Manufacturing process of instrument carriage with raw materials containing ACS (acrylonitrile-chlorinated polyethylene-styrene) resins

A technology of manufacturing process and raw materials, applied in the field of manufacturing process of instrument brackets, can solve the problems of whitening, low strength, poor toughness, etc., and achieve the effects of improving production efficiency, stable product quality, and reducing production costs.

Active Publication Date: 2013-03-27
ANHUI KAIDI ELECTRIC
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to alleviate the deficiencies and defects of the prior art, the object of the present invention is to provide a manufacturing process for instrument brackets whose raw materials contain ACS resin, which solves the problem that the instrument brackets used for automobiles in injection mol

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process of instrument carriage with raw materials containing ACS (acrylonitrile-chlorinated polyethylene-styrene) resins

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] A manufacturing process of an instrument bracket whose raw material contains ACS resin,

[0026] (1) Mix the raw materials of material A and material B separately and carry out drying treatment. The drying temperature is 120°C and the drying time is 4 hours. Then, material A and material B are mixed according to the weight parts and then granulated. Granulated materials A and B;

[0027] Described A material is made by the raw material of following weight (kg): Nylon PA66 65, ACS resin 15, bisphenol A type polycarbonate 5, polycaprolactone 2, anilinomethyltriethoxysilane 1 , Vinyl triethoxysilane 1, antioxidant 168 0.5, polyethylene wax 0.7, dimethyl dimercaptoacetate isooctyl tin 1;

[0028] Described B material is made by the raw material of following weight (kg): Nylon PA66+20%GF 65, bisphenol A type polycarbonate 8, modified nanopowder 10, poly-4-methyl-1-pentane ene 10, ACS resin 15, polycaprolactone 3, tetraisopropylbis(dioctylphosphite acyloxy) titanate 1, anti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing process of an instrument carriage with raw materials containing ACS (acrylonitrile-chlorinated polyethylene-styrene) resins. The manufacturing process is characterized by respectively drying a material A and a material B at 100-120 DEG C for 3-5 hours, then uniformly mixing the material A and the material B according to parts by weight and then granulating the material A and the material B and remixing and then granulating the granulated material A and material B; and adding the obtained granulated materials to an injection molding machine to be molded and demolding the materials, thus obtaining the instrument socket, wherein the material B contains the ACS resins. The manufacturing process has the beneficial effects that the injection-molded instrument carriage for a car easily suffer from such physical property defects as drag marks, breakage, poor toughness and low strength during molding; and meanwhile, the injection molding process is good in stability, the obtained product has stable quality and high surface gloss, the production efficiency is improved and the production cost is reduced.

Description

technical field [0001] The invention relates to the field of automobile manufacturing, in particular to a manufacturing process of an instrument bracket whose raw material contains ACS resin. Background technique [0002] With the progress of society, the use of cars is increasing. [0003] In the prior art, the instrument brackets used in automobile manufacturing are mainly made of nylon materials, which are compounded by adding a toughening agent. After mixing various materials, the dispersion of each component is not good during the blending process, and the components are compatible. Poor performance, insufficient strength, toughness, and corrosion resistance, high material cost, difficult demoulding, poor surface gloss, poor processing performance, and unstable product quality. Contents of the invention [0004] In order to alleviate the deficiencies and defects of the prior art, the object of the present invention is to provide a manufacturing process for instru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/06C08L51/00C08L69/00C08L67/04C08L23/20C08K13/06C08K9/04C08K3/26C08K3/34C08K7/14C08K5/544C08K5/5425B29B9/06B29C47/92B29C45/76B29C48/92
CPCB29C48/04
Inventor 张强
Owner ANHUI KAIDI ELECTRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap