High-impedance soldering flux for single panel of power source charger and preparation method of high-impedance soldering flux

A charger and single-panel technology, which is applied in welding equipment, welding media, manufacturing tools, etc., can solve the problems of insufficient surface insulation, insufficient solder flux impedance, and easy moisture absorption of solder flux, etc., and achieve hydrolytic stability. Good, good film-forming and solubilizing effects, good moisture-proof performance

Active Publication Date: 2012-09-26
广东剑鑫科技股份有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flux used in the prior art usually contains glutaric acid, which causes the flux to absorb moisture easily, so that the produced power charger single panel is easy to absorb moisture and cause product quality problems when it rains and is wet in spring. question
In addition, the resistance value of the soldering flux commonly used in the prior art is not high enough, so that the insulation of the single-sided circuit after soldering is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0084] The preparation method of the high-impedance flux for the single-panel of the power charger is as follows:

[0085] Weigh 3Kg of hydrogenated rosin, 0.4Kg of adipic acid, 0.8Kg of sebacic acid, 1.5Kg of succinic acid, 1Kg of glycolic acid, 0.4Kg of dibromobutenediol, 1Kg of FT-900 surfactant, and 2 , 2,4-trimethyl-1,3-pentanediol monoisobutyrate 4Kg and solvent absolute ethanol 87.9Kg, put the above-mentioned weighed solvent absolute alcohol in a container with a stirring device at room temperature , then add the above-mentioned weighed dibromobutene glycol into the container, and stir until uniform, then add the above-mentioned weighed FT-900 surfactant into the container, and stir for 10 minutes, then the above-mentioned weighed Add good hydrogenated rosin, adipic acid, sebacic acid, succinic acid, glycolic acid and coalescent 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate into the container , and stirred for 20 minutes to obtain a high-impedance flux for the single...

Embodiment 2

[0087] The preparation method of the high-impedance flux for the single-panel of the power charger is as follows:

[0088] Weigh 4Kg of hydrogenated rosin, 0.5Kg of adipic acid, 1.0Kg of sebacic acid, 1.2Kg of succinic acid, 0.8Kg of glycolic acid, 0.3Kg of dibromobutenediol, 1.3Kg of FT-900 surfactant, film-forming assistant Agent 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate 5Kg and solvent absolute ethanol 85.9Kg, put the above-mentioned weighed solvent absolute alcohol in a stirring device at room temperature container, then add the above-mentioned weighed dibromobutenediol in the container, and stir until uniform, then add the above-mentioned weighed FT-900 surfactant in the container, and stir for 15 minutes, then the above-mentioned Weighed hydrogenated rosin, adipic acid, sebacic acid, succinic acid, glycolic acid and coalescent 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate were added to container, and stirred for 25 minutes to obtain the high-impedance flux for t...

Embodiment 3

[0090] The preparation method of the high-impedance flux for the single-panel of the power charger is as follows:

[0091] Weigh 2Kg of hydrogenated rosin, 0.2Kg of adipic acid, 0.6Kg of sebacic acid, 2Kg of succinic acid, 1.5Kg of glycolic acid, 0.6Kg of dibromobutenediol, 0.8Kg of FT-900 surfactant, and coalescent 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate 3Kg and solvent absolute ethanol 89.3Kg, put the above-mentioned weighed solvent absolute alcohol in a container with stirring device at room temperature Then add the above weighed dibromobutene diol into the container, and stir until uniform, then add the above weighed FT-900 surfactant into the container, and stir for 12 minutes, then the above weighed Add a good amount of hydrogenated rosin, adipic acid, sebacic acid, succinic acid, glycolic acid and coalescent 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate into the container and stirred for 23 minutes to obtain a high-impedance soldering flux for a single panel ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of soldering flux, in particular to high-impedance soldering flux for a single panel of a power source charger and a preparation method of the high-impedance soldering flux. The high-impedance soldering flux for the single panel of the power source charger consists of the following ingredients in percentage by weight: 1 percent to 5 percent of hydrogenated rosin, 0.1 percent to 0.8 percent of adipic acid, 0.4 percent to 1.2 percent of sebacic acid, 1 percent to 3 percent of succinic acid, 0.5 percent to 2 percent of glycollic acid, 0.1 percent to 0.8 percent of dibromo butylene glycol, 0.5 percent to 2 percent of surface active agents, 2 percent to 7 percent of film forming additives and 80 percent to 92 percent of absolute ethyl alcohol. The high-impedance soldering flux for the single panel of the power source charger has the advantages that the moisture cannot be easily absorbed, so the single panel of the power supply charger is prevented from generating quality problems caused by moisture absorption in rainy humid weather in spring, and in addition, the single panel of the power supply charger has the characteristic of high impedance.

Description

technical field [0001] The invention relates to the technical field of soldering flux, in particular to a high-impedance soldering flux for a single panel of a power charger and a preparation method thereof. Background technique [0002] When producing the single panel of the power charger, it is necessary to use flux to weld the circuit of the single panel. However, the flux used in the prior art usually contains glutaric acid, which causes the flux to absorb moisture easily, so that the produced power charger single panel is easy to absorb moisture and cause product quality problems when it rains and is wet in spring. question. In addition, the resistance value of the flux commonly used in the prior art is not high enough, so that the insulation of the surface of the single-sided circuit after soldering is not ideal. Contents of the invention [0003] The object of the present invention is to aim at the deficiencies in the prior art, provide a kind of high-impedance so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/362
Inventor 邓剑明
Owner 广东剑鑫科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com