Preparation method of chromite oxide pellets

A technology for oxidizing pellets and chromite ore, which is applied in the field of chromite mineral agglomeration, can solve the problems of poor high-temperature smelting performance and low strength, and achieve good spheroidizing effect

Active Publication Date: 2015-09-16
INNER MONGOLIA BAOTOU STEEL UNION
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for preparing chromite oxide pellets to solve the problems of poor high-temperature smelting performance and low strength of the agglomerates existing in the existing chromite agglomeration technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of chromite oxide pellets
  • Preparation method of chromite oxide pellets
  • Preparation method of chromite oxide pellets

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The present invention will be further described below in conjunction with drawings and embodiments.

[0018] Such as figure 1 Shown, the preparation method of chromite oxide pellets is as follows:

[0019] S1: Add 1%-2% bentonite, 1%-2% metallurgical coke powder and 0.5%-2% dolomite to the chromium-containing raw material according to the weight percentage, and mix thoroughly to obtain a mixture. Preferably, the bentonite is sodium bentonite.

[0020] S2: The mixed material is moistened and ground into a fine powder, wherein the powder with a particle size of 200 mesh accounts for 80%±2% of the total fine powder volume, and pelletized to obtain green pellets.

[0021] S3: The raw balls are dried at a temperature of 450-600° C. for 5-10 minutes to obtain dry balls.

[0022] S4: Preheating the dry bulbs at a temperature of 1150-1250° C. for 5-10 minutes to obtain preheated bulbs.

[0023] S5: The preheated balls are roasted at a temperature of 1300-1350° C. for 5-10 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a chromite oxide pellet. Raw materials of the chromite oxide pellet comprise 40-60wt% of first chromite, 10-15wt% of second chromite, 25-50wt% of third chromite, 1-2wt% of bentonite, 1-2wt% of metallurgical coke powder and 0.5-2wt% of dolomite. The invention also discloses a preparation method of the chromite oxide pellet. The prepared chromite oxide pellet has a good ballability, a high strength and an excellent smelting performance.

Description

technical field [0001] The invention relates to the technical field of chromite mineral agglomeration, in particular to a preparation method of chromite oxide pellets. Background technique [0002] Chromium is a strategically important metal that always coexists with iron in nature to form ferrochrome spinel (FeO Cr 2 o 3 ), its mineralogical name is chromite (David, Shuli. Ferroalloy Metallurgical Engineering, Beijing: Metallurgical Industry Press, 1999, 92: 121-122). In the metallurgical industry, chromite ore is mainly used to produce ferrochrome alloy and metallic chromium. Ferrochrome alloy is used as a steelmaking additive to produce a variety of high-strength, corrosion-resistant, and oxidation-resistant special steels, and is widely used in aviation, automobiles, shipbuilding, and military industries. With the development of stainless steel products, the metallurgical industry's demand for chromite will also increase (Liu Yuangen. Conference on Rational Exploitati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B1/24C22B1/16C22B34/32
Inventor 付国伟邬虎林吕志义白晓光沈茂森张永李玉柱刘周利赵永红
Owner INNER MONGOLIA BAOTOU STEEL UNION