High-toughness composite SBR modified asphalt for warm-mixed asphalt technology, and preparation method thereof

A technology of warm-mixed asphalt and modified asphalt, which is applied to coagulation pavement paved on site, building insulation materials, building components, etc. It can solve problems such as viscosity and toughness of asphalt that are not mentioned, and achieve improved water stability and anti-aging Performance, improving adhesion performance, improving the effect of asphalt viscosity and toughness

Inactive Publication Date: 2013-01-16
南京中公材料科技发展有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Chinese patent CN101838468A "a nano-silica powder composite modified asphalt material composition and its preparation method" discloses a nano-silica powder and SBR styrene-butadiene rubber modified asphalt technology, which improves the high-temperature performance of the asphalt material, and also Improves the low-temperature performance of asphalt materials, but does not mention the improvement of the viscosity, toughness and toughness of asphalt—improving the tensile strength of the pavement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A composite SBR modified asphalt, the main raw material: No. 70 asphalt, produced by SK Company in South Korea, and the trade name of SBR asphalt modifier—PC1468, produced by Meadwestvaco.

[0033] Based on the total mass of modified asphalt raw materials, weigh 95 Kg (95%) of No. 70 asphalt, 3.8 Kg (3.8%) of asphalt modifier PC1468, 1 Kg (1%) of alkyl condensate, and 0.2 Kg of sulfur stabilizer (0.2%) reserve;

[0034] A preparation method of composite SBR modified asphalt, carried out according to the following steps:

[0035] (1) Put 95 Kg of No. 70 asphalt into a heating and stirring container, heat it to 120-160°C, make it melt completely, and stir while keeping warm;

[0036] (2) Add 3.8 Kg of asphalt modifier PC1468 and 1 Kg of alkyl condensate to the above molten No. 70 asphalt, and stir to mix;

[0037] (3) Raise the temperature to 160-180°C; add 0.2 Kg of sulfur as a stabilizer, stir and mix evenly, and discharge the material from the heating and stirring c...

Embodiment 2

[0039] A composite SBR modified asphalt, the main raw material: No. 70 asphalt, produced by SK Company in South Korea, and the trade name of SBR asphalt modifier—PC1468, produced by Meadwestvaco.

[0040] Based on the total mass of modified asphalt raw materials, weigh 93.8 Kg (93.8%) of No. 70 asphalt, 6 Kg (6%) of asphalt modifier PC1468, 3 Kg (3%) of alkyl condensate, and 1.2 Kg of stabilizer sulfur ( 1.2%) for reserve;

[0041] A preparation method of composite SBR modified asphalt, carried out according to the following steps:

[0042] (1) Put 93.8 Kg of No. 70 asphalt into a heating and stirring container, heat it to 120-160°C, make it melt completely, and stir while keeping warm;

[0043] (2) Add 6 Kg of asphalt modifier PC1468 and 3 Kg of alkyl condensate to the above molten No. 70 asphalt, and stir and mix;

[0044](3) Raise the temperature to 160-180°C; add 1.2 Kg of sulfur as a stabilizer, stir and mix evenly, and discharge the material from the heating and stirr...

Embodiment 3

[0046] A composite SBR modified asphalt, the main raw material: No. 70 asphalt produced by SK Corporation of Korea, the trade name of SBR asphalt modifier - PC1468, produced by Meadwestvaco.

[0047] Based on the total mass of modified asphalt raw materials, after the asphalt is heated and melted, weigh 85 Kg of No. 70 asphalt, asphalt modifier PC1468 8 Kg (8%), alkyl condensate 5 Kg (5%), stabilizer sulfur 2 Kg (2%) spare;

[0048] A preparation method of composite SBR modified asphalt, carried out according to the following steps:

[0049] (1) Put 85 Kg of No. 70 asphalt into a heating and stirring container, heat it to 120-160°C, make it melt completely, and stir while keeping warm;

[0050] (2) Add 8 Kg of asphalt modifier PC1468 and 5 Kg of alkyl condensate to the above molten No. 70 asphalt, and stir and mix;

[0051] (3) Raise the temperature to 160-180°C; add 2 Kg of sulfur as a stabilizer, stir and mix evenly, and discharge the material from the heating and stirrin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to high-toughness composite SBR modified asphalt for a warm-mixed asphalt technology, and a preparation method thereof, and belongs to the technical field of composite modified asphalt. The high-toughness composite SBR modified asphalt is prepared through mixing matrix asphalt, an alkyl condensation substance, an asphalt modifier and a stabilizer. The raw materials comprise,by mass, 85-95% of the matrix asphalt, 1-5% of the alkyl condensation substance, 2-10% of the asphalt modifier and 0.2-2% of the stabilizer. The preparation method comprises the following steps: (1) weighing the matrix asphalt according to the mass percentage of 85-95%, then placing the matrix asphalt in a heating and mixing container, carrying out heating to a temperature of 120-160 DEG C to enable the matrix asphalt to be molten completely, carrying out heat insulation while carrying out stirring; (2) weighing the asphalt modifier according to the mass percentage of 2-10%, weighing the alkyl condensation substance according to the mass percentage of 1-5%, then adding the asphalt modifier and the alkyl condensation substance to the molten matrix asphalt, and carrying out stirring and mixing; (3) heating to the temperature of 160-180 DEG C, weighing the stabilizer according to the mass percentage of 0.2-2%, then adding the stabilizer to the resulting mixture from the step (2), uniformly stirring and mixing, removing the material from the heating and mixing container to prepare the high-toughness composite SBR modified asphalt.

Description

technical field [0001] The invention relates to a high-viscosity and toughness composite SBR modified asphalt which can be used in warm-mix asphalt technology and a preparation method thereof, belonging to the technical field of composite modified asphalt. Background technique [0002] Asphalt concrete is one of the most used building materials in the world. With the rapid development of my country's expressways, the traffic volume continues to increase, the performance of vehicles continues to improve, and the speed of vehicles continues to increase. Road safety and environmental protection issues are becoming more and more serious. At the same time, with the development of the national economy, the rapid growth of traffic volume, the increasing number of heavy-duty and overloaded vehicles, and the channelization of vehicles, the requirements for traffic road surfaces are getting higher and higher. Heavy-duty emulsified asphalt can no longer adapt to the special conditions of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L9/06C04B26/26E01C7/26
CPCY02A30/30
Inventor 张兰
Owner 南京中公材料科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com