A collagen squalane composition and its preparation, its preparation method and application

A technology of collagen and squalane, which is applied in application, food preparation, drug combination, etc., can solve the problem of low transdermal absorption rate and transdermal absorption rate, which affects patch whitening, moisturizing, anti-wrinkle and repairing, and is not easy Through the skin and other problems, it can reduce the dosage, improve the bioavailability, and increase the transdermal penetration rate.

Active Publication Date: 2014-10-22
ZHEJIANG HAILISHENG BIOTECH +2
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] At present, the collagen product on the market is collagen aqueous solution dressing patch (manufactured by Guangzhou Chuanger Biological Co., Ltd.), because the molecular weight of collagen in the dressing patch is relatively large, it is not easy to penetrate the skin and has a transdermal absorption rate. and low transdermal absorption rate, thus affecting the whitening, moisturizing, anti-wrinkle and repairing effects of the patch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A collagen squalane composition and its preparation, its preparation method and application
  • A collagen squalane composition and its preparation, its preparation method and application
  • A collagen squalane composition and its preparation, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-9

[0059] Examples 1-9 Preparation of Collagen Squalane Emulsion and Study on Transdermal Penetration Rate

[0060] The composition of the collagen squalane emulsion in Examples 1-9 is shown in Table 1.

[0061] Table 1

[0062]

[0063] The preparation method of collagen squalane emulsion in embodiment 1-9 may further comprise the steps:

[0064] 1) According to Table 1, weigh or measure the amount of squalane and its surfactants described in Examples 1-9 respectively, put them together, stir evenly, add an appropriate amount of distilled water, and use a high-speed homogenizer to Stir, 10000 rpm, until squalane emulsion is formed;

[0065] 2) According to Table 1, weigh or measure the collagen of the composition amount described in Examples 1-9, respectively add them to the squalane emulsion prepared in step 1), and adjust the pH to 0.1% acetic acid solution to 4.0-7.5, add an appropriate amount of distilled water, set the volume to 100ml, and mix evenly to prepare a c...

Embodiment 10-18

[0081] Examples 10-18 Preparation of Collagen Squalane Dressing Patches

[0082] The collagen squalane emulsions prepared in Examples 1-9 were prepared into collagen squalane dressings according to the following preparation methods.

[0083] The preparation method of embodiment 10-18 collagen squalane dressing patch, comprises the following steps:

[0084] 1) Fold the non-woven fabric, put it into an aluminum foil bag, add 20ml of the collagen squalane microemulsion prepared in any one of the examples 1-9 to each aluminum foil bag, number, seal;

[0085] 2) with Co 60 Irradiated at 15-25Kgy / h for 3h-5h to sterilize.

Embodiment 19

[0086] Example 19 Study on Particle Size of Collagen Squalane Emulsion

[0087] Adopt laser particle size analyzer (Delsa Nano C particle Analyzer, Beckman Co μlter), measure the particle size distribution of embodiment 1-2 collagen squalane emulsion, the results are shown in Figure 2-Figure 3 .

[0088] Wherein the test condition and result of embodiment 1 are as follows:

[0089] Temperature: 24.8°C

[0090] Thinner: water

[0091] Refractive index: 1.3328

[0092] Viscosity: 0.8919

[0093] Scattering intensity: 9736(cP)

[0094] The particle size-intensity distribution table of table 4 embodiment 1

[0095]

[0096]

[0097] It can be seen from the statistics in the above table that D (10%): 51.90 (nm) D (50%): 95.80 (nm) D (90%): 180.60 (nm).

[0098] The test condition and result of embodiment 2 are as follows:

[0099] Temperature: 0.1°C;

[0100] Thinner: water;

[0101] Refractive index: 1.3345;

[0102] Viscosity: 1.7831;

[0103] Scattering inte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
water absorptionaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a collagen and squalane composition. The composition comprises 0.1-20 parts by weight of collagen, 0.1-30 parts by weight of squalane and 1-150 parts by weight of a pharmaceutically acceptable carrier. The invention also relates to preparations containing the collagen and squalane composition, and a preparation method and an application of the composition. The collagen and squalane composition has the advantages of high biological availability, excellent curative effect, good stability, carrying and use convenience and the like.

Description

technical field [0001] The invention relates to the technical field of medical products, in particular to a collagen squalane composition and its preparation, its preparation method and application. Background technique [0002] Acne is a common chronic hair follicle and sebaceous gland inflammatory skin disease in adolescence. According to the survey, the incidence rate of acne among teenagers aged 12 to 25 is as high as 85%, and it mostly occurs on the face, and acne and its wounds are easy to form pigmentation after healing, which affects people's appearance. Studies have found that the main pathogenic factors of acne include skin allergies, excessive sebum production, hyperkeratosis of hair follicle orifice epithelium, and proliferation of Propionibacterium acnes in hair follicles. In addition, heredity, psychological factors, endocrine disorders, lipopolysaccharides, stimulating diet, high temperature and certain chemical factors may also cause acne. [0003] Skin all...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K38/39A61K8/65A23L1/29A61P17/10A61Q19/00A61K8/31A61K31/01A23L33/00
Inventor 夏志国张望刚袁军岳郑海辉
Owner ZHEJIANG HAILISHENG BIOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com