Composition of aluminum surface polishing agent

A technology of polishing agent and composition, applied in the field of polishing agent composition, can solve problems such as damage to the surface of aluminum products

Inactive Publication Date: 2013-06-05
孔龙
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, it can be polished to brighten the surface, but this will damage the surface of aluminum products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1, a kind of composition of aluminum surface polish, it is made by the raw material of following weight ratio,

[0015] Sulfamic acid 10; Nitric acid 15;

[0016] Ethylene glycol monobutyl ether 1; phosphoric acid 1;

[0017] Water 90.

Embodiment 2

[0018] Embodiment 2, a kind of composition of aluminum surface polish, it is made by the raw material of following weight ratio,

[0019] Sulfamic acid 20; Nitric acid 25;

[0020] Ethylene glycol monobutyl ether 10; phosphoric acid 5;

[0021] Water 100.

Embodiment 3

[0022] Embodiment 3, a kind of composition of aluminum surface polish, it is made by the raw material of following weight ratio,

[0023] Sulfamic acid 15; Nitric acid 20;

[0024] Ethylene glycol monobutyl ether 5; phosphoric acid 3;

[0025] Water 95.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a composition of an aluminum surface polishing agent. The composition of the aluminum surface polishing agent comprises, by weight, 10-20 parts of sulfamic acid, 15-25 parts of nitric acid, 1-10 parts of ethylene glycol monobutyl ether, 1-5 parts of phosphoric acid and 90-100 parts of water. When the composition of the aluminum surface polishing agent is prepared, the raw materials are sequentially added in the water and are evenly stirred. The composition of the aluminum surface polishing agent is simple to prepare, and convenient to use, can be directly used for wiping surfaces of aluminum products through wet cloth to ensure that shine of the surfaces of the aluminum products is quickly recovered, and does not corrode an aluminum surface.

Description

technical field [0001] The present invention relates to a composition of polish, especially a composition of aluminum surface polish. Background technique [0002] After the aluminum product is not used for a long time, a layer of oxide film will be formed on its surface, which will darken the surface of the aluminum product. Calcium scale, rust, oil and other dirt on the surface of aluminum products will also darken the surface. In the prior art, the surface can be brightened by grinding, but this will damage the surface of the aluminum product. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an aluminum surface polish composition that is easy to use and reasonably compatible in view of the deficiencies of the prior art. [0004] The technical problem to be solved by the present invention is achieved through the following technical solutions. The present invention is a kind of composition of aluminum surface ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/12
Inventor 孔龙
Owner 孔龙