High-tension/hot-rolled steel sheet having excellent workability, and method for producing same

A technology of hot-rolled steel sheets with excellent workability, applied in the direction of manufacturing tools, chemical instruments and methods, heat treatment furnaces, etc., can solve the problems of insufficient workability, extension flange, etc., and achieve excellent workability and remarkable effects

Active Publication Date: 2013-03-06
JFE STEEL CORP
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, in the technique proposed in Patent Document 1, it was found that when the tensile strength (TS) of the steel sheet is increased to 590 MPa l

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-tension/hot-rolled steel sheet having excellent workability, and method for producing same
  • High-tension/hot-rolled steel sheet having excellent workability, and method for producing same
  • High-tension/hot-rolled steel sheet having excellent workability, and method for producing same

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0128] (Example 1)

[0129] The molten steel having the composition shown in Table 1 was melted and continuously cast by a generally known method to produce a billet (raw steel) with a wall thickness of 250 mm. After heating these slabs to 1250°C, rough rolling was performed, and finishing rolling set to the finishing temperature shown in Table 2 was implemented. After finishing rolling, the temperature range from the temperature of 880°C to the coiling temperature Cooling was performed at the average cooling rate shown in Table 2, and coiling was performed at the coiling temperature shown in Table 2, to produce a hot-rolled steel sheet having a thickness of 2.3 mm. In addition, some hot-rolled steel sheets (hot-rolled No. 2 of steel No. A) were immersed in a 480°C galvanizing bath (0.1% Al-Zn) to form an adhesion amount of 45g / m 2 After the hot-dip galvanized film, alloying treatment is performed at 520°C to make an alloyed hot-dip galvanized steel sheet.

[0130] [Table 1]

[013...

Example Embodiment

[0155] (Example 2)

[0156] The molten steel of the composition shown in Table 4 was melted and continuously cast by a generally known method to produce a billet (raw steel) with a wall thickness of 250 mm. After heating these slabs to 1250°C, rough rolling was carried out, and finishing rolling set to the finishing temperature shown in Table 5 was implemented. After finishing rolling, the temperature range from the temperature of 880°C to the coiling temperature Cooling was performed at the average cooling rate shown in Table 5, and coiling was performed at the coiling temperature shown in Table 5 to produce a hot-rolled steel sheet having a thickness of 2.3 mm. In addition, some hot-rolled steel sheets (hot-rolled No. 13 for steel No. H and hot-rolled No. 15 for steel No. I) were immersed in a galvanizing bath (0.1% Al-Zn) at 480°C to form adhesion 45g / m 2 The hot-dip galvanized film is made into hot-dip galvanized steel sheet. In addition, for the other part of the hot-rolle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Thicknessaaaaaaaaaa
Adhesionaaaaaaaaaa
Login to view more

Abstract

Provided is a high-tension/hot-rolled steel sheet which has both strength and workability (stretch flangeability). The high-tension/hot-rolled steel sheet has: a composition comprising, by mass%, 0.005% to 0.050% of C, 0.2% or less of Si, 0.8% or less of Mn, 0.025% or less of P, 0.01% or less of S, 0.01% or less of N, 0.06% or less of Al, and 0.05% to 0.10% of Ti such that S, N, and Ti satisfy Ti>=0.04+(N/1448+S/3248), and with Fe and inevitable impurities as the balance; a matrix in which the ferrite phase is 95% or more by surface area percentage with respect to the overall structure; a structure in which carbide microparticles comprising Ti and having an average grain size of less than 10 nm are dispersed and precipitated, and the volume ratio of the carbide microparticles with respect to the overall structure is 0.0007 or greater; a tensile strength of 590 MPa or greater; and excellent workability.

Description

technical field [0001] The present invention relates to a high-strength hot-rolled steel sheet excellent in workability (stretch flangeability) suitable as a raw material for transportation machinery materials and structural materials such as automobile parts and a method for producing the same. Background technique [0002] From the viewpoint of protecting the global environment, in order to reduce CO 2 Emissions, while maintaining the strength of the car body, reducing its weight to improve the fuel efficiency of the car is often regarded as an important issue in the automotive industry. In order to reduce the weight of the automobile body while maintaining the strength of the automobile body, it is effective to increase the strength of the steel sheet used as a raw material for automobile parts and reduce the thickness of the steel sheet. For example, reducing the thickness of high-strength steel sheets for automobile running parts leads to significant weight reduction o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/14C22C38/54C21D8/02C21D9/46
CPCC21D9/46C22C38/14C22C38/002B32B15/01C22C38/12C22C38/04C21D2211/004C22C18/04C22C38/004C22C38/06C22C38/008C21D8/0226C22C38/02B32B15/013C21D8/0205C22C38/10C22C38/08C22C38/16C22C38/001C22C38/18C23C2/06C23C2/285C22C38/54C21D8/02
Inventor 有贺珠子中岛胜己船川义正森安永明村田贵幸
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap