Process for rolling thin low-temperature tank box steel plate by using rolling machine with single machine frame furnace
A furnace coil rolling mill and low temperature tank technology, applied in metal rolling, manufacturing tools, metal rolling and other directions, can solve the problems of excessive steel plate rolling force, steel plate rolling waste, uneven temperature distribution, etc., to meet the requirements of refined structure Grain, ensure the effect of plate shape
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] A process for rolling thin low-temperature tank steel plates with a single-stand furnace coil mill. A slab with a thickness of 150 mm is used to roll a low-temperature tank steel plate with a thickness of 11 mm. The process flow is: cold loading or hot charging in the slab warehouse → heating Furnace heating→coarse descaling→finish descaling→steel rolling mill rolling→flying shear head or section→laminar cooling→hot straightening machine straightening→cooling bed air cooling→steel plate bottom surface inspection→double side shearing→ Cut to length, segment or sample→spraying and stamping→stacking→warehousing of finished products;
[0021] In the heating process of the heating furnace, the tapping temperature of the heating furnace: 1150°C;
[0022] In the rough descaling process, high-pressure water is used to descale, and the oxide scale caused by one heating is removed at the outlet of the heating furnace. The water pressure of the nozzle is 20Mpa, and the descaling n...
Embodiment 2
[0031] A process for rolling thin low-temperature tank steel plates with a single-stand furnace coil mill. A slab with a thickness of 150 mm is used to roll a low-temperature tank steel plate with a thickness of 10 mm. The process flow is: cold loading or hot charging in the slab warehouse→heating Furnace heating→coarse descaling→finish descaling→steel rolling mill rolling→flying shear head or section→laminar cooling→hot straightening machine straightening→cooling bed air cooling→steel plate bottom surface inspection→double side shearing→ Cut to length, segment or sample→spraying and stamping→stacking→warehousing of finished products;
[0032] In the heating process of the heating furnace, the tapping temperature of the heating furnace: 1200°C;
[0033] In the rough descaling process, high-pressure water is used to descale, and the oxide scale caused by one heating is removed at the outlet of the heating furnace. The water pressure of the nozzle is 21Mpa, and the descaling noz...
Embodiment 3
[0042] A process for rolling thin low-temperature tank steel plates with a single-stand furnace coil mill. A slab with a thickness of 150 mm is used to roll a low-temperature tank steel plate with a thickness of 8 mm. The process flow is: cold loading or hot charging in the slab warehouse→heating Furnace heating→coarse descaling→finish descaling→steel rolling mill rolling→flying shear head or section→laminar cooling→hot straightening machine straightening→cooling bed air cooling→steel plate bottom surface inspection→double side shearing→ Cut to length, segment or sample→spraying and stamping→stacking→warehousing of finished products;
[0043] In the heating process of the heating furnace, the tapping temperature of the heating furnace: 1230°C;
[0044] In the rough descaling process, high-pressure water is used to descale, and the oxide scale caused by one heating is removed at the outlet of the heating furnace. The water pressure of the nozzle is 22Mpa, and the descaling nozz...
PUM
Property | Measurement | Unit |
---|---|---|
Yield strength | aaaaa | aaaaa |
Tensile strength | aaaaa | aaaaa |
Yield strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information

- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com