Method for preparing Pt-C3N4-TiO2 three-component visible light photocatalyst

A pt-c3n4-tio2 and photocatalyst technology, which is applied in the field of visible light photocatalyst preparation, can solve the problems such as the preparation of ternary composite photocatalysts that have not yet occurred, and achieves the effects of stable reaction, simple reaction conditions and easy to scale up production.

Inactive Publication Date: 2013-08-07
NANCHANG HANGKONG UNIVERSITY
View PDF2 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many studies on binary composite photocatalysts at home and abroad, but there is no preparation of Pt-C 3 N 4 -TiO 2 Report on Ternary Composite Photocatalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing Pt-C3N4-TiO2 three-component visible light photocatalyst
  • Method for preparing Pt-C3N4-TiO2 three-component visible light photocatalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] 1. Preparation of g-C by cleavage of melamine 3 N 4

[0013] Weigh 3.0000g of melamine and place it in a 50 mL porcelain crucible, put it in a muffle furnace, and raise the temperature from room temperature to 540 o C, after keeping the temperature for 2 h, cool down naturally. After cooling to room temperature, take out to obtain g-C 3 N 4 , after weighing, grind the sample into powder and save it.

[0014] 2. Preparation of g-C by ultrasonic mixing 3 N 4 / TiO 2

[0015] Weigh 0.1000 gTiO 2 Put four parts of solid powder in four 100 mL beakers, add 50 mL of absolute ethanol solution, and then add 0.002 g, 0.004 g, 0.008 g, 0.01 g of g-C 3 N 4 powder, namely to get g-C 3 N 4 / TiO 2 The mass ratios are: 2%, 4%, 8%, and 10%, respectively. Then ultrasonically mix for 15 min until the powder is completely dispersed. 80 o C dried for 5 h to evaporate to dryness to obtain a powder, which was ground and placed in a muffle furnace at 400 o C under calcination ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing a Pt-C3N4-TiO2 three-component visible light photocatalyst. The method is characterized by comprising the steps of: firstly heating melamine up to the temperature of 540 DEG C so as to be cracked into graphite-like nitrogen carbide (g-C3N4); then carrying out ultrasonic mixing so as to enable P25 to be loaded with g-C3N4; and finally synthesizing by using an immobilized sol process, thereby preparing the target product. The composite photocatalyst with the structure has high visible light activity, thus the photocatalyst becomes an important sewage treatment agent with a potential research value. The method has the advantages that the reaction conditions are simple, the reaction is mild and stable, and the production enlargement is facilitated.

Description

technical field [0001] The invention relates to a preparation method of a visible light photocatalyst, in particular to a Pt-C 3 N 4 -TiO 2 A preparation method of a ternary visible light photocatalyst. Background technique [0002] Pt-C 3 N 4 -TiO 2 The ternary visible light photocatalyst has become an important sewage treatment agent with potential research value because the composite photocatalyst containing this structure has visible light activity. There are many studies on binary composite photocatalysts at home and abroad, but there is no preparation of Pt-C 3 N 4 -TiO 2 A report on ternary composite photocatalysts. Therefore, there is no complete preparation method for synthesizing the ternary composite photocatalyst; for this fact, the present invention elaborates the whole preparation process: using melamine as raw material, followed by high-temperature cracking, ultrasonic mixing, immobilized sol process to finally prepare The target product was obtained...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/24
Inventor 吴小琴柳泽斌马文天李帅龙胡秋明廖黎明李建
Owner NANCHANG HANGKONG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap