Fireproof diatomite plate and fabrication method thereof

A technology of diatomite and fireproof board is applied in the field of fireproof board, which can solve the problems of human health damage, waste, and large core board capacity, and achieve the effects of saving freight, reducing production cost and improving economic benefits.

Active Publication Date: 2013-04-03
营口盼盼硅藻材料集团有限公司
View PDF5 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, a large number of "aluminum silicate fiber materials" and "magnesite composite materials" are used in fireproof boards. Due to the production and use of products, fibers and halogens will be produced, which will cause damage to human health, and the existing problem is that the core Large plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The diatomite fireproof board consists of the following ingredients in parts by weight: 30 parts of tertiary diatomite, 50 parts of Portland cement, 5 parts of fly ash, 1 part of animal protein foaming agent, and 1 part of polyvinyl alcohol , 0.5 parts of NC-II type early strength agent, 0.5 parts of ACC foam stabilizer, and 1 part of polypropylene fiber.

[0016] The preparation method of the diatomite fire-proof board consists of the following steps: firstly add 6% polyvinyl alcohol aqueous solution into the mixer, start the machine, and then mix 200 mesh three-grade diatomite, Portland cement, pulverized coal Add ash, NC-II type early strength agent, insulation board foam stabilizer and polypropylene fiber into the mixer, stir for 2 minutes at 80 rpm at room temperature, add animal protein foaming agent with a foaming machine and continue stirring 2 minutes, until fully mixed into a paste; the material mixed into a paste is injected into a mold with a hopper to make ...

Embodiment 2

[0018] The diatomite fireproof board is composed of the following ingredients in parts by weight: 35 parts of secondary diatomite, 55 parts of sulphoaluminate cement, 5 parts of fly ash, 1.5 parts of vegetable protein foaming agent, and 1.5 parts of polyvinyl alcohol 1 part, 1 part of ACC accelerator, 1 part of cement foam stabilizer, 1.5 parts of carbon fiber.

[0019] The preparation method of the diatomite fireproof board consists of the following steps: first add 4% polyvinyl alcohol aqueous solution into the mixer, start the machine, and then mix 80-mesh second-grade diatomite, sulphoaluminate cement, pulverized coal Add ash, ACC quick-setting agent, cement foam stabilizer and carbon fiber into the mixer, stir for 3 minutes at 80 rpm at room temperature, add vegetable protein foaming agent with a foaming machine and continue stirring for 1 minute until fully mixed Uniformly form a paste; inject the material mixed into a paste into a mold with a hopper to make a diatomite ...

Embodiment 3

[0021] 33 parts of secondary diatomite in embodiment 2, 53 parts of sulphoaluminate cement, 5 parts of fly ash, 1.2 parts of synthetic foaming agent, 1.3 parts of polyvinyl alcohol, 0.8 part of ACC accelerator, cement foam stabilization 0.7 parts of agent, 1.2 parts of wood fiber. Others are identical with embodiment 2.

[0022] The preparation method of the diatomite fire-proof board is composed of the following steps: first, add 8% polyvinyl alcohol aqueous solution into the mixer, start the machine, and then mix 100 mesh second-grade diatomite, sulphoaluminate cement, powder Add coal ash, ACC quick-setting agent, cement foam stabilizer and wood fiber into the mixer, stir for 3 minutes at 80 rpm at room temperature, use a foaming machine to inject synthetic foaming agent and continue stirring for 1 minute until fully Mix evenly to form a paste; inject the material mixed into a paste into a mold with a hopper to make a diatomite fireproof board.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a fireproof plate, in particular to a fireproof diatomite plate and a fabrication method thereof. The fireproof diatomite plate comprises the following components in parts by weight: 30-35 parts of diatomite, 50-55 parts of cement, 5 parts of fly ash, 1-1.5 parts of foaming agent, 1-1.5 parts of polyvinyl alcohol, 0.5-1 parts of early strength agent or accelerating agent, 0.5-1 parts of foam stabilizer, and 1-1.5 parts of anti-cracking fiber. The fireproof diatomite plate has the advantages and the effects that the disadvantages that a core plate of the original fireproof door is large in unit weight, low in strength and high in hydroscopicity, erodes a steel plate, and cannot be bonded with the steel plate easily are overcome, and the fireproof diatomite plate is an optimal filling material for a fireproof door. The fireproof diatomite plate is green, environment-friendly, nontoxic, innocuous, fireproof, flame-retardant and smokeless, and does not erode the steel plate.

Description

technical field [0001] The invention relates to a fireproof board, in particular to a diatomite fireproof board and a preparation method thereof. Background technique [0002] At present, a large number of "aluminum silicate fiber materials" and "magnesite composite materials" are used in fireproof boards. Due to the production and use of products, fibers and halogens will be produced, which will cause damage to human health, and the existing problem is that the core Large plate volume, low strength, corroded steel plate, strong water absorption and difficult to bond with steel plate, high cost. The secondary and tertiary diatomite raw materials are low-value-added products. If the raw materials are not utilized, they will only be sold at a very low price or thrown away, resulting in waste. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the present invention provides a diatomite fireproof board and a preparation method thereof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B28/06
Inventor 梅长伏阎文吉凯
Owner 营口盼盼硅藻材料集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap