon to suck out the upper layer slurry in the sorting bucket once, then add clear water to the initial liquid level before the siphon in the sorting bucket; then stir, settle, and siphon, the stirring speed is 500 rpm...

Embodiment 3

[0037] Embodiment three: a kind of production method of novel hybrid grinding material, comprises the following processing steps: its formula ratio is counted by weight parts:

[0038] (1) Mixing: Put zirconium silicate and alumina micropowder into the mixing tank and mix, the mass ratio of zirconium silicate and alumina micropowder is 1:1;

[0039] (2) Ball milling: Mill the mixed fine powder on a ball mill for 5 hours to obtain mixed fine powder with a particle size of 10-11 μm;

[0040] (3) Put 400 parts of ball-milled mixed micropowder, 900 parts of water and 3 parts of dispersant into the sorting barrel, and fully stir at a stirring speed of 400 rpm for 30 minutes; after stirring, let it settle, Settling time is 20min;

[0041] (4) Sorting:

[0042] a. Use a siphon to suck out the upper layer slurry in the sorting bucket once, then add clear water to the initial liquid level before the siphon in the sorting bucket; then stir, settle, and siphon, and the stirring speed i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a novel production method for a mixed grinding material. The method comprises the following steps: mixing zirconium silicate and alumina; carrying out ball milling on the mixture so as to obtain mixed micro-powder; putting the mixed micro-powder, water and a dispersant into a sorting barrel and standing the mixture for settlement after stirring; carrying out sorting, wherein two sub-steps are included, namely, a) sucking out a slurry on the upper layer of the sorting barrel with a siphon, adding clear water to the sorting barrel until the mixture reaches the initial liquid level before siphoning, and carrying out stirring, settling and siphoning so as to obtain particles of a grade, and b) adding the dispersant and clear water into the sorting barrel until the mixture reaches the initial liquid level before siphoning and repeating the steps of stirring, settling and siphoning so as to obtain particles of another grade; drying the obtained particles with different grades so as to obtain a finished product. The mixed grinding material produced in the invention enables damage of micro-powder to the surface of a ground material in grinding to be substantially reduced and plays a very critical role in improving the quality of surface polishing of an object and in reducing polishing cost.

Description

technical field [0001] The invention relates to a micropowder production method, which is a production method of a mixed abrasive material for improving the grinding surface quality, and belongs to the technical field of micropowder production. Background technique [0002] In the process of surface grinding, because of the contact between the grinding powder and the surface of the object, it will inevitably cause damage to the surface of the object. The degree of damage will affect the efficiency of the subsequent process, especially the quality and cost of polishing the surface of the object. In the prior art, the surface quality of the object is controlled by controlling the proportion of the abrasive during the grinding process, but the effect of this method is not satisfactory. Contents of the invention [0003] The object of the present invention is to overcome the above-mentioned disadvantages and provide a production method of a novel hybrid abrasive material, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/14
Inventor 虞向荣
Owner 无锡成旸科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka