Stainless steel tooth zipper and manufacture method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A stainless steel and zipper technology, applied in the field of zippers, can solve the problems of stainless steel zipper being uncompetitive, high cost, unable to be popularized and used, and achieve the effect of excellent flat tensile strength, service life and high bonding strength.
Inactive Publication Date: 2012-09-19
广东辉丰科技股份有限公司
View PDF8 Cites 10 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the stainless steel materials available on the market are relatively hard. If the traditional flat wire is used to punch and then arrange the teeth in the tooth row machine to make stainless steel chain teeth, the loss of the mold will be large, the material utilization rate will be high, and the cost will be high; if the stainless steel powder is added with a binder Injection molding and sintering, the process is complicated, the relative density of the product is lower than the original density of stainless steel, and the advantages of stainless steel cannot be fully realized
So far, stainless steel tooth zippers are not competitive in the market and cannot be promoted.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0022] Embodiment 1: a kind of preparation method of stainless steel tooth slide fastener, comprises the steps:
[0023] A. Design the drawing and rolling "Y" shaped wire die, and select the suitable drawing and rolling equipment;
[0024] B. Select 2.65mm in diameter and grade 202 stainless steel wire, and anneal and soften it to make the Brinell hardness ≤ 200;
[0025] C. Stainless steel wire rod 2 drawn and rolled into a "Y"-shaped section 1, such as figure 1 and figure 2 shown;
[0026] D. Arrange the teeth in the tooth row machine, and prepare the chain teeth 3 on the cloth belt 4 such as Figure 3-Figure 5 As shown, the stainless steel tooth zipper products are made by post-processing combination, such as Image 6 shown.
[0027] Wherein, in the stainless steel wire rod 2 of "Y" shape section 1, "U" shape part 11 is provided, and inside the port of "U" shape part 11, a pair of convex parts 12 are set; A pair of ribs 13 are provided in the inner groove of 11 .
...
Embodiment 2
[0031] Embodiment 2: A preparation method of a stainless steel tooth zipper, select a diameter of 2.95mm, grade 304L stainless steel wire, annealing and softening treatment, so that its Brinell hardness is less than 200; the rest of the process and the structure of the product are the same or similar to Example 1 .
Embodiment 3
[0032] Embodiment 3: A kind of preparation method of stainless steel tooth zipper, select diameter to be 3.45mm, grade is 317L stainless steel wire rod, annealing and softening treatment, make its Brinell hardness less than 200; The structure of other processes and products is the same or similar to that of embodiment 1 .
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a stainless steel tooth zipper and a manufacture method thereof. The stainless steel teeth include pairs of bilaterally-symmetrical tooth bodies, concave surface portions and tooth point portions, wherein the concave surface portions and the tooth point portions are connected in a consubstantiality mode and arranged on the tooth bodies. The concave surface portion is matched with the tooth point portion on the other tooth body in a buckled mode, external clamping convex portions are arranged at the ports on the inner sides of the tooth bodies, and internal clamping convex portions are arranged in the middle of the inner sides of the tooth bodies. The manufacture method of the stainless steel tooth zipper is that a stainless steel wire processed by softening is pull-rolled into a stainless steel wire with a Y-shaped section, then arrangement of teeth is performed by a tooth arrangement machine, and post-processing combination is performed to obtain a stainless steel tooth zipper product. The product has the advantages of being high in corrosion resistance, large in tensile strength, good in quality, high in grade and the like. In addition, the cost of the product is reduced.
Description
technical field [0001] The invention relates to the technical field of slide fasteners, in particular to a stainless steel tooth slide fastener and a preparation method thereof. Background technique [0002] The zippers currently on the market are widely used with nylon tooth zippers, resin tooth zippers, copper tooth zippers, aluminum alloy tooth zippers, etc. These zippers have defects such as low tensile strength, easy wear, tooth burst, low lifespan, discoloration, and fading to varying degrees. Stainless steel has the characteristics of high tensile strength, corrosion resistance, permanent capital return, etc., and the product is of high grade. However, the stainless steel materials available on the market are relatively hard. If the traditional flat wire is used to punch and then arrange the teeth in the tooth row machine to make stainless steel chain teeth, the loss of the mold will be large, the material utilization rate will be high, and the cost will be high; if ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more