A technology of polyester sheet and polyethylene terephthalate, which is applied in the fields of polyester sheet, polyester molded products, and polyester resin masterbatch, which can solve the problems of poor sliding properties of raw materials and achieve excellent anti-blocking properties , Excellent effect of transparency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1~6、 comparative example 1~8
[0088] Such as Figure 5 As shown in the table of , a total of 14 types of single-layer sheets were prepared as Examples 1-6 and Comparative Examples 1-8. Specifically, a raw material mixture of PET resin or PETC resin, ester compound, and spherical silica in the blending amount shown in the figure was supplied to three twin-screw extruders (Extruder), and the barrel was heated to temperature The mixture was melted at 260°C to 285°C, extruded from a T-die by a three-layer co-extrusion method, and cooled by a cooling roll at 35°C to form a sheet with a thickness of 0.2mm.
[0089] from Figure 5 It can be seen that, in Examples 1 to 6, favorable results were obtained in which all of the sliding properties, blocking resistance, and transparency were well-balanced.
Embodiment 7~11、 comparative example 9~10
[0092] Such as Figure 6 As shown in the table of , as Examples 7 to 11 and Comparative Examples 9 to 10, a total of 7 types of polyester sheets with a multilayer structure were produced. Only PET raw materials are used in the base layer without any slip agent, and PETC is used as the base polymer on both surface layers, and ester compound and spherical silica are added.
[0093] Depend on Figure 6 It can be seen that, in Examples 7 to 11, favorable results were obtained in which all aspects of sliding properties, blocking resistance, and transparency were well-balanced. In addition, it can be seen that when PETC is used as the matrix polymer of the surface layer, the same Figure 5 Compared with the case of using PET, when the blending amount of the ester compound and the blending amount of silica are increased, good sliding properties can be obtained.
[0094] In Comparative Example 9, in which no ester compound was added to the surface layer, both slipperiness and block...
Embodiment 12~14
[0096] Such as Figure 7 As shown in the table of , as Examples 12 to 14, three types of polyester sheets with a multilayer structure were produced. In the base layer, only PET raw material is used without adding any slip agent. In both surface layers, PET raw material is used as the matrix polymer, and ester compound and spherical silica are compounded.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap