Foam glass insulation board

A foam glass and thermal insulation board technology is applied in the field of building materials to achieve the effect of reducing pollution and solving energy saving and emission reduction.

Inactive Publication Date: 2014-12-24
JIAXING UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems existing in the recycling and treatment of existing foam glass, the present invention provides a foam glass insulation board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The board-making raw materials are prepared in parts by weight as follows: desulfurized gypsum 50, foam glass 20, fly ash 30, mineral powder 20, water 25, lime 2w / w% and sodium sulfate 1w / w%. After testing, the thermal conductivity of the prepared foam glass insulation board is 0.12w / m·k, the compressive strength reaches 1.0Mpa, and the bulk density is 637kg / m 3 .

Embodiment 2

[0017] The board-making raw materials are prepared in parts by weight as follows: desulfurized gypsum 50, foam glass 20, fly ash 30, mineral powder 20, water 25, lime 2w / w% and sodium sulfate 2w / w%. After testing, the thermal conductivity of the prepared foam glass self-insulating block is 0.14w / m·k, the compressive strength reaches 0.8Mpa, and the bulk density is 652kg / m 3 .

Embodiment 3

[0019] Prepare board raw materials in parts by weight as follows: desulfurized gypsum 40, foam glass 20, fly ash 20, mineral powder 40 and water 25, lime 2w / w% and sodium sulfate 2w / w%. After testing, the thermal conductivity of the prepared foam glass self-insulating block is 0.11w / m·k, the compressive strength of the block reaches 0.9Mpa, and the bulk density is 611kg / m 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a foam glass insulation board, comprising the following ingredients in parts by weight: 40-50 parts of desulfurization gypsum, 20-22 parts of foam glass, 20-30 parts of coal ash, 20-40 parts of mineral powder, 24-26 parts of water, 2 w / w% of lime, and 1-2 w / w% of admixture. The insulation board is prepared from foam glass scraps; the waste foam glass and the waste such as the desulfurization gypsum, the coal ash and the like of a thermal power plant are changed into precious resources by utilizing local resources; not only can the targets of saving energy and reducing emission of buildings be solved; but also the problems of no place to stack waste products and the like are solved; the pollution on the environment is reduced; the foam glass insulation board accords with the principle of sustainable development; the heat conductivity coefficient of the prepared foam glass insulation board is 0.10-0.15 w / m.k; the compressive strength achieves over 0.8 Mpa; and the volume density is 600-700 kg / m<3>.

Description

technical field [0001] The invention relates to a building material, in particular to a foam glass insulation board. Background technique [0002] At present, foam glass is widely used in domestic and foreign buildings because of its excellent thermal insulation performance. However, in the production process, a large amount of discarded foam glass scraps will be generated due to cutting and other reasons. According to the survey, a foam glass company in Jiaxing produces 20,000 cubic meters of waste foam glass every year, causing great environmental pollution and waste of resources. Recycling waste foam glass scraps, supplemented by thermal power plant waste desulfurization gypsum and fly ash and other cementitious materials to make self-insulation boards, not only energy-saving, environmental protection, but also can avoid alkali-aggregate reaction, and achieve fire prevention in essence , durable and corrosion-resistant. The raw material price of the insulation board is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/14C04B18/04
CPCY02W30/91
Inventor 薛力梨刘红飞牛志荣
Owner JIAXING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com