Additive for pervious concrete and application thereof

A permeable concrete and admixture technology, which is applied in the field of concrete admixtures, can solve the problems of low strength, poor work performance, and poor durability in the later stage, and achieve the effects of improving fluidity, preventing drying and condensation, and improving durability and strength in the later stage

Inactive Publication Date: 2013-12-25
JIANGSU MINGHE GRP
View PDF3 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To meet the above requirements, special admixtures need to be adjusted. At present, there is no special admixture for permeable concrete. In actual projects, ordinary concrete admixtures are often used instead, which will cause permeable conc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Additive for pervious concrete and application thereof
  • Additive for pervious concrete and application thereof
  • Additive for pervious concrete and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0013] Example 1: (1) According to mass ratio polyethylene glycol: butyl methacrylate: methyl methacrylate: alkenyl ether-based polyoxyethylene: maleic anhydride: water = 2:2:5:25:5: 61. Mix the components in a proportion and react at 70~100℃ until a yellow-brown viscous liquid appears to prepare a polycarboxylic acid water-reducing agent; (2) The mass ratio of sodium lauryl sulfate: stearic acid: sulfonic acid Melamine=75:15:10 ratio and mix the components to prepare air-entraining agent; (3) According to the mass ratio of polycarboxylic acid water reducing agent: aminotrimethyl phosphoric acid: hydroxymethyl cellulose ether ether: air-entraining Agent: water=40:2.5:1:0.5:56 in proportions of the components, mixed and stirred uniformly to obtain an admixture for permeable concrete. When the concrete is prepared according to the C25 permeable concrete construction mix ratio, the amount of the above-mentioned admixture is 1.8% of the mass of the cementitious material. The perfor...

Example Embodiment

[0015] Example 2: (1) According to the mass ratio polyethylene glycol: butyl methacrylate: methyl methacrylate: alkenyl ether-based polyoxyethylene: maleic anhydride: water = 2:2:5:25:5: 61. Mix the components in a proportion and react at 70~100℃ until a yellow-brown viscous liquid appears to prepare a polycarboxylic acid water-reducing agent; (2) The mass ratio of sodium lauryl sulfate: stearic acid: sulfonic acid Melamine=80:10:10 ratio and mix the components to prepare air-entraining agent; (3) According to the mass ratio of polycarboxylic acid water reducing agent: phosphinobutane tricarboxylic acid: polyacrylamide: air-entraining agent: water =48:2.3:0.9:0.8:48 proportion of each component, mixing and stirring uniformly, to obtain the admixture for permeable concrete. When preparing concrete according to the C25 permeable concrete construction mix ratio, the amount of the above-mentioned admixture is 2.0% of the mass of the cementitious material. The performance test resul...

Example Embodiment

[0017] Example 3: (1) According to the mass ratio polyethylene glycol: butyl methacrylate: methyl methacrylate: alkenyl ether-based polyoxyethylene: maleic anhydride: water = 2:2:5:25:5: 61. Mix the components in a proportion and react at 70~100℃ until a yellow-brown viscous liquid appears to prepare a polycarboxylic acid water-reducing agent; (2) The mass ratio of sodium lauryl sulfate: stearic acid: sulfonic acid Melamine=78:12:12 to mix the components to prepare air-entraining agent; (3) According to the mass ratio of polycarboxylic acid water reducer: phosphinobutane tricarboxylic acid: starch: air-entraining agent: water = 46 2:2.3:1:0.8:48 ratio of each component, mixing and stirring uniformly, to obtain an admixture for permeable concrete. When preparing concrete according to the C25 permeable concrete construction mix ratio, the amount of the above-mentioned admixture is 2.0% of the mass of the cementitious material. The performance test results of the above-mentioned a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an additive for pervious concrete. The additive for the pervious concrete comprises a water reducer, a retarder, a viscosity modifier, an entraining agent and water, wherein the mass ratio of the water reducer to the retarder to the viscosity modifier to the entraining agent to the water is (30-50): (1-3): (0.5-3): (0.3-1.5): (42-60). The invention further discloses the application of the additive for the pervious concrete. The additive for the pervious concrete has the advantages that for the application requirement of the pervious concrete, the additive special for the pervious concrete is provided; after the additive is added to the pervious concrete to be used, the fluidity of the pervious concrete can be improved, premature drying and condensation can be avoided, unloading is facilitated, and the durability and the long-term strength of the previous concrete are improved.

Description

technical field [0001] The invention relates to an admixture for concrete and its application, in particular to an admixture for permeable concrete and its application. Background technique [0002] Permeable concrete is an eco-friendly concrete. It is a concrete with continuous pores made through material research and special technology. It has both certain strength and certain air and water permeability. Permeable concrete is a pavement material that can not only satisfy the road performance, but also coexist harmoniously with the natural environment, and construct a comfortable living environment for human beings. The circulation of water is of great significance to increasing groundwater resources in cities, alleviating the heat island effect, and improving the urban climate. [0003] The successful application of pervious concrete requires the following: it can be quickly unloaded from the mixer truck and achieve a certain degree of compactness, and there is no flow of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/38C04B24/26C04B24/24
Inventor 臧军王晓明宋生辉马树泉
Owner JIANGSU MINGHE GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap