Scouring method of real silk fabric

A silk fabric and refining agent technology, applied in animal fibers, textiles, papermaking, fiber processing, etc., can solve the problems of increased production difficulty, poor fabric whiteness, and long refining time, so as to avoid gray damage and excellent whiteness , The effect of simple refining process

Active Publication Date: 2013-12-25
山东信开源科技创新发展有限责任公司
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The various physical indexes of the above-mentioned soap-alkaline refining are basically within the standard range, and the silk fabric has good smoothness and bright luster, but the soap consumption is large, the cost is high, the refining time is too long, and the whiteness of the fabric after refining is poor, and the water discharge is poor. unclear, and the refining time is long and the temperature is high, which increases the difficulty of production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A method for refining silk fabrics, comprising the steps of:

[0017] (1) Peracid pretreatment: Put the raw silk into the acid solution at a temperature of 50-60°C for pretreatment, the silk is puffed, and then the gray silk obtained is decompressed twice by a vacuum machine , after the silk fabric has fully absorbed water, put it into the puffing agent and soak it for 10 minutes, the puffed pretreated silk can effectively avoid gray damage;

[0018] (2) Preliminary training: Put the pretreated silk fabric in step (1) into the refining agent for preliminary training for 10 minutes. The pH value of the preliminary training solution is 7, and the initial training temperature is 60-65°C. The refining agent is A compound of alkali refining agent and surfactant refining agent, the surfactant in the described surfactant refining agent is natural tea saponin, and the alkali in the described alkali refining agent is sodium oleate, and the alkali The mass ratio of refining agen...

Embodiment 2

[0022] A method for refining silk fabrics, comprising the steps of:

[0023] (1) Peracid pretreatment: the raw silk is put into acid solution at a temperature of 50-60°C for pretreatment, the silk is puffed, and then the obtained gray silk is decompressed for 3 times by a vacuum machine , after the silk fabric has fully absorbed water, put it into the puffing agent and soak it for 15 minutes, the puffed pretreated silk can effectively avoid gray damage;

[0024] (2) Preliminary training: Put the pretreated silk fabric in step (1) into the refining agent for preliminary training for 15 minutes. The pH value of the preliminary training solution is 8, and the initial training temperature is 60-65°C. The refining agent is A compound of an alkali refining agent and a surfactant refining agent, the surfactant in the surfactant refining agent is sucrose fatty acid ester, and the alkali in the alkali refining agent is sodium oleate, and the alkali The mass ratio of refining agent and...

Embodiment 3

[0028] A method for refining silk fabrics, comprising the steps of:

[0029] (1) Peracid pretreatment: Put the raw silk into the acid solution at a temperature of 50-60°C for pretreatment, the silk is puffed, and then the gray silk obtained is decompressed twice by a vacuum machine , after the silk fabric has fully absorbed water, put it into the puffing agent and soak it for 12 minutes, the pretreated silk can effectively avoid gray damage;

[0030] (2) Preliminary training: put the pretreated silk fabric in step (1) into the refining agent for preliminary training for 12 minutes, the pH value of the preliminary training solution is 8, and the initial training temperature is 60-65°C. The refining agent is A compound of an alkali refining agent and a surfactant refining agent, wherein the surfactant in the surfactant refining agent is an alkyl glucoside, and the alkali in the alkali refining agent is sodium oleate, and the alkali The mass ratio of refining agent and surfactan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a scouring method of a real silk fabric. The scouring method comprises the following steps: (1) pre-treating raw silks in an acid liquid at the temperature of 50-60 DEG C to swell the silks; (2) performing primary scouring with a scouring agent, namely a composite of an alkali scouring agent and a surfactant scouring agent; (3) performing secondary scouring, wherein a bleaching agent is added into a secondary scouring agent; and (4) after-treating, namely treating the scoured real silks from step (3) in water at 45-55 DEG C after swelling. The scouring method is simple, enhances the scouring effect of the scouring agents, and effectively solves the problem of unclean effluent of the alkali scouring agent; meanwhile, the scoured silks have the characteristics of high strength, good capillary effect, soft handfeel, excellent whiteness and low cost, and the product quality is ensured.

Description

technical field [0001] The invention relates to a method for refining silk fabrics, belonging to the technical field of textile engineering. Background technique [0002] Refining is an important process in the production and processing of silk fabrics. The success of refining is closely related to the quality of silk fabrics. In addition to dissolving most of the sericin wrapped around the silk fibers during the refining process and keeping the silk fibers from being lost as much as possible, the capillary effect of the silk fibers should also be improved to increase the affinity for dyeing materials, which will be used later. Create a good foundation for dyeing and finishing processing. The current refining method adopts the soap-alkali method, that is, the pretreated silk fabric is obtained after the initial scouring, secondary scouring, second heat soaking, washing and dehydration processes. The physical indexes of the above-mentioned soap-alkaline refining are basical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M13/00D06M13/224D06M13/11D06M13/203D06L3/00D06M101/10D06L4/13
Inventor 王斌
Owner 山东信开源科技创新发展有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap