An environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material and its preparation process

A polyvinyl chloride cable, high insulation technology, applied in the direction of organic insulators, plastic/resin/wax insulators, etc., can solve the problems of insufficient electrical insulation performance, influence on power supply reliability, and insufficient low temperature resistance, etc., to shorten the processing cycle and achieve good Compatibility and stability, effect of reducing mixing time

Active Publication Date: 2015-10-28
深圳市帝源新材料科技股份有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the long-term outdoor operation and the relatively low winter temperature in most parts of northern my country, ordinary PVC insulation materials have been used due to their relatively thin insulation thickness. Breakdown and other problems seriously affect the reliability of power supply

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material and its preparation process
  • An environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material and its preparation process
  • An environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The environment-friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material of the present embodiment and its content are:

[0051] 100 parts of polyvinyl chloride;

[0052] 30 parts of organic modified kaolin;

[0053] 50 parts of plasticizer;

[0054] 5 parts of stabilizer;

[0055] 5 parts of flame retardant;

[0056] Low temperature impact toughening agent 5 parts;

[0057] 1 part lubricant;

[0058] Coloring agent 0.5 parts.

[0059] The specific process of the preparation process of the environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material of this embodiment is as follows:

[0060] S11: Weigh each component according to the above formula of environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material, and divide the plasticizer into two parts, one of which is 70% of the plasticizer;

[0061] S12: Add...

Embodiment 2

[0066] The environment-friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material of the present embodiment and its content are:

[0067] 100 parts of polyvinyl chloride;

[0068] 40 parts of organically modified kaolin;

[0069] 70 parts of plasticizer;

[0070] 10 parts of stabilizer;

[0071] 10 parts of flame retardant;

[0072] 8 parts of low temperature impact toughening agent;

[0073] 3 parts lubricant;

[0074] Coloring agent 1 part.

[0075] The specific process of the preparation process of the environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material of this embodiment is as follows:

[0076] S21: Weigh each component according to the above formula of environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material, and divide the plasticizer into two parts, one of which is 90% of the plasticizer;

[0077] S...

Embodiment 3

[0082] The environment-friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material of the present embodiment and its content are:

[0083] 100 parts of polyvinyl chloride;

[0084] 35 parts of organically modified kaolin;

[0085] 60 parts of plasticizer;

[0086] 7 parts of stabilizer;

[0087] 7 parts of flame retardant;

[0088] 6 parts of low temperature impact toughening agent;

[0089] 2 parts lubricant;

[0090] Coloring agent 0.8 parts.

[0091] The specific process of the preparation process of the environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material of this embodiment is as follows:

[0092] S31: Weigh each component according to the formula of the above-mentioned environmentally friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material, and divide the plasticizer into two parts, one of which is 80% of the plasticiz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention provides an environment-friendly nontoxic high-insulation low temperature-resistant polyvinyl chloride cable material which comprises, by weight, 100 parts of polyvinyl chloride, 30 to 40 parts of organic modified kaolin, 50 to 70 parts of a plasticizer, 5 to 10 parts of a stabilizing agent, 5 to 10 parts of a fire retardant, 5 to 8 parts of a low temperature antishock toughening agent and 1 to 3 parts of a lubricant. The invention further provides a preparation process for the anti-tarnish crosslinked polyvinyl chloride material. The environment-friendly nontoxic high-insulation low temperature-resistant polyvinyl chloride cable material provided by the invention has the advantages of low cost for raw materials, environment-friendliness, excellent insulating properties and low temperature resistance and wide application prospects.

Description

technical field [0001] The invention belongs to the technical field of polymer material modification, and specifically relates to an environment-friendly, non-toxic, high-insulation and low-temperature-resistant polyvinyl chloride cable material and a preparation process thereof. Background technique [0002] With the rapid development of the national grid construction, more and more high-voltage power cables are used, and people's requirements for power supply reliability are getting higher and higher. In order to ensure the safe and stable operation of cables, all kinds of safety problems such as grounding wires and coaxial cables in newly commissioned and operating lines should be eliminated. [0003] At present, coaxial cables and grounding cables are mostly made of ordinary polyvinyl chloride insulation materials, and the insulation thickness is 2.0~2.5mm. Due to the long-term outdoor operation and the relatively low winter temperature in most parts of northern my coun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06H01B3/44C08K13/06C08K9/06C08K3/34
Inventor 张万涛曹明勇曾美昌熊陶
Owner 深圳市帝源新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More