Preparation method of double-faced compound warm-keeping and energy-saving wallboard
A technology of composite thermal insulation and wall panels, applied in the direction of chemical instruments and methods, hydraulically coagulable material layered products, layered products, etc., can solve problems such as environmental pollution and occupation of land resources, achieve good fire performance, and conform to circular economy Requirements, the effect of good building energy saving effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0019] (1) Prepare the panel: Pour 50% of the bottom ash, 20% of the ground sand and 15% of the lime in the mixer into the mixer and mix evenly, then add 15% of the water and continue to stir until Dry hard slurry, inject the slurry into the prepared panel mold, and then place a certain amount of steel mesh. After three rolls, the bulk density will reach 1900kg / m 3 , and then sent to the autoclave for 8 hours, the temperature and pressure of the water vapor in the autoclave were 200 ° C, 1.6 MPa, and the temperature was naturally cooled for 2 hours after leaving the autoclave. After demoulding, three thicknesses of 6mm, 8mm, and 10mm can be obtained panel.
[0020] (2) Preparation of wall panels: First, fix the two prepared panels on both sides of the wall panel mold according to the design requirements. In addition, by mass percentage, 40% of the bottom ash after incineration of domestic waste for power generation, 10% of lime, 20% of ground sand, 10% of cement, 2% of gypsum...
Embodiment 2
[0022] (1) Preparation of panels: Pour 65% of the bottom ash, 15% of finely ground sand and 5% of lime by mass percentage into the mixer and mix evenly, then add 15% of water and continue to stir until dry For hard slurry, inject the slurry into the prepared panel mold, and then place a certain amount of steel mesh. After three rolls, the bulk density will reach 2200kg / m 3 , and then sent to the autoclave for 8 hours, the temperature and pressure of the water vapor in the autoclave were 184 ° C, 1.2 MPa, and the temperature was naturally cooled for 2 hours after leaving the autoclave. After demoulding, three thicknesses of 6mm, 8mm, and 10mm can be obtained. panel.
[0023] (2) Preparation of wall panels: First, fix the two prepared panels on both sides of the wall panel mold according to the design requirements. In addition, by mass percentage, 30% of the bottom ash after incineration of domestic waste for power generation, 15% of lime, 15% of ground sand, 15% of cement, 4% ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com