Preparation method of good sanding performance putty

A grinding performance and atomic ash technology, applied in the direction of filling slurry, etc., can solve the problem of unsatisfactory effect, and achieve the effect of easy scraping operation, uniform and stable performance, and excellent grinding performance

Inactive Publication Date: 2012-04-25
赵爱荣
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although its patent literature claims that it has excellent grinding performance, it has been verified by experiments that its effect is not ideal, and it still cannot meet the needs of various industries.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for preparing putty with good grinding performance, which is formed by mixing and reacting a main agent and a curing agent, the mass ratio of the main agent and the curing agent is: 100:2, wherein the main agent is composed of the following components in parts by weight: Parts composition: unsaturated polyester resin: 56 parts; styrene: 8 parts; talcum powder: 10 parts; barium sulfate: 8 parts; titanium dioxide: 2 parts; heavy calcium carbonate: 9 parts; Phenol: 0.5 parts; Anti-settling agent: 1.8 parts; Accelerator: 0.2 parts; Wherein the curing agent consists of the following components by weight: 80 parts of benzoyl peroxide; Pigment: 8 parts; Filler: 10 parts; Accelerator: 10% dimethylaniline: 6 parts; wherein the preparation method of the main agent is as follows:

[0018] 1) Put the unsaturated polyester resin into the dispersion tank according to the formula amount, add styrene, tert-butyl hydroquinone, accelerator, anti-sedimentation agent and stir for ...

Embodiment 2

[0022] A method for preparing putty with good grinding performance, which is formed by mixing and reacting a main agent and a curing agent, the mass ratio of the main agent and the curing agent is: 100:2, wherein the main agent is composed of the following components in parts by weight: Parts composition: unsaturated polyester resin: 64 parts; styrene: 4 parts; talcum powder: 15 parts; barium sulfate: 5 parts; titanium dioxide: 3 parts; heavy calcium carbonate: 6 parts; Phenol: 1 part; Anti-settling agent: 1.4 parts; Accelerator: 0.4 parts; Wherein the curing agent consists of the following components by weight: 84 parts of benzoyl peroxide; Pigment: 5 parts; Filler: 12 parts; Accelerator: 10% dimethylaniline: 5 parts; wherein the preparation method of the main agent is as follows:

[0023] 1) Put the unsaturated polyester resin into the dispersion tank according to the formula amount, add styrene, tert-butyl hydroquinone, accelerator, anti-sedimentation agent at the same time...

Embodiment 3

[0027] A method for preparing putty with good grinding performance, which is formed by mixing and reacting a main agent and a curing agent, the mass ratio of the main agent and the curing agent is: 100:2, wherein the main agent is composed of the following components in parts by weight: Parts composition: unsaturated polyester resin: 60 parts; styrene: 6 parts; talcum powder: 13 parts; barium sulfate: 6.5 parts; titanium dioxide: 2.5 parts; heavy calcium carbonate: 7.5 parts; Phenol: 0.7 parts; Anti-settling agent: 1.6 parts; Accelerator: 0.3 parts; Wherein the curing agent consists of the following components by weight: 82 parts of benzoyl peroxide; Pigment: 6.5 parts; Filler: 11 parts; Accelerator: 10% dimethylaniline: 5.5 parts; wherein the preparation method of the main agent is as follows:

[0028] 1) Put the unsaturated polyester resin into the dispersion tank according to the formula quantity, add styrene, tert-butyl hydroquinone, accelerator, anti-sedimentation agent a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of good sanding performance putty. The putty is prepared by mixing and reacting a main agent with a curing agent according to a mass ratio of 100:2. According to the invention, components of the putty are optimized to obtain an optimum content ratio of the components, so a very excellent sanding effect, which is characterized in that the putty does not stick sand paper during sanding and the sanded putty is finished and smooth and has no honeycombs, is achieved. To counter the designed components, the method of the invention selects a procedure that the components are mixed step by step, and the components are added in a batch mode according to performances of the components, so the uniformity and the stability of performances of the prepared main agent are guaranteed.

Description

technical field [0001] The invention relates to the field of chemical industry, in particular to a method for preparing atomic ash with good grinding performance. Background technique [0002] Atomic ash is mainly used for repairing and painting primers of various vehicles, machine tools, ships, instruments, instrument shells and furniture. At present, the production technology of atomic ash is basically mature, and whether the atomic ash is easy to polish after forming a film has become an important issue. It is an important index to evaluate the product quality of putty manufacturers. [0003] At present, in order to improve the grinding performance of putty after film formation, many manufacturers have adopted various methods: for example, reducing the viscosity of unsaturated polyester resin, while reducing the viscosity of the resin, the risk is high, and it is easy to reduce the activity of the resin. Even putty film formation and cracking; some add mono-acid or fumar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/34
Inventor 卢齐元
Owner 赵爱荣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com