Method for preparing acrylic ester-styrene butadiene styrene (SBS) copolymer

A technology of -SBS and acrylate, which is applied in the field of preparation of acrylate-SBS copolymer, can solve the problems of short viscosity maintenance time, poor initial adhesion, and low bonding strength, so as to improve peel strength and enhance polarity , Improve the effect of adhesion

Inactive Publication Date: 2013-04-03
QINGDAO SAMUELS INDAL & COMML
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when SBS is used as an adhesive, due to the lack of polar groups of SBS itself, when it is applied to the bonding of polar materials,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A kind of preparation method of acrylate-SBS copolymer, its steps are specifically: (1) when 65 ℃, start stirring, and the rotating speed is 600r / min, and 50 parts of styrene-butadiene-styrene triblock copolymer (SBS) was dissolved in 20 parts of N-methylpyrrolidone (NMP). (2) Using methyl methacrylate (MMA) and dipropylene glycol diacrylate (DPGDA) as mixed monomers with a mass ratio of 1:1.3 and a total amount of 15 parts, the SBS was grafted and modified for 2 hours. (3) Add 1 part of initiator benzoyl peroxide (BPO), stir and react for 7 hours at a temperature of 83° C. and a rotation speed of 1000 r / min to obtain an acrylate-SBS copolymer.

[0012] The peel strength of acrylate-SBS copolymer is 8.1kN / m -1 .

Embodiment 2

[0014] A kind of preparation method of acrylate-SBS copolymer, its steps are specifically: (1) when 65 ℃, start stirring, and the rotating speed is 600r / min, and 50 parts of styrene-butadiene-styrene triblock copolymer (SBS) was dissolved in 20 parts of N-methylpyrrolidone (NMP). (2) Using methyl methacrylate (MMA) and dipropylene glycol diacrylate (DPGDA) as mixed monomers with a mass ratio of 1:1.3 and a total amount of 20 parts, the SBS was grafted and modified for 2 hours. (3) Add 1 part of initiator benzoyl peroxide (BPO), stir and react for 7 hours at a temperature of 83° C. and a rotation speed of 1000 r / min to obtain an acrylate-SBS copolymer.

[0015] The peel strength of acrylate-SBS copolymer is 8.6kN / m -1 .

Embodiment 3

[0017] A kind of preparation method of acrylate-SBS copolymer, its steps are specifically: (1) when 65 ℃, start stirring, and the rotating speed is 600r / min, and 50 parts of styrene-butadiene-styrene triblock copolymer (SBS) was dissolved in 20 parts of N-methylpyrrolidone (NMP). (2) Using methyl methacrylate (MMA) and dipropylene glycol diacrylate (DPGDA) as mixed monomers with a mass ratio of 1:1.3 and a total amount of 25 parts, the SBS was grafted and modified for 2 hours. (3) Add 1 part of initiator benzoyl peroxide (BPO), stir and react for 7 hours at a temperature of 83° C. and a rotation speed of 1000 r / min to obtain an acrylate-SBS copolymer.

[0018] The peel strength of acrylate-SBS copolymer is 8.3kN / m -1 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing an acrylic ester-styrene butadiene styrene (SBS) copolymer. The method comprises a step of performing graft modification on SBS in a solvent N-class A pyrrolidone (NMP) by using the SBS triblock copolymer as a matrix and methyl methacrylate (MMA), dipropylene glycol diacrylate ester (DPGDA) as a mixed monomer. An ester group and a carboxyl group are introduced into the SBS, so that the polarity of the SBS is increased, and the method is high in binding performance for the SBS subjected to graft modification and the polarity material.

Description

technical field [0001] The invention relates to a preparation method of acrylate-SBS copolymer, which belongs to the field of chemical industry. technical background [0002] SBS is a thermoplastic elastomer, which is easy to dissolve in non-polar solvents, and has the characteristics of low melt viscosity and easy modification. It is widely used in architectural decoration, paper-plastic lamination, pressure-sensitive adhesives and other industries. However, when SBS is used as an adhesive, because SBS itself lacks polar groups, when it is applied to bonding polar materials, it has disadvantages such as poor initial adhesion, low bonding strength, and short viscosity maintenance time, which limits its application. Therefore, the introduction of polar groups on SBS was originally modified to increase the compatibility and bonding performance of SBS and polar materials. Contents of the invention [0003] The purpose of this invention is to provide a kind of preparation met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F287/00
Inventor 袁三平
Owner QINGDAO SAMUELS INDAL & COMML
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap