Door manufactured by environment-friendly, energy-saving and fireproof composite board and manufacture method of composite board

A technology of environmental protection, energy saving, and production method, which is applied in the direction of fire doors, wooden veneer joints, manufacturing tools, etc., can solve the problems of poor fireproof performance of wooden fire doors, monotonous and disharmonious colors, peeling of wooden board layers, etc., and achieve saving Raw materials, extended service life, and improved fire performance

Inactive Publication Date: 2013-06-26
HEILONGJIANG HUAXIN FURNITURE
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the existing steel fire doors with poor thermal insulation, poor sound insulation, single appearance, and monotonous and disharmonious colors; The problem of spalling in a fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Door manufactured by environment-friendly, energy-saving and fireproof composite board and manufacture method of composite board
  • Door manufactured by environment-friendly, energy-saving and fireproof composite board and manufacture method of composite board
  • Door manufactured by environment-friendly, energy-saving and fireproof composite board and manufacture method of composite board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A method for making an environmentally friendly, energy-saving and fireproof multi-layer board, as attached figure 1 As shown, the method includes the following steps: the method includes two steps, the first step is to use pure solid wood to make the flame-retardant veneer, and the second step is to make the flame-retardant veneer cross one layer of vertical grain veneer and one layer of transverse grain veneer Arranged in a superimposed manner to make a fireproof multi-layer board.

Embodiment 2

[0053] The manufacturing method of the environment-friendly, energy-saving and fireproof multi-layer board described in Embodiment 1, as attached Figure 2-6 As shown, the first step is to use pure solid wood to make flame-retardant veneer. The first process is to soften the log. When the log is stored at an outdoor temperature below 0°C, first soak the log in water at 25-35°C for 6-10 hours. hours, and then steam the water with steam at 1.5 to 3 atmospheres;

[0054] The second process is to make the veneer, slice or peel the log into the veneer, first put the log on the planer or rotary cutter, adjust the speed, adjust the thickness to 2mm, and cut the log into the veneer of 1.8-2mm ;

[0055] The third process is to perform flame-retardant treatment on the veneer. ①Put the veneer with a moisture content of 70% into the flame-retardant mixture a for 48 hours, take it out, dry it, and dry it naturally until the moisture content is below 40%; Put 22 parts of triammoniu...

Embodiment 3

[0063] The manufacturing method of the environment-friendly, energy-saving and fireproof multi-layer board described in Embodiment 1, as attached Figure 2-6 As shown, in the second step, the flame-retardant veneers are arranged in a cross-overlay manner of one layer of longitudinal grain veneer 1 and one layer of transverse grain veneer 2 to make a fireproof multi-layer board, and the total number of layers is an odd number; the first The upper layer flame retardant panel, the middle layer flame retardant veneer and the lower layer flame retardant panel that have been coated with glue are pressed into shape at one time under high temperature and high pressure; Arrange according to the structure of one layer of vertical grain veneer and one layer of transverse grain veneer, put it into the hot press, and adjust the pressure to 15kg / cm 2 , the relatively high-quality veneer pressure is adjusted to 4 kg / cm 2 ;Adjust the compression ratio to 90%, heat pressing time is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a door manufactured by an environment-friendly, energy-saving and fireproof composite board and a manufacture method of the composite board. At present, fireproof doors on the market include two kinds including steel fireproof doors and wood fireproof doors, wherein the steel fireproof doors are manufactured by steel plates outside, and the interiors of the steel fireproof doors are filled with rock wool or expanded perlite. The manufacture method of the composite board comprises the following two steps. Firstly, pure solid wood is adopted to manufacture inflaming retarding veneers. Secondly, the inflaming retarding veneers are manufactured to be the fireproof composite board according to a manner that one layer of longitudinal texture veneers and one layer of transverse texture veneers are stacked in an intersected mode. The manufacture method is used for manufacturing the environment-friendly, energy-saving and fireproof composite board.

Description

technical field [0001] The invention relates to a production technology of a door made of an environmental protection, energy saving and fireproof multilayer board, in particular to a door made of an environmental protection, energy saving and fireproof multilayer board and its manufacturing method . Background technique [0002] At present, there are two types of fire doors on the market: steel fire doors and wooden fire doors. Steel fire doors are usually filled with steel plates, internal rock wool or expanded perlite; , density board or magnesium oxide, magnesium chloride board and other materials, internal rock wool or expanded perlite filling combination; [0003] The existing fire doors mainly have the following problems: steel fire doors have poor thermal insulation, poor sound insulation, single appearance, and monotonous and disharmonious colors, which affect the beauty of the public environment; The fire doors are easy to deform, and the fire performance is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E06B5/16B27M3/18B27D1/08B27K3/02
Inventor 张福贵吴海红张禄彬
Owner HEILONGJIANG HUAXIN FURNITURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com