Coordination crosslinking method for reinforced anti-aging nitrile elastomer

A coordination cross-linking and elastomer-like technology is applied in the cross-linking field of nitrile elastomers to achieve good mechanical properties and enhance anti-aging properties.

Inactive Publication Date: 2012-06-27
FUJIAN NORMAL UNIV
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method has no reinforcement and anti-aging formula design, from which only nitrile elastomers with unsatisfactory mechanical properties can be obtained, which is far from the actual application requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Put 100 kilograms of nitrile rubber resin, 5 kilograms of ferric sulfate heptahydrate, 25 kilograms of stearic acid, 50 kilograms of carbon black and 0.1 kilogram of anti-aging agent A into the internal mixer at one time, and mix them evenly at 30 ° C. Obtain a composite rubber material; then send the composite rubber material into a flat vulcanizer for a cross-linking reaction at 160°C for 30 minutes, then discharge the material, and cool to obtain a reinforced anti-aging nitrile elastomer. The physical parameters of the sample were tested according to the relevant national standards: the tensile strength was 16.3Mpa, the elongation at break was 980%, and the Shore hardness was 63. The physical parameters of the sample aged in an air oven at 130°C for 500 hours were tested by the same method: the tensile strength was 15.9Mpa, the elongation at break was 970%, and the Shore hardness was 64.

Embodiment 2

[0028] Put 100 kg of mixed nitrile rubber resin mixed with nitrile rubber and hydrogenated nitrile rubber with a weight ratio of 3:2 into the internal mixer at one time, and 13 kg of sulfuric acid nonahydrate with a weight ratio of 11:1 Mixed ferric sulfate mixed with iron and anhydrous ferric sulfate, 15 kg of stearylamine, 25 kg of carbon black and 3 kg of mixed antioxidant A and BZ with a weight ratio of 6:1 Five kinds of raw materials were mixed evenly at 45°C to obtain a composite rubber; then the composite rubber was sent to a flat vulcanizer for a cross-linking reaction at 175°C for 25 minutes, and then discharged, cooled to obtain a reinforced anti-aging nitrile elastomer . The physical parameters of the sample were tested according to the relevant national standards: the tensile strength was 18.9Mpa, the elongation at break was 897%, and the Shore hardness was 58. The physical parameters of the sample aged in an air oven at 130°C for 500 hours were tested by the same...

Embodiment 3

[0030] 100 kilograms of mixed nitrile rubber resin mixed with nitrile rubber, hydrogenated nitrile rubber and powdered nitrile rubber with a weight ratio of 4:4:1 are thrown into the internal mixer at one time, and 20 kilograms are mixed with a weight ratio of 4:4:1. 3:6:1 mixed ferric sulfate heptahydrate, ferric sulfate nonahydrate and anhydrous ferric sulfate, 15 kg of lauric acid, 5 kg of white carbon black and 1.5 kg by weight ratio of 6:3: 1 anti-aging agent A, anti-aging agent RD and anti-aging agent 264 are mixed five kinds of raw materials of mixed anti-aging agent, mixed uniformly at 55 ℃ to obtain a compound rubber; then the compound rubber is sent to a flat vulcanizing machine at 185 After 21 minutes of cross-linking reaction, the material was discharged and cooled to obtain a reinforced anti-aging nitrile elastomer. The physical parameters of the sample were tested according to the relevant national standards: the tensile strength was 23.4Mpa, the elongation at br...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a coordination crosslinking method for reinforced anti-aging nitrile elastomer. The method is characterized by comprising the following steps of: feeding 100 weight parts of nitrile rubber resin, 5 to 20 weight parts of coordination crosslinking agent, 5 to 25 weight parts of compatilizer, 5 to 50 weight parts of reinforcing filler, and 0.1 to 3 weight parts of antiager into processing equipment at one time, and uniformly mixing at the temperature of between 30 and 55 DEG C to obtain a composite sizing material; and feeding the composite sizing material to reaction equipment, performing crosslinking reaction at the temperature of between 160 and 230 DEG C for 4 to 30 minutes, discharging and cooling to obtain the reinforced anti-aging nitrile elastomer. Compared with non-reinforced anti-aging nitrile elastomer, the reinforced anti-aging nitrile elastomer which is obtained by the method has good mechanical properties, and meets the actual application requirement well.

Description

technical field [0001] The invention relates to a crosslinking method for nitrile elastomers, in particular to a coordination crosslinking method for reinforcing and antiaging nitrile elastomers. [0002] Background technique: [0003] Nitrile elastomers, including nitrile rubber (NBR), hydrogenated nitrile rubber (HNBR), powdered nitrile rubber, carboxylated nitrile rubber, liquid carboxylated nitrile rubber, and their mixed rubbers, contain a large amount of cyano (- CN), showing strong polarity, good compatibility with metal salts, and easy to coordinate with metal ions, so they can achieve vulcanization through coordination crosslinking. Compared with traditional sulfur-containing substances or peroxide covalent cross-linking methods, the coordination cross-linking method has the following advantages: (1) The vulcanization system is simple, and the processing technology is energy-saving; (2) It can produce thermally reversible coordination cross-linking bonds , so that ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J3/24C08L9/02C08L15/00C08L13/00C08K13/02C08K3/04C08K5/09C08K3/30C08K5/17C08K3/36C08K3/26
Inventor 陈庆华陈荣国钱庆荣曹长林肖荔人刘欣萍卓倩黄宝铨许兢
Owner FUJIAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap