Shaping glaze and firing technology of bone china containing high-permeability pigment

A high-permeability, pigment technology, used in the field of ceramic materials, can solve the problems of difficult to achieve blue and white porcelain, blurred patterns, weak density, etc., and achieve the effect of pure color, clear pattern, and no color flow.

Active Publication Date: 2013-07-03
SHENZHEN YONGFENGYUAN PORCELAIN
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, bone china is a medium-temperature ceramic with weak density.
Therefore, when bone china meets blue and white pigments, because the density of bone china products is low, and the pigments containing cobalt and chromium have high permeability, the result often causes the blue and white pigments on the fired bone china to penetrate into the bone. In the porcelain body of high-quality porcelain, the edges of the blue and white patterns tend to spread, resulting in blurred patterns and colored flowers, and it is difficult to achieve the general effect of blue and white porcelain, thus limiting the application of high-permeability pigments in bone china products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] To make a blue and white pattern bone china teacup, the specific steps are as follows:

[0039] 1. Take the mixture of potassium feldspar 3.9kg, kaolin 1.2kg, quartz 3.2kg, sintered talc 0.5kg, magnesium chloride 0.5kg, lead-free cadmium frit glaze 1.2kg and zirconium silicate 0.05kg Chromium-containing pigments and 5kg of cobalt-containing pigments are mixed with the ingredients, and then the mixture is mixed with 30kg of water;

[0040] 2. Put the mixture into the fast ball mill and grind it for 20 minutes, then pass the 350-mesh mesh grid, and take the fine powder material;

[0041] 3. Grind the bisque-fired bone china teacup porcelain embryo with blue and white patterns, and spray the above-mentioned fine powder material on the porcelain embryo as a setting glaze;

[0042] 4. Put the porcelain blank sprayed with the shaped glaze into the kiln for 15 hours at a temperature of 1250°C;

[0043] 5. After cooling, take out the porcelain embryo sprayed with the shaped g...

Embodiment 2

[0048] To make a blue and white pattern bone china teacup, the specific steps are as follows:

[0049] 1. Take the mixture of potassium feldspar 4.5kg, kaolin 0.7kg, quartz 2.0kg, sintered talc 0.35kg, magnesium chloride 0.6kg, lead-free cadmium frit glaze 1.8kg and zirconium silicate 0.05kg mixture as styling glaze ingredients, then take 1kg The chromium-containing pigment and 4kg of cobalt-containing pigment are mixed with the ingredients, and then the mixture is mixed with 35kg of water;

[0050] 2. Put the mixture into the rapid ball mill and grind it for 25 minutes, then pass the 350-mesh mesh grid, and take the fine powder material;

[0051] 3. Grind the bisque-fired bone china teacup porcelain embryo with blue and white patterns, and spray the above-mentioned fine powder material on the porcelain embryo as a setting glaze;

[0052]4. Put the porcelain blank sprayed with the setting glaze into the kiln for 13 hours at a temperature of 1256°C.

[0053] 5. After cooling,...

Embodiment 3

[0058] To make a blue and white pattern bone china vase, the specific steps are as follows:

[0059] 1. Take the mixture of 3.0 kg of potassium feldspar, 1.0 kg of kaolin, 3.6 kg of quartz, 0.4 kg of sintered talc, and 2.0 kg of lead-free cadmium frit glaze as a setting glaze ingredient, take 2.5 kg of chromium-containing pigment and mix with the ingredient, then The mixture was mixed with 18.75kg of water;

[0060] 2. Put the mixture into the rapid ball mill and grind it for 20 minutes, then pass the 400-mesh mesh grid, and take the fine powder material;

[0061] 3. Grind the bone china vase embryo with blue and white pattern after baking pigment, and spray the above-mentioned fine powder material on the porcelain embryo as a setting glaze;

[0062] 4. Put the porcelain blank sprayed with the shaped glaze into the kiln for 15 hours at a temperature of 1250°C;

[0063] 5. After cooling, take out the porcelain embryo sprayed with the shaped glaze;

[0064] 6. Add the surface...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to shaping glaze and a firing technology of bone china containing a high-permeability pigment. The shaping glaze consists of the high-permeability pigment and ingredients comprising components in percentage by weight as follows: 30% to 45% of potash feldspar, 5% to 12% of kaolinite, 20% to 40% of quartz, 2% to 6% of fired talc and 10% to 20% of lead-and-cadmium free fritted glaze. According to the firing technology, the shaping glaze is introduced, and three firing technologies of color baking, shaping glaze coating and surface layer glaze coating are used. According to the shaping glaze and the firing technology of the bone china containing the high-permeability pigment, the shaping glaze is introduced, and three firing technologies are used, so that conventional two times of high-temperature firing are broken through, the pigment containing cobalt and chromium is in the charge of the shaping glaze, the pigment is prevented from spreading and permeating, the problem that high-permeability pigments cannot be applied to a bone china product is fundamentally solved, and the color system of the bone china product is enriched.

Description

technical field [0001] The invention belongs to the field of ceramic materials, in particular to a component of a shaping glaze for bone china and a firing process of a bone china embryo containing high permeability pigments using the shaping glaze. [0002] Background technique [0003] Nowadays, among household porcelains, bone china products are favored by people because of their thin and translucent characteristics, but the colors are less than those of traditional Chinese ceramics. Especially the unique Chinese porcelain with blue and white patterns is very popular in the world. If the traditional blue and white patterns are applied to Bone china will have a huge impact. However, the traditional Chinese blue and white pattern is made of cobalt-containing and chromium-containing high-penetration pigments and other compositions in a certain proportion and then painted on the white porcelain embryo. Due to the traditional Chinese ceramic firing process and bone china Dep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 刘权辉王劲刘建广
Owner SHENZHEN YONGFENGYUAN PORCELAIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap