White corundum powder coating method

A technology of white corundum powder and coating, which is applied in coating, casting equipment, molds, etc., can solve the problems of casting sand sticking, bubbles, and expensive zirconium substances, and achieve the effect of avoiding sand sticking.

Active Publication Date: 2011-11-30
SUFA HENGDIAN MACHINERY CNNC
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, zircon powder paint is usually applied to the surface of the sand mold cavity, so that the sand mold cavity can play a role in high temperature resistance during pouring, and avoid sand inclusions and blisters in the casting caused by sand washing during pouring. With the development of the nuclear industry, the price of zirconium materials is becoming more and more expensive, and the price of zircon powder coatings is also rising rapidly, which greatly increases the production cost.
The material cost of the white corundum powder coating with aluminum oxide as the main body is much lower than that of the zircon powder coating with zirconia as the main body. The use performance and brushing performance of the white corundum powder coating are similar to the zircon powder coating. However, there are also differences. During the brushing process, the brushing concentration of each layer is not prepared well. After brushing and ignition, bubbles will be generated, and castings will produce serious sticky sand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The brushing method of white corundum powder coating comprises the following steps:

[0012] Step 1: Prepare a white corundum powder paint with a Baume degree of 76°Bé, paint the surface of the sand mold cavity for the first time, ignite it immediately after painting, and then cool to room temperature;

[0013] Step 2: Prepare a white corundum powder paint with a Baume degree of 58°Bé, and paint the surface of the sand cavity for the second time. After the paint is finished, wait for 30 seconds to ignite, and then cool to room temperature;

[0014] Step 3: Prepare white corundum powder paint with a Baume degree of 42°Bé, and paint the third time on the surface of the sand mold cavity. After the paint is completed, wait for 60 seconds to ignite, then cool to room temperature, and the paint is completed.

[0015] Baume degree °Bé is a method to express the concentration of the solution. The Baume hydrometer is immersed in the measured solution, and the degree obtained is ...

Embodiment 2

[0017] The brushing method of white corundum powder coating comprises the following steps:

[0018] Step 1: Prepare a white corundum powder paint with a Baume degree of 80°Bé, paint the surface of the sand mold cavity for the first time, ignite it immediately after painting, and then cool to room temperature;

[0019] Step 2: Prepare a white corundum powder paint with a Baume degree of 56°Bé, and paint the surface of the sand mold cavity for the second time. After the paint is finished, wait for 40 seconds to ignite, and then cool to room temperature;

[0020] Step 3: Prepare white corundum powder paint with a Baume degree of 42-50°Bé, and paint the surface of the sand cavity for the third time. After the paint is finished, wait for 45 seconds to ignite, then cool to room temperature, and the paint is completed.

Embodiment 3

[0022] The brushing method of white corundum powder coating comprises the following steps:

[0023] Step 1: Prepare a white corundum powder paint with a Baume degree of 84°Bé, paint the surface of the sand cavity for the first time, ignite it immediately after painting, and then cool to room temperature;

[0024] Step 2: Prepare white corundum powder paint with a Baume degree of 58°Bé, and paint the surface of the sand cavity for the second time. After the paint is finished, wait for 60 seconds to ignite, and then cool to room temperature;

[0025] Step 3: Prepare a white corundum powder paint with a Baume degree of 50°Bé, and paint the surface of the sand mold cavity for the third time. After the paint is completed, wait for 55 seconds to ignite, then cool to room temperature, and the paint is completed.

[0026] Adopting the brushing method of the white corundum powder paint provided by the present invention ensures that no air bubbles will be generated after the painted coa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Baume degreesaaaaaaaaaa
Baume degreesaaaaaaaaaa
Baume degreesaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for brushing white alundum powder paint, and the method comprises the following steps of: 1, preparing the white alundum powder paint with a baume degree of 76-84 [Be], carrying out primary brushing of the white alundum powder paint on a surface layer of a sand cavity, lighting the white alundum powder paint immediately after brushing is completed, and then coolingto a room temperature; 2, preparing the white alundum powder paint with the baume degree of 52-58 [Be], carrying out secondary brushing of the white alundum powder paint on the surface layer of the sand cavity, lighting the white alundum powder paint 30-60 seconds after the brushing, and then cooling to the room temperature; and 3, preparing the white alundum powder paint with the baume degree of42-50 [Be], carrying out tertiary brushing of the white alundum powder paint on the surface layer of the sand cavity, lighting the white alundum powder paint 30-60 seconds after the brushing, and then cooling to the room temperature so as to complete the brushing, thereby ensuring that a brushed coating layer cannot generate air bubbles after being lighted and preventing a casting from being subjected to sand fusion.

Description

technical field [0001] The invention relates to a coating method of a coating, in particular to a coating method of a white corundum powder coating suitable for the surface layer of a sand mold cavity. Background technique [0002] In the prior art, zircon powder paint is usually applied to the surface of the sand mold cavity, so that the sand mold cavity can play a role in high temperature resistance during pouring, and avoid sand inclusions and blisters in the casting caused by sand washing during pouring. With the development of the nuclear industry, the price of zirconium materials is becoming more and more expensive, and the price of zircon powder coatings is also rising rapidly, which greatly increases the production cost. The material cost of the white corundum powder coating with aluminum oxide as the main body is much lower than that of the zircon powder coating with zirconia as the main body. The use performance and brushing performance of the white corundum powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22C23/02B22C3/00
Inventor 叶永姣
Owner SUFA HENGDIAN MACHINERY CNNC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products