Method for thermally bulging high-temperature alloy rectangular ring rolled member

A superalloy and rectangular ring technology is applied in the field of thermal expansion of superalloy rectangular ring rolling pieces, which can solve the problems of low dimensional accuracy and inapplicability of ring rolling pieces, and achieve the effect of improving dimensional accuracy.

Active Publication Date: 2014-04-02
GUIZHOU ANDA AVIATION FORGING
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since this method relies on the flexible contact between the liquid and the inner peripheral surface of the ring to cold-expand the rectangular ring, it is only suitable for some materials with small deformation resistance, and its main function is to strengthen the ring. For materials with greater deformation resistance For example, superalloys are not applicable; and this method does not disclose in detail how to improve the dimensional accuracy of the ring through bulging, but it is generally concluded that the purpose of improving the forming accuracy of the retaining ring can be achieved, that is, this method cannot solve the existing problems. The problem of low dimensional accuracy of ring rolling parts in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for thermally bulging high-temperature alloy rectangular ring rolled member
  • Method for thermally bulging high-temperature alloy rectangular ring rolled member
  • Method for thermally bulging high-temperature alloy rectangular ring rolled member

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0043] The main chemical element content (percentage by weight) of the alloy is: C content ≤ 0.08%, Cr content 17.0% ~ 21.0%, Ni content 50.0% ~ 55.0%, Co content ≤ 1.0%, Mo content 2.80% ~3.30%, Al content 0.30%~0.70%, Ti content 0.75%~1.15%, Nb content 4.75%~530%, B content ≤0.006%, Mg content ≤0.01%, Mn content ≤0.35 %, Si content ≤0.35%, P content ≤0.015%, S content ≤0.015%, Cu content ≤0.30%, Ca content ≤0.01%, Pb content ≤0.0005%, Se content ≤0.0003% , The balance is Fe.

[0044] The structural diagram of the bulging machine for implementing the thermal bulging method of the present invention is as follows: figure 2 As shown, the bulging machine is mainly composed of a mandrel slider 1, a radial slider 2, a bulging block 3, a workbench 4 and a guide rail 5. The mandrel slider 1 is conical and is set in the radial slider 2 to cooperate with the conical inner peripheral surface of the radial slider 2. The mandrel slider 1 can be driven by the hydraulic cylinder of the b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
heightaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for thermally bulging a high-temperature alloy rectangular ring rolled member. The method comprises the following steps of: sleeving a hot rolled high-temperature alloy rectangular ring rolled member on the periphery of a pre-heated bulged block in a bulging machine, and starting the bulging machine to enable the bulged block to extrude the ring rolled member from the inner circumferential surface of the ring rolled member in a radial direction, so that bulging for the first time is completed, wherein the bulging temperature is 800-850 DEG C, the bulging time is 20-30 s, the pressure maintaining time is 9-10 s, and the deformation is 0.6-0.8%; rotating the ring rolled member along a central axis for 45 DEG, so that rotating for the first time is completed; then, carrying out bulging for the second time according to the above operations, wherein the bulging temperature is 770-820 DEG C, the bulging time is 20-30 s, the pressure maintaining time is 17-18 s, and the deformation is 0.7-0.9%; rotating the ring rolled member again according to the first rotary direction, so that rotating for the second time is completed; and carrying out bulging for the third time according to the above operations, wherein the bulging temperature is 740-790 DEG C, the bulging time is 30-40 s, the pressure maintaining time is 25-28 s, and the deformation is 0.8-1%. The size precision of the bulged ring rolled member can be up to 0.001-0.002 of that of corresponding sizes. The ring rolled member disclosed by the invention is mainly applied to the fields, such as aerospace and the like.

Description

technical field [0001] The invention relates to a bulging method for a ring, in particular to a thermal bulging method for a high-temperature alloy rectangular ring rolling piece. Background technique [0002] After the high-temperature alloy rectangular ring-rolled piece (referring to the ring-rolled piece with a rectangular cross-section in the longitudinal section) is rolled by the ring rolling mill, due to the influence of the rolling process and equipment limitations, its dimensional accuracy is generally not high; only in the shape of the ring-rolled piece In the case of ideal and excellent equipment performance, the dimensional accuracy can reach 3‰~5‰ (three thousandths to five thousandths) of the corresponding size. If the control is not good in the follow-up processing process, defects such as warping, deformation and even cracking may easily occur. [0003] The Chinese invention patent specification CN101367104A published on February 18, 2009 discloses a hydrauli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21D39/20B21D37/16
Inventor 魏志坚葛金峰叶俊青邓远翔占立水冯琼
Owner GUIZHOU ANDA AVIATION FORGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products