Composite silicate heat-insulating coating

A composite silicate and thermal insulation coating technology, applied in the coating field, can solve the problems of poor decoration, weak impact resistance, long drying cycle, etc., achieve good film-forming and waterproof effects, and overcome the effects of poor water resistance

Inactive Publication Date: 2013-04-17
QINGDAO CREEK NEW ENVIRONMENTAL PROTECTION MATERIAL
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Composite silicate thermal insulation coating is currently the most widely used thermal insulation coating, but there are still the following defects: long drying cycle, weak impact resistance, poor decoration, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1 A composite silicate thermal insulation coating

[0020] Composed of raw materials with the following weight components:

[0021] 15 parts silicone resin

[0022] meerschaum 10 parts

[0023] Serpentine fiber 15 parts

[0024] 5 parts expanded perlite

[0025] 3 servings of floating beads

[0026] 15 parts of hydroxymethyl cellulose

[0027] Silica sol 5 parts

[0028] 8 parts polyacrylamide

[0029] Compound penetrating agent 3 parts

[0030] Ethylenediamine 5 parts

[0031] Tris(2-chloropropyl) phosphate 2 parts

[0032] 35 parts of water

Embodiment 2

[0033] Example 2 A composite silicate thermal insulation coating

[0034] Composed of raw materials with the following weight components:

[0035] 15 parts silicone resin

[0036] 15 parts meerschaum

[0037] Serpentine fiber 10 parts

[0038] 5 parts expanded perlite

[0039] 4 servings of floating beads

[0040] 15 parts of hydroxymethyl cellulose

[0041] Silica sol 5 parts

[0042] 7 parts polyacrylamide

[0043] Compound penetrating agent 4 parts

[0044] Ethylenediamine 4 parts

[0045] Tris(2-chloropropyl) phosphate 3 parts

[0046] 32 parts of water

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses composite silicate heat-insulating coating. The traditional binder water glass is replaced by the composite effect of organic resin and inorganic binder, so that better film-forming and waterproof effects are achieved, and the defects that the conventional heat-insulating coating has low water resistance and cannot reach the fireproof requirement are overcome.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a composite silicate thermal insulation coating. Background technique [0002] With the increasing energy consumption, the issue of energy conservation has also attracted much attention, and the market for thermal insulation materials, especially coatings, is optimistic. [0003] Composite silicate thermal insulation coating is currently the most widely used thermal insulation coating, but it still has the following defects: long drying cycle, weak impact resistance, poor decoration, etc. Contents of the invention [0004] In order to solve the above problems, a composite silicate thermal insulation coating was invented. The coating of the present invention is made up of the raw material of following weight component: [0005] 15 parts silicone resin [0006] 10~15 parts of meerschaum [0007] Serpentine fiber 10~15 parts [0008] Expanded perlite 3~5 parts [0009] 3~5 servings o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/24
Inventor 翟传伟李壮贤
Owner QINGDAO CREEK NEW ENVIRONMENTAL PROTECTION MATERIAL