Method of increasing the high-speed performance of a carcass structure in a tyre for vehicle wheels and tyre for vehicle wheels

A carcass structure and tire technology, applied in the direction of wheels, vehicle parts, tire parts, etc., can solve the problems of difficult man-made fiber performance, detachment, and increased real deformation of the carcass, and achieve the effect of enhancing high-speed performance.

Active Publication Date: 2012-09-12
PIRELLI TYRE SPA
View PDF10 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The Applicant has found that the above-mentioned heating of the known reinforcing cords belonging to the carcass structure determines a decrease in the modulus of the yarns forming the cords, as a result, relative to the The ideal deformation under the condition of ℃ room temperature), the real deformation of the carcass subjected to acceleration increases
[0012] In addition, the Applicant has found that because man-made fibers are highly hygroscopic, i.e. have a modulus that is very dependent on the moisture content of the fibers, and because during the processing of fibers the drying process is complex and difficult to obtain in an optimal manner (Some amount of moisture is trapped in the fibers anyway), so the modulus of wet rayon yarns incorporated into the tire carcass is less than the modulus given by theory, which leads to an ideal Deformation of the carcass, the real deformation of said carcass is increased
[0013] In addition, it will be more difficult to set the performance of man-made fibers on tires since the mechanical characteristics of man-made fibers depend on the water content in the fibers (which is variable and depends on the efficiency of the drying system)
In addition, water trapped in man-made fibers can cause defects (bubbles, debonding, etc.) in the finished tire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of increasing the high-speed performance of a carcass structure in a tyre for vehicle wheels and tyre for vehicle wheels
  • Method of increasing the high-speed performance of a carcass structure in a tyre for vehicle wheels and tyre for vehicle wheels
  • Method of increasing the high-speed performance of a carcass structure in a tyre for vehicle wheels and tyre for vehicle wheels

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0131] Three blended yarns according to the invention have been prepared:

[0132] A1- Aromatic polyamide (AR) + polyethylene terephthalate (PET) (aramid 50%)

[0133] A2-aramid+polyethylene terephthalate (aramid 25%)

[0134] A3-aramid+polyethylene terephthalate (aramid 20%)

[0135] And two non-mixed yarns:

[0136] B1-Kevlar 440

[0137] B2-Polyethylene terephthalate 1670

[0138] A1 is a mixed fiber yarn made of aramid (AR) multifilament yarn and polyethylene terephthalate (PET) multifilament yarn; Silk yarn constitutes 50% by weight of the mixed fiber yarn A1.

[0139] Yarn A1 is prepared by feeding aramid (AR) multifilament yarn and polyethylene terephthalate (PET) multifilament yarn to an air-jet texturising device .

[0140] A2 is a mixed fiber yarn made of aramid (AR) multifilament yarn and polyethylene terephthalate (PET) multifilament yarn; Silk yarn constitutes 25% by weight of mixed fiber yarn A2.

[0141] The yarn A2 is prepared by feeding an aramid (AR) multifilament yarn a...

example 2

[0149] Figure 7 Shows the traction load (Newtons) as a function of elongation (%) for three cords according to the invention:

[0150] Aramid + polyethylene terephthalate (37%) 1840×2405×405 (made of two kinds of mixed yarn aramid + polyethylene terephthalate (37%) The cord, each blended yarn aramid + polyethylene terephthalate (37%) has a yarn count of 1840 (dtex) and 405 twisting operations per meter);

[0151] Aramid + polyethylene terephthalate (37%) 1840×2305×305 (made of two kinds of mixed fiber yarn aramid + polyethylene terephthalate (37%) For cords, each blended yarn aramid + polyethylene terephthalate (37%) has a yarn count of 1840 (dtex) and 305 twisting operations per meter);

[0152] Aramid + polyethylene terephthalate (20%) 2130×2405×405 (made of two kinds of mixed fiber yarn aramid + polyethylene terephthalate (20%) The cord, each blended yarn aramid + polyethylene terephthalate (20%) has a yarn count of 2130 (dtex) and 450 twisting operations per meter);

[0153] An...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a method of increasing the high-speed performance of a carcass structure in a tyre for vehicle wheels. The method includes: preparing at least one hybrid yarn (13) and assembling a carcass structure (2) comprising at least one carcass ply (3a, 3b) substantially built on cords (12) comprising the hybrid yarn (13). The hybrid yarn (13) comprises a plurality of filaments (14a, 15a) obtained from a first multi-filament yarn (14) of polyester and a second multi-filament yarn (15) having a decay of the modulus with the temperature lower than 20%. Each of the first multi-filament yarn (14) and second multi-filament yarn (15) comprises a plurality of individual filaments (14a, 15a). The individual filaments (14a) of the first multi-filament yarn (14) are at least partly mixed in proportions of at least 50% with the individual filaments (15a) of said second multi-filament yarn (15).

Description

Technical field [0001] The present invention relates to a method for enhancing the high-speed performance of a carcass structure in a tire for a vehicle wheel and a tire for a vehicle wheel. Background technique [0002] Tyres for vehicle wheels generally include a carcass structure associated with a belt structure. The tread band is applied at a radially outer position of the belt structure. Green tires are constructed by assembling corresponding semi-finished products made of elastomer mixtures and then molded / cured. [0003] Specifically, the present invention relates to a high-performance tire such as, for example, HP (high-performance) tires and UHP (ultra-high-performance) tires or tires used in sports fields such as track racing, or used in various SUVs (sports Multi-function vehicles), the SUVs combine mass and volume that are typical characteristics of wagons with sports car performance), the high-performance tires are used for very powerful cars or motorcycles, or more ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B60C9/00D02G3/48B29D30/38
CPCB29D30/38D02G3/48D10B2331/04B60C2009/0416B60C9/005B60C2009/0475B60C2009/0078B60C2009/0433Y10T152/10855
Inventor B·拉姆帕纳R·圣加利D·蒂雷利
Owner PIRELLI TYRE SPA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap