Low-water absorption stoneware and production method thereof

A technology with low water absorption rate and production method, which is applied in the field of low water absorption rate stoneware and its production, and the field of stoneware production and products, can solve the problems of reducing water absorption rate, low water absorption rate, low water absorption rate, etc., and achieves reducing water absorption rate. , Guaranteed quality effect

Active Publication Date: 2013-12-11
HUNAN HUALIAN CHINA IND
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The purpose of the present invention is to solve the problem of high water absorption of existing stoneware, and propose a stoneware product with lower water absorption and its production method. The main purpose is to reduce the water absorption of existing daily-use stoneware products and provide a low water absorption Stoneware product and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of stoneware with low water absorption rate, the ingredients are formulated according to the following percentages by weight: 33 parts of albite, 20 parts of quartz, 45 parts of kaolin, and 2 parts of additives;

[0035] And ensure that the weight percentages of K, Na, Fe, and Ti in the stoneware products are: K 1%-1.5%; Na 2.5%-3%; Fe <0.9%; Ti <0.15%.

[0036] The additive is lithium china stone powder.

[0037] A method for preparing stoneware with low water absorption rate, comprising the following steps.

[0038] Step 1: Albite, quartz, and kaolin are selected as raw materials, hard raw materials are crushed, and impurities are removed.

[0039] In step 2, ingredients are formulated according to the following weight percentages: 33 parts of albite, 20 parts of quartz, 45 parts of kaolin, and 2 parts of additives.

[0040] Step 3: add water and dispersant, pack into balls, and mill for 8 hours.

[0041] Step 4, fineness test, pulping, iron removal, pulping...

Embodiment 2

[0048] A kind of stoneware with low water absorption rate, the ingredients are formulated according to the following percentages by weight: 35 parts of albite, 18.7 parts of quartz, 45 parts of kaolin, and 1.3 parts of additives;

[0049]And ensure that the weight percentages of K, Na, Fe, and Ti in the stoneware products are: K 1%-1.5%; Na 2.5%-3%; Fe <0.9%; Ti <0.15%.

[0050] The additive is a mixture formed by mixing lithium china stone and talc; the ratio of lithium china stone and talc is arbitrary and can be determined according to the user's requirements for product quality and cost. Generally, the weight ratio of lithium china stone and talc is selected. The ratio is: 10:1-5 ratio.

[0051] A method for preparing stoneware with low water absorption rate, comprising the following steps.

[0052] Step 1: Albite, quartz, and kaolin are selected as raw materials, hard raw materials are crushed, and impurities are removed.

[0053] In step 2, ingredients are formulated a...

Embodiment 3

[0062] A kind of stoneware with low water absorption rate, the ingredients are formulated according to the following weight percentage: 30 parts of albite, 25 parts of quartz, 50 parts of kaolin, and 1 part of additive;

[0063] And ensure that the weight percentages of K, Na, Fe, and Ti in the stoneware products are: K 1%-1.5%; Na 2.5%-3%; Fe <0.9%; Ti <0.15%.

[0064] The additive is a mixture formed by mixing lithium china stone and talc; the proportion of lithium china stone and talc is 10:2-3 in parts by weight.

[0065] A method for preparing stoneware with low water absorption rate, comprising the following steps.

[0066] Step 1: Albite, quartz, and kaolin are selected as raw materials, hard raw materials are crushed, and impurities are removed.

[0067] In step 2, ingredients are formulated according to the following weight percentages: 30 parts of albite, 25 parts of quartz, 50 parts of kaolin, and 1 part of additive.

[0068] Step 3: add water and dispersant, pack...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A low-water absorption stoneware product is prepared from the following components in parts by weight: 30 to 40 parts of sodaclase, 15 to 25 parts of quartz, 40 to 50 parts of kaolinite and 1 to 2 parts of additive; the percentage content of K, Na, Fe and Ti in the stoneware product is guaranteed to be the followings in percentage by weight: 1 to 1.5 percent of K, 2.5 to 3 percent of Na, less than 0.9 percent of Fe, and less than 0.15 percent of Ti. The additive is a mixture formed by mixing lithium porcelain stone or lithium porcelain stone with soapstone; the mixing ratio of the lithium porcelain stone and the soapstone is optional, and can be selected according to the requirements of the cost and the quality of a product. The production method of the low-water absorption stoneware product comprises the steps of sorting, batching, ball milling, slurry discharging, squeezing, primary refining, refining, staling, blank making and burning; according to the invention, through rationally selecting raw material formulation and adding moderate lithium porcelain stone or lithium porcelain stone to be mixed with the soapstone to form the mixture serving as the additive, not only is the conventional firing temperature of the stoneware followed, but also the water absorption can be effectively lowered, and the product quality is ensured.

Description

technical field [0001] The invention relates to a ceramic product and a manufacturing method thereof, in particular to a stoneware with a low water absorption rate and a manufacturing method thereof, and is mainly suitable for making stoneware and its products. Background technique [0002] Stoneware, also known as "stone-bodied porcelain", is one of many types of ceramics. It is fired at a high temperature of about 1,200°C to achieve vitrification (that is, similar to glass, impermeable to liquids). Stoneware is loved by users all over the world because of its compact body, high strength and good thermal stability, lead-free, non-toxic, high-quality and environmentally friendly. However, in the process of making stoneware, the high water absorption rate of stoneware has always been a difficult problem in daily-use stoneware products. Under the premise of controlling cost and quality, appropriate water absorption rate is conducive to improving the service life of products. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C04B33/22
Inventor 麦潮棠谢富飞周志扬
Owner HUNAN HUALIAN CHINA IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com